SYNTHESIS, CHARACTERIZATION AND APPLICATION OF Ni /SiO2 HETEROGENEOUS NANO CATALYST IN OPTIMIZATION OF METHYL ESTER FROM Khaya senegalensis SEED OIL

Subject Areas : Journal of Nanoanalysis

Mela Yoro ¹ , Wilson Lamayi ² , Nasiru Pindiga ³ , Zaccheus Shehu ⁴

1 - Department of Chemical Sciences, Faculty of Science, Federal University of Kashere, Gombe, Nigeria
2 - Chemistry department, Faculty of Science, Gombe State University, Nigeria.
3 - Department of Chemistry, Gombe state University, Nigeria
4 - Chemistry Department, Faculty of Science, Gombe State University, Gombe, Nigeria.

Received: 2021-04-23 Accepted : 2022-02-24 Published : 2023-02-15

Keywords: Optimization, Characterization, Methyl ester, nano catalyst,

Abstract :

Ni / SiO2 heterogeneous nano catalyst was synthesized and characterized using different analytical tools including FT-IR, UV spectrophotometer, SEM equipped with an energy dispersive X-ray spectrometer (EDX), and XRD. The synthesized catalyst was used in the transesterification of methyl ester produced from mahogany seed oil. The reaction conditions for the transesterification process were optimized. The yield of 85% was achieved when the reaction was carried using Ni / SiO2 with concentration of 1.5% wt, volume ratio of methanol to oil of 5:1, reaction temperature of 60 °C, and a reaction time of 120 min. The Ni / SiO2 nano catalyst was regenerated from the mixture and was reused for various circles by applying the optimum conditions obtained during the present study. The results showed that the methyl ester yield decreased exponentially by increasing the cycle number when the regenerated catalyst was used. However, good conversion (>72%) was obtained up to the 4th cycles. It could be concluded that Ni / SiO2 nano catalyst is catalytically active and may serve as a potential catalyst for biodiesel production.

References:

[1] Leo V., Vineeth B., and Bhim P.S. Green Nanotechnology for Biofuel Production, Journal of Nanotechnology, 2018; 9(3): 129-139.
[2] Pandit P. R., and Fulekar M.H. Egg shell waste as heterogeneous nanocatalyst for biodiesel production: optimized by response surface methodology, Journal of environmental management, 2017; 198 (9): 319-329.
[3] Reddy A.N.R., Abu A., Saleh M.D., Saiful I., Sinin H., and Md Abdul M. Biodiesel production from crude Jatropha oil using a highly active heterogeneous nanocatalyst by optimizing transesterification reaction parameters. Journal of Energy & Fuels, 2015; 30(1): 334-343.
[4] Widayat W., Satriadi H., Yuariski O. and Murwono D. Preparation of Heterogeneous CaO Catalysts for Biodiesel Production, Research. Journal of Applied Sciences, Engineering and Technology, 2015; 6 (10): 1732-1739.
[5] Widayat W., Darmawan T., Hadiyanto H., and Arosyid R. Preparation of Heterogeneous CaO Catalysts for Biodiesel Production, Journal of Physical Sciences, 2017; 17(3):221- 233
[6] Rintu V. Joy P. and Johnson.H. I. Synthesis And Characterizations Of Needle- Shaped Cuo Nanoparticles For Biodiesel Application, International Journal of Advanced Research Research, 2017; 30(3): 2930 - 2939.
[7] Kashif A. , Iqbal T., Solat U. S. and Muhammad M. Green synthesis of cobalt nanoparticles by using methanol extract of plant leaf as reducing agent, Pure Appl. Biol., 2016; 5(3): 453-457.
[8] Najlaa S. A. Green synthesis of platinum nanoparticles using Saudi’s Dates extract and their usage on the cancer cell treatment, Arabian Journal of Chemistry, 2018; 4(3):30-35
[9] Sharmila B. A., Thirumurugan V., Amudha M. Green Biosynthesis of Silver Nano Particles from Aegle Marmelos Aqueous Leaf Extract, IOSR Journal of Applied Chemistry (IOSR-JAC), 2018; 11(7): 2278-5736.
[10] Bashpa P., Seema D. R., and Bijudas K. Green synthesis of silver nanoparticles from Orthosiphon thymiflorus leaf extract, International Journal of Green and Herbal Chemistry, 2017; 6(4): 207-211.
[11] Flora J. P, Sivakumari K., Rajini S., Ashok K, Jayaprakash P, Rajesh S. green synthesis of silver nanoparticles from propolis, Research Journal of Life Sciences, Bioinformatics, Pharmaceutical and Chemical Sciences, 2018; 4(2):23
[12] Ruíz-Baltazar A., Esparza R., Pérez R., and Rosas G. Structural Characterization of Fe-Ag Bimetallic Nanoparticles Synthesized by Chemical Reduction, International Research Journal of Pure & Applied Chemistry, 2014; 4(3): 263-269
[13] Anuoluwa A. A., Enock O. D., Kolawole O. A., Olayinka O. A., Joseph A., Olugbuyiro O. Tolutope O. S., Oluwaseun E. and Moses E. E. Modeling and Synthesis of Ag and Ag/Ni Allied Bimetallic Nanoparticles by Green Method: Optical and Biological Properties, International Journal of Biomaterials, 2018; 2018(1): 1-17
[14] Pradeep K. K., Meet A. M., Purnima S. K. Development of Fe/Ru Bimetallic Nanoparticles for Promising Application in the Selective Synthesis of SWNTs, Materials international Journal, 2020; 2(2): 0250-0255
[15] Hamid T. N., Elham A., Soodabeh D., Mohammad K., and Abolfazl A. Bimetallic nanoparticles: Preparation, properties, and biomedical applications, International Journal of Artificial Cells, Nanomedicine, and Biotechnology, 2016; 44(1) 376-380
[16] Tooba M., Vikas S., and Rajesh S.T. Green Synthesis of Bimetallic Nanoparticles and its Applications: A Review, Journal of pharmaceutical Sciences and research, 2017; 9(2): 102-110
[17] Rehman A., Pullabhotla V.S.R., and Jonnalagadda S.B. Catalysis Communications, Journal of Chemical Engineering and Technology Royal Institute of Technology, 2008; 9 (14): 2417-2421.
[18] Balaji P., Qin S., Wang J., Bian K., and Tao C. Biodiesel Synthesis with Iron Oxide Nano-Catalyst Catalyzed Pongamia Pinnata Seed Oil and Dimethyl Carbonate, American Journal of Energy Engineering,2018; 6(3): 21 -28.
[19] Abdelrahman B., Fadhil, A., Aziz M. and Marwa H. A. Optimization of methyl esters production from non-edible oils using activated carbon supported potassium hydroxide as a solid base catalyst,. Arab Journal of Basic and Applied Sciences, 2018; 27(5): 25-27
[20] Nasar M. and Taufiq Y. H. Synthesis And Characterization Of Solid Heterogeneous Catalyst For The Production Of Biodiesel From High FFA Waste Cooking Oil, Bayero Journal of Pure and Applied Sciences, 2017; 10(1) : 62 – 66.
[21] Al-Jammal, N., Al-Hamamre, Z., & Alnaief, M. Manufacturing of zeolite based catalyst from zeolite tuft for biodiesel production from waste sunflower oil, Journal of Renewable Energy, 2016; 29(3): 449–459.
[22] Dian M., Widjo N.J., Indriana ., and Nuryono. Phosphate modified silica for adsorption of Co(II), Ni(II), Cu(II), and Zn(II). Indo. J. Chem, 14(2): 143-151.
[23] Wu W. He Q. G and Jiang C. Z. (2008). Magnetic iron nanoparticles: synthesis and surface functionalization strategies. journal of nano technology, 8(5): 397-401
[24] Danbature W.L., Aliyu J., Adamu H.M. (2015). Production of methyl ester from mahogany (Khaya senegalensis) seed oil. Journal of Chemistry and Chemical Sciences, 5(9): 489-499.
[25] Dass P.M. , Louis H., Alheri A., Amos P.I., Bifam M. and Ago M.A. (2018). Production of Biodiesel Oil from Desert Dates (Balanites aegyptiaca)

Full-Text:



J. Nanoanalysis., 10(1): 390-400, Winter 2023

 

SYNTHESIS, CHARACTERIZATION AND APPLICATION OF Ni /SiO2 HETEROGENEOUS NANOCATALYST IN OPTIMIZATION OF METHYL ESTER FROM Khaya senegalensis SEED OIL

Mela Yoro*,1, Wilson Lamayi 2, Nasiru Pindiga 2, Zaccheus Shehu 2

1       Department of Chemical Sciences, Faculty of Science, Federal University of Kashere, Gombe, Nigeri        

2       Chemistry Department, Faculty of Science, Gombe State University, Gombe, Nigeria        

 

ARTICLE INFO Article History: Received 2021-04-23 Accepted 2022-02-24 Published 2023-02-15   Keywords:  Methyl ester,                Nano catalyst,                Optimization,               Characterization.

ABSTRACT   Ni / SiO2 heterogeneous nanocatalyst was synthesized and characterized using different analytical tools including FT-IR, UV spectrophotometer, SEM equipped with an energy dispersive X-ray spectrometer (EDX), and XRD. Subjecting the synthesized heterogeneous nanoparticle into catalysis, Biodiesel was produced from mahogany seed oil and methanol using the synthesized nanocatalyst. The reaction conditions were optimized. The yield of 85% was achieved when the reaction was carried out using Ni / SiO2 with concentration of 1.5%wt, a volume ratio of methanol to oil of 5:1, a reaction temperature of 60 °C, and a reaction time of 120 min. The Ni / SiO2 nanocatalyst was regenerated from the mixture and was reused for various circles by applying the optimum conditions obtained during the present study. The results showed that the methyl ester yield decreased exponentially by increasing the cycle number when the regenerated catalyst was used. However, good conversion (>72%) was obtained up to the 4th cycles. All the biodiesel quality parameters determined agreed with the specifications for biodiesel quality standards, hence, Ni / SiO2 nanocatalyst is catalytically active.

How to cite this article Yoro M., Lamayi W., Pindiga N., Shehu Z.,  SYNTHESIS, CHARACTERIZATION AND APPLICATION OF Ni /SiO2 HETEROGENEOUS NANOCATALYST IN OPTIMIZATION OF METHYL ESTER FROM Khaya senegalensis SEED OIL. J. Nanoanalysis., 10(1): 390-400, Winter 2023. DOI: 10.22034/jna.2022.1928789.1253.

 

INTRODUCTION

 

Nano catalyst is a type of nanomaterial with the size range of 1-100nm [1]. Recently, Nano catalysts have become the focus as efficient biodiesel production because of high surface area, high catalytic efficiency and resistance to saponification along with good rigidity [2]. The particle size of the catalyst that is used in biodiesel production is one of the most important factors for its catalytic activity [3]. Many studies have confirmed that catalyst with a lower particle size and higher surface area accelerate reaction rates due to an increased number of molecules that have minimum required energy for the reaction to occur. Generally speaking, Heterogeneous catalysis is a type of catalysis in which the catalyst occupies a different phase than the reaction mixture. But running a reaction under heterogeneous catalytic conditions has several advantages compared to other catalytic processes; easy handling, good selectivity (having multiple binding sites), safe to store, long life time, good thermal stability, rigid structure avoids the aggregation of active catalyst, insoluble in organic solvents and finally easy and inexpensive removal from reaction mixture by filtration or centrifugation. In another word, heterogeneous catalysts are catalysts that are in different phase with the reactants (the catalyst is usually in solid phase while the reactant is in liquid phase).They can be separated from final product by filtration and reused. This causes less consumption of both chemicals and time of course. Heterogeneous catalysts are noncorrosive. They have a high selectivity and can be easily separated from the products. The disadvantages of utilization of homogeneous catalysts in biodiesel production are saponification reaction and regeneration issue after the transesterification process is completed as well as producing toxic wastewater [4-5]. Biodiesel is one of the promising options for the alternative renewable fuels that can be used in existing engines [6] and nanoparticles are therefore used as catalysts for production of biodiesel. Nanoparticles of most transition metals have been synthesized and applied either as a catalyst, a reducing agent or as an antibacterial agent [7-11]. Nanoparticles can be synthesized either as monometallic or bimetallic nano particles [12-16]. In this research, the choice of Ni/SiO2 nanocatalyst over others was conceived out of the fact that Ni/SiO2 demonstrates special properties including lower particle size, higher surface area, multiple binding sites as well as good thermal stability. Hence, accelerates reaction rates [17].

 

EXPERIMENTAL SECTION

Materials

The main materials used during this work were Nickel (ii) nitratehexahydrate, silica gel, doubly distilled water, all of which were of analytical grade and were supplied from Sigma Aldrich.

 

Synthesis of Ni / SiO2 as heterogeneous Nano catalyst

The catalyst was prepared by the impregnation method with slight modifications as reported by the literature [17]. This was achieved by dissolving 2.51g nickel (II) nitrate hexahydrate in 20ml of distilled water and adding it to 5.0g silica gel and stirring for 2 h using a magnetic stirrer at room temperature (20 ±1 oC). This was aged at room temperature overnight. The excess water was removed by heating the mixture on water bath and a Rota vapor was used under vacuum to evaporate water. The catalyst material was dried in an oven at 100–120 oC for 12 h. Figure 1 shows the synthesized Ni / SiO2.

 

Characterization of Ni / SiO2 heterogeneous Nano catalyst

The catalyst was characterized using UV Spectroscopic technique, Fourier Transform Infra-red spectroscopy, SEM and XRD for its absorption, functional group, surface morphology and crystalline shape respectively.

 

Transesterification Process of Khaya senegalensis Seed Oil Using Ni / SiO2 Heterogeneous Nano catalyst

Modified method of Balaji et al., 2018 [18] was adopted as follows:

Mahogany seed oil was used as a` reactant in the biodiesel transesterification process. First the mahogany seed oil was boiled at 50°C. The reaction was carried out in a 250ml three necked flask. A Liebig condenser was attached onto the middle neck; a thermometer was inserted through the second neck; while the third neck was used for sample introduction and withdrawal. The catalyst was first dissolved in methanol. The measured amount of the oil and a stirring bar were introduced into the three necked flask. The flask and its content were heated on a hot plate equipped with a magnetic stirrer. Volume ratio of mahogany seed oil to methanol varied from 1:1 to 6:1. The Ni/ SiO2 nanocatalyst concentration was 0.5wt% to 3.0wt%. The reaction temperature was varied from 10oC to 80°C under standard conditions. The reaction was allowed to run for various reaction times, from 30 min to 180 min, to study the transesterification process. The sample was allowed to settle by gravity for 12 h after collection with a separation funnel, and it settled into a clear, liquid layer of biodiesel on top of a glycerol layer. The glycerol was drained from the bottom of the separation funnel, and the remaining crude biodiesel was washed four times with millipore water to remove the catalyst. To ensure the high purity of the biodiesel, a rotary evaporator was employed to remove excess methanol from the biodiesel. The high-purity biodiesel was dried with anhydrous sodium sulfate and the percentage of biodiesel yield was calculated. The standard ASTM D6751-02 methods were used in determining the properties of the biodiesel produced.

 

 

 

Figure 1. The synthesized Ni / SiO2 heterogeneous nanocatalyst

 

Figure 2. The collected sample showing the biodiesel layer on top and glycerol at the bottom

 

 

The % yield of the methyl ester produced was calculated using the equation below

        

% Yield =    X 100%

 

Regeneration and Reusability of the Catalyst

Regeneration of the resulting heterogeneous nanocatalysts was performed by filtration method, as reported by the literature [19]. The residue which is the catalyst was washed with a methanol so as to remove biodiesel, glycerol and the oil molecules attached to the catalyst surface [19]. After the regeneration, the regenerated catalyst was tested for transesterification of the mahogany seed oil with methanol using the optimal conditions obtained during the present study.

 

Catalysts Reusability Test

The reusability of the catalysts was performed under the optimized reaction conditions of 1.5wt% catalyst loading, 60oC reaction temperature, 5:1 methanol to oil ratio and 120 min reaction time. After completion of each run, the used catalyst was separated from the reaction mixture and was reused without further regeneration treatment.

 

RESULTS AND DISCUSSION

UV analysis

The wavelengths of the sample were varied from 200 – 800nm. After each run, the absorbance was recorded and the wavelength was adjusted before proceeding to the next. Figure 2 shows the graph of absorbance against wavelength for Ni / SiO2. The highest absorbance was noticed at 300nm and then there was a decrease in the absorbance (see figure 3) which might be attributed to the reduction of Ni (+2) to Ni (+0). This trend agrees with the one reported by some researchers [19-20].

 

FT- IR Analysis

        FT-IR is used to determine different functional groups such as alcohol, alkane, alkynes, alkenes and other such groups present in the substance which here is Ni / SiO2.

FT-IR studies presented in Table 1 on Ni / SiO2 catalyst shows a sharp band at 1384.48 cm-1 on the catalyst. This band is due to the presence of Ni-O and a broad band at 3430.33 cm-1 is due to N-H stretch. The absorption band in the range of 1092.62 cm-1 indicates the presence of C-OH group. Similarly, the bands at 802 cm-1 and 455cm-1 is due to Si-O stretching and bending vibration respectively. The FT-IR results are in good agreement with the one reported by another researcher (21-22).

 

(a)       UV image	(b)       FT-IR Spectrum

Figure 3. UV and FT-IR images for Ni / SiO2 nanocatalyst

 

Table 1. FT-IR studies of Ni / SiO2 Heterogeneous nanocatalyst

Peak(cm-1)	Bond	Mode	Transmittance (%)	Intensity
802	Si-O	Stretch	26.16	Strong
1384.48	Ni-O	Stretch	29.19	Strong
1636.22	C-C		49.7	Strong
1092.62	C-OH	Stretch	51.99	Strong

 

 

SEM and XRD Analysis

The morphologies of the synthesized Ni / SiO2 catalyst was examined by scanning electron microscope (SEM) equipped with an energy dispersive X-ray spectrometer (EDX). The analysis of the synthesized catalyst using Scanning electron microscopy provided the morphology and size details of the Ni / SiO2 nanoparticles. It was identified that shapes of Ni / SiO2 nanoparticles gave a closely packed but porous and well dispersed surface morphology which is slightly different with the one reported by another researcher[22]. This slight variation is possibly due to environmental working conditions. In the same vein, XRD measurements were carried out to understand the crystalline structure of Ni / SiO2 catalysts, and the results were presented in figure 5(b). Patterns of Ni / SiO2 exhibited a broad and large peak around 22∘, which was attributed to amorphous silica of support. The sample showed the fcc NiO phase, with typical reflections of the (111), (200), and (220) planes at 2𝜃 = 37∘, 43∘, 63o, respectively. This result is in conformity with the one reported by another researcher [23].

 

Energy dispersive micro analysis (EDAX)

The elemental analysis of the synthesized Ni / SiO2 nanoparticles was studied using energy dispersive micro analysis (EDAX). The analysis revealed highest proportion of silicon with 78.39 and 66.91 for atomic and weight concentrations respectively in the nanoparticles followed by nickel with 15.92 and 28.40 for atomic and weight concentrations respectively. It was followed by nitrogen with 3.89 and 3.23 for atomic and weight concentrations respectively (table 2). The structure is formed by nano-sized silica particles linked together, resulting in a random arrangement of holes and cavities. The EDS spectrum of Ni / SiO2 contains signals belonging to Si and O due to the SiO2 support. In addition to O and Si signals, the EDS spectrum of Ni / SiO2 showed signs of Ni suggesting that the Ni was successfully impregnated on the silica support [22].

 

The effect of optimization parameters on % yield of Methyl Ester using Ni/ SiO2 as a catalyst

        The effect of the following process parameters were studied using Ni/ SiO2 as heterogeneous nanocatalyst using optimum conditions obtained earlier during the present study

 

The effect of reaction temperature

        Transesterification reaction was performed for 120 min at 5:1 volume ratio with 1.5 wt % of catalyst (Ni/ SiO2) at different temperature ranges with 10oC starting from 30 to 80oC. From the graph it was observed that as temperature increases, reaction also increases hence the yield also increases up to 60oC and then decreases because higher reaction temperatures cause methanol to vaporize resulting in decreased yield. In other words, the boiling point of methanol is 64.7 °C and in order to avoid alcohol evaporation, reaction temperature has to be less than 64.7 oC. Increasing the temperature will reduce the viscosity of the oil which leads to a sufficient contact at the active site of catalyst surface between the oil and the methanol. Reaction temperature was a significant factor in biodiesel synthesis as the yield increased significantly for all the two catalysts. Increasing reaction temperature reduces the viscosity of Khaya senegalensis seed oil and enhances the product yield because of the inhibition of mass transfer resistance which agrees with the other researcher’s report [24]. 

 

 

(a)       SEM image of the unused Ni/SiO2	(b)       SEM image of the last regenerated Ni/SiO2
(c)       X-Ray Diffraction image of Ni / SiO2

Figure 4. SEM and XRD image for Ni / SiO2 nanocatalyst

 

Table 2. Elemental Analysis for Ni / SiO2 nanocatalyst

Element Number	Element symbol	Element name	Atomic Concentration	Weight Concentration
14 28 7 6 11 8	Si Ni N C Na O	Silicon Nickel Nitrogen Carbon Sodium Oxygen	78.39 15.92 3.89 1.03 0.75 1.9	66.91 28.40 3.23 0.73 0.72 0.83

 

 

The effect of catalyst concentration

        Catalyst concentration is the key variable which enhances the yield of methyl ester production. In general, as the catalyst concentration increases, the conversion of triglycerides is also increased. This is because an insufficient amount of catalyst results in an incomplete conversion of triglycerides into fatty acid esters. That is why optimization was carried out using Ni/SiO2 concentrations of 0.5, 1.0, 1.5, 2.0, 2.5 and 3.0wt% at reaction temperature of 60oC with volume ratio of 5:1 for 120 min reaction time. As the catalyst increases, the yield also increases up to 1.5wt% and then decreases gradually because the addition of excess heterogeneous catalysts causes more triglycerides participation in the saponification reaction, resulting in increased production of soap and reduction of the methyl ester yield. So, any increase in concentration of catalyst beyond the neutralization limit results in decrease in methyl ester conversion [24].

 

The effect of Reaction Time

        In the present study, the effect of reaction time on transesterification process with percentage yield of biodiesel produced was also evaluated. The reaction time was taken from 30 to 180 Min., with the interval of 30 min., keeping the optimum volume ratio 5:1, catalyst concentration of 1.5wt% with the previously found optimum reaction temperature 60°C.The transesterification reaction proceeds quickly and around 55 % of ester was converted in 30 min. After one hour around 70 % of ester was produced, after 90 min around 80% of ester was produced, after 120min, around 85% was found and after that slightly reduced percentage of ester was observed, this phenomenon might simply have resulted from the exhaustion of methanol due to the longer time taken. Graphically, it can be seen in figure 8, that the constant value of ester produced was observed after 120 min as a result of forward and reversed reactions. So it is concluded that around 120 min, reaction time was optimum and we got around 85% of ester production and after that, ester production decreased drastically. This result is in agreement with previous research [25].

 

The effect of volume ratio

The stoichiometry of the reaction generally, requires 3 moles of methanol per mole of triglycerides to yield 3 moles of methyl ester and 1 mole of glycerol. The alcohol may be methanol, ethanol, isobutanol and isopropanol. In this present study, methanol has been considered due to its low price and highly reactive nature. Volume ratio of methanol to oil was varied from 1:1 to 6:1 at 60o C reaction temperature of 1.5wt% catalyst concentrations for 120 min reaction time in transesterification reaction. Starting with 1:1 volume ratio the yield started increasing for the catalyst because higher alcohol volume ratio interferes with the separation of glycerol because there is an increase of solubility. From the graph it is noticed that yield of 1:1 is 40%, 2:1 is 50%, 3:1 is 65%, 4:1 is 73% and 5:1 gave 85% which is the optimum yield, then a decrease in yield was observed from 6:1 methanol to oil volume ratio which although exhibited the same trend, yet slightly differs from the earlier research [25].

 

(a)       Effect of Temperature

(b)       Effect of Catalyst

(c)       Effect of Time

(d)       Effect of Methanol to Oil Volume Ratio

 

Figure 5. The effect of Temperature, Catalyst, Time and Methanol to oil Volume ratio respectively on the % yield

 

 

 

 

Recoverability and reusability of the synthesized heterogeneous nanocatalysts

The most important characteristics of the heterogeneous nanocatalysts are their recoverability and reusability. Based on this fact, the utilized catalysts were regenerated and examined for transesterification of mahogany seed oil with methanol for further cycles by applying the optimum conditions obtained during the present study as shown in figure 10. The results pointed out that the methyl ester yield decreased exponentially by increasing the cycle number when the regenerated catalyst was used. However, good conversion (>72%) was obtained up to the 4th cycle for Ni /SiO2 nanocatalyst. The drop in biodiesel yield in the fourth cycle was due to deactivation of catalyst sample, which might be as a result of adsorption of fatty acid, glycerol or water molecule on the active sites of the catalyst [26]. In another words, the reduction in the methyl ester yield with increasing the regeneration runs could be attributed to the leaching of active metals from the support surface. As a result, the number of the active sites available for the reaction will be less in number. These achievements are in concord with the previously reported data by other researchers [27]. So it can be seen that, the catalyst in question was regenerated and reused producing good yield up to a good number of cycles (four cycles) which explains why the choice of this catalyst over other catalysts is quite paramount.

CONCLUSION

Ni / SiO2 heterogeneous nanocatalyst was synthesized using the method outlined earlier and characterized using different analytical tools / machines including FT-IR, UV spectrophotometer, SEM equipped with an energy dispersive X-ray spectrometer (EDX), and XRD. Subjecting the synthesized heterogeneous nanocatalyst into catalysis, biodiesel was produced from mahogany seed oil and methanol using the synthesized nanocatalyst. The reaction conditions were optimized. The Ni / SiO2 nanocatalyst was efficient and reusable in the production of biodiesel of international standard. The yield of 85% was achieved as the optimum with concentration of 1.5%wt, a volume ratio of methanol to oil of 5:1, a reaction temperature of 60 °C, and a reaction time of 120 min. The nanocatalyst was regenerated from the mixture and reused for various circles by applying the optimum conditions obtained during the present study as shown in figure 11. The results pointed out that the methyl ester yield decreased exponentially by increasing the cycle number when the regenerated catalyst was used. However, good conversion (>72%) was obtained up to the 4th cycles. All the biodiesel quality parameters determined agreed with the specifications for biodiesel quality standards, hence, Khaya senegalensis seed oil is a good biodiesel feedstock.

 

 

Figure 6: The influence of catalysts (Ni / SiO2) reusability on % yield of biodiesel

 

REFERENCES

[1]       Leo V., Vineeth B., and Bhim P.S. Green Nanotechnology for Biofuel Production, Journal of Nanotechnology, 2018; 9(3): 129-139.

[2]       Pandit P. R., and Fulekar M.H. Egg shell waste as heterogeneous nanocatalyst for biodiesel production: optimized by response surface methodology, Journal of environmental management, 2017; 198 (9): 319-329.

[3]       Reddy A.N.R., Abu A., Saleh M.D., Saiful I., Sinin H., and Md Abdul M. Biodiesel production from crude Jatropha oil using a highly active heterogeneous nanocatalyst by optimizing transesterification reaction parameters. Journal of Energy & Fuels, 2015; 30(1): 334-343.

[4]       Widayat W., Satriadi H., Yuariski O. and Murwono D. Preparation of Heterogeneous CaO Catalysts for Biodiesel Production, Research. Journal of Applied Sciences, Engineering and Technology, 2015; 6 (10): 1732-1739.

[5]       Widayat W., Darmawan T., Hadiyanto H., and Arosyid R. Preparation of Heterogeneous CaO Catalysts for Biodiesel Production, Journal of Physical Sciences, 2017; 17(3):221- 233

[6]       Rintu V. Joy P. and Johnson.H. I. Synthesis And Characterizations Of Needle- Shaped Cuo Nanoparticles For Biodiesel Application, International Journal of Advanced Research Research, 2017; 30(3): 2930 - 2939.

[7]       Kashif A. , Iqbal T., Solat U. S. and Muhammad M. Green synthesis of cobalt nanoparticles by using methanol extract of plant leaf as reducing agent, Pure Appl. Biol., 2016; 5(3): 453-457.

[8]       Najlaa S. A. Green synthesis of platinum nanoparticles using Saudi’s Dates extract and their usage on the cancer cell treatment, Arabian Journal of Chemistry, 2018; 4(3):30-35

[9]       Sharmila B. A., Thirumurugan V., Amudha M. Green Biosynthesis of Silver Nano Particles from Aegle Marmelos Aqueous Leaf Extract, IOSR Journal of Applied Chemistry (IOSR-JAC), 2018; 11(7): 2278-5736.

[10]       Bashpa P., Seema D. R., and Bijudas K. Green synthesis of silver nanoparticles from Orthosiphon thymiflorus leaf extract, International Journal of Green and Herbal Chemistry, 2017; 6(4): 207-211.

[11]       Flora J. P, Sivakumari K., Rajini S., Ashok K, Jayaprakash P, Rajesh S. green synthesis of silver nanoparticles from propolis, Research Journal of Life Sciences, Bioinformatics, Pharmaceutical and Chemical Sciences, 2018; 4(2):23

[12]       Ruíz-Baltazar A., Esparza R., Pérez R., and Rosas G. Structural Characterization of Fe-Ag Bimetallic Nanoparticles Synthesized by Chemical Reduction, International Research Journal of Pure & Applied Chemistry, 2014; 4(3): 263-269

[13]       Anuoluwa A. A., Enock O. D., Kolawole O. A., Olayinka O. A., Joseph A., Olugbuyiro O. Tolutope O. S., Oluwaseun E. and Moses E. E. Modeling and Synthesis of Ag and Ag/Ni Allied Bimetallic Nanoparticles by Green Method: Optical and Biological Properties, International Journal of Biomaterials, 2018; 2018(1): 1-17

[14]       Pradeep K. K., Meet A. M., Purnima S. K. Development of Fe/Ru Bimetallic Nanoparticles for Promising Application in the Selective Synthesis of SWNTs, Materials international Journal, 2020; 2(2): 0250-0255

[15]       Hamid T. N., Elham A., Soodabeh D., Mohammad K., and Abolfazl A. Bimetallic nanoparticles: Preparation, properties, and biomedical applications, International Journal of Artificial Cells, Nanomedicine, and Biotechnology, 2016; 44(1) 376-380

[16]       Tooba M., Vikas S., and Rajesh S.T. Green Synthesis of Bimetallic Nanoparticles and its Applications: A Review, Journal of pharmaceutical Sciences and research, 2017; 9(2): 102-110

[17]       Rehman A., Pullabhotla V.S.R., and Jonnalagadda S.B. Catalysis Communications, Journal of Chemical Engineering and Technology Royal Institute of Technology, 2008; 9 (14): 2417-2421.

[18]       Balaji P., Qin S., Wang J., Bian K., and Tao C. Biodiesel Synthesis with Iron Oxide Nano-Catalyst Catalyzed Pongamia Pinnata Seed Oil and Dimethyl Carbonate, American Journal of Energy Engineering,2018; 6(3): 21 -28.

[19]       Abdelrahman B., Fadhil, A., Aziz M. and Marwa H. A. Optimization of methyl esters production from non-edible oils using activated carbon supported potassium hydroxide as a solid base catalyst,. Arab Journal of Basic and Applied Sciences, 2018; 27(5): 25-27

[20]       Nasar M. and Taufiq Y. H. Synthesis And Characterization Of Solid Heterogeneous Catalyst For The Production Of Biodiesel From High FFA Waste Cooking Oil, Bayero Journal of Pure and Applied Sciences, 2017; 10(1) : 62 – 66.

[21]       Al-Jammal, N., Al-Hamamre, Z., & Alnaief, M. Manufacturing of zeolite based catalyst from zeolite tuft for biodiesel production from waste sunflower oil, Journal of Renewable Energy, 2016; 29(3): 449–459.

[22]       Dian M., Widjo N.J., Indriana ., and Nuryono. Phosphate modified silica for adsorption of Co(II), Ni(II), Cu(II), and Zn(II). Indo. J. Chem, 14(2): 143-151.

[23]       Wu W. He Q. G and Jiang C. Z. (2008). Magnetic iron nanoparticles: synthesis and surface functionalization strategies. journal of nano technology, 8(5): 397-401

[24]       Danbature W.L., Aliyu J., Adamu H.M. (2015). Production of methyl ester from mahogany (Khaya senegalensis) seed oil. Journal of Chemistry and Chemical Sciences, 5(9): 489-499.

[25]       Dass P.M. , Louis H., Alheri A., Amos P.I., Bifam M. and Ago M.A. (2018). Production of Biodiesel Oil from Desert Dates (Balanites aegyptiaca) Seeds Oil Using a Hetrogeneous Catalyst Produced from Mahogany (Khaya senegalensis) Fruit Shells. Analytical chemistry: An indian journal Research, 18(1): 42-53.

[26]       Nasar M. and Taufiq Y. H. Synthesis And Characterization Of Solid Heterogeneous Catalyst For The Production Of Biodiesel From High FFA Waste Cooking Oil, Bayero Journal of Pure and Applied Sciences, 2017; 10(1) : 62 – 66.

[27]       Al-Jammal, N., Al-Hamamre, Z., & Alnaief, M. Manufacturing of zeolite based catalyst from zeolite tuft for biodiesel production from waste sunflower oil, Journal of Renewable Energy, 2016; 29(3): 449–459.

 

 

 

 

*Corresponding Author Email: [e-mail]

  This work is licensed under the Creative Commons Attribution 4.0 International License.

To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.

 

 

---