1 - Effect of Ni-P electroless coating and heat treatment on tribological and corrosion properties of copper substrate
masoud soltani Ali Shafyei Kianoush Zarrin naghsh Reihane Aliramezani

Copper is relatively soft metal and its wear and corrosion are considered to be a major factors of degradation of this metal. For this reason, when the higher wear and corrosion properties are needed, surface properties should be improved with different surface treatmen More

Copper is relatively soft metal and its wear and corrosion are considered to be a major factors of degradation of this metal. For this reason, when the higher wear and corrosion properties are needed, surface properties should be improved with different surface treatments. One of these methods is the applying of Ni-P electroless coating due to good mechanical properties, suitable corrosion resistance and its ability of heat treatment on Cu. In this research after the surface preparation of Cu, which included grinding, degreasing and surface activation, the specimens were dipped into commercial electroless nickel bath (SLOTONIP 70A) for 60 minutes. SEM images and the results of the EDS test confirmed the formation of Ni-P electroless coating (with 10.83 wt. % phosphorus) with a spherical structure. Applying the heat treatment increased the hardness from 495 to 880 Vickers. XRD results showed this hardening is due to the formation of Ni crystal and Ni3P phases at this temperature in the coating. The study of wear resistance and corrosion property of coatings was also done using pin-on test and polarization tests, respectively. The results showed that the heat treatment improved the wear resistance of the coating, and the weight loss in the presence of the heat treated coating reduced to 76% due to increasing hardness and roughness of the coating by performing heat treatment. Manuscript profile
Open Access Article
- Abstract Page
- Full-Text
2 - Fabrication of anodic aluminium oxide template and the generation of magnetic Co nanowires within it
masoud soltani Reihane Aliramezani saeid akhavan Zeinab Erfani Gahrouei mohammad noormohammadi
20.1001.1.2322388.2019.7.4.6.4

Among nanostructured materials, magnetic nanowires have been heeded because of their high shape anisotropy and their easy fabrication methods. Electrochemical deposition on the anodic aluminium oxide (AAO) is one of the best methods to grow different nanowires. In this More

Among nanostructured materials, magnetic nanowires have been heeded because of their high shape anisotropy and their easy fabrication methods. Electrochemical deposition on the anodic aluminium oxide (AAO) is one of the best methods to grow different nanowires. In this paper, the AAO was fabricated on the 1100 Al alloy substrate by hard anodizing in 0.3 M oxalic acid solution. Then, a barrier layer thinning process was carried out for the electrodeposition process. A pulsed electrodeposition process was used to fill the nano-pores. According to this method, cobalt nanowires were grown in the nano-holes. Structural, crystalline, and magnetic properties of the samples were evaluated using field emission scanning electron microscopy (FESEM), X-ray diffraction (XRD), and vibrating sample magnetometer (VSM), respectively. The results showed that nanowires have a diameter of 87 nm and crystalline structure with crystalline plates in directions (100), (002), and (110). A coercivity value of 600 Oe was obtained for nanowires, which is several times larger than cobalt bulk. Manuscript profile