It is well-known that the harsh operational conditions of turbine blades lead to a gradual change in the microstructure of underlying Ni-based superalloy of blades. According to this, a rejuvenation process should be conducted on turbine blades superalloys to recover th چکیده کامل
It is well-known that the harsh operational conditions of turbine blades lead to a gradual change in the microstructure of underlying Ni-based superalloy of blades. According to this, a rejuvenation process should be conducted on turbine blades superalloys to recover their microstructures. The first and main step of rejuvenation process is the determination of appropriate solution condition in which ϒʹ precipitates dissolve in the ϒ matrix. In this study, different heat treatment conditions were applied on a Ni-based single crystal superalloy to determine its solution condition. The results of scanning electron microscopy (SEM) studies showed that with increasing the solution treatment temperature from 1275°C (3h) to 1330°C (3h), first, ϒʹ precipitates at dendritic regions dissolve and only after increasing the solution temperature to 1350°C (3h), complete solution of ϒʹ phase occurs. The full solution condition (1350°C-3h) will be used as the first step of the rejuvenation process of these blades in future studies.
پرونده مقاله
Journal of Advanced Materials and Processing
,
شماره1,سال
2
,
زمستان
2014
Homogeneous distribution of mullite in the matrix of alumina can be obtained through sol-gel method. In this work, nanopowder of alumina-mullite composite was synthesized with high homogeneity and high purity. So aluminum chloride hexahydrate and tetraethyl orthosilicat چکیده کامل
Homogeneous distribution of mullite in the matrix of alumina can be obtained through sol-gel method. In this work, nanopowder of alumina-mullite composite was synthesized with high homogeneity and high purity. So aluminum chloride hexahydrate and tetraethyl orthosilicate were used instead of alumina or mullite nanopowder. Studying the simultaneouse thermal analysis (STA) of mullite precursor reveals two endothermic peaks at 145 and 240°C due to dehydration and removal of the molecular water and the chloride component. An exothermic peak is also detected at 855°C. According to the XRD patterns of alumina-15vol.% mullite precursors calcined at different temperatures, crystallization of transitional alumina phases (γ, κ) occurs approximately at 800°C. Then these phases transform to α alumina approximately at 1000°C. XRD patterns of alumina-15%vol. mullite which were calcined at different temperatures show peaks of mullite relating to 1000°C. The specific surface area of this nanopowder calcined at 900°C was calculated to be 120.9±0.5 m2/g. The nanopowder was observed by TEM.
پرونده مقاله
فرآیندهای نوین در مهندسی مواد
,
شماره4,سال
17
,
پاییز
1402
در این پژوهش رفتار شوک حرارتی ، سه نوع پوشش سد حرارتی زیرکونیای پایدار شده با ایتریا (YSZ) ، پوشش لایهای زیرکونیای پایدار شده با ایتریا و پوشش مولایت (YSZ/Mullie) و پوشش گرادیانی از زیرکونیای پایدار شده با ایتریا و مولایت (YSZ/Mullie) بر روی سوپر آلیاژ پایه نیکل اینکون چکیده کامل
در این پژوهش رفتار شوک حرارتی ، سه نوع پوشش سد حرارتی زیرکونیای پایدار شده با ایتریا (YSZ) ، پوشش لایهای زیرکونیای پایدار شده با ایتریا و پوشش مولایت (YSZ/Mullie) و پوشش گرادیانی از زیرکونیای پایدار شده با ایتریا و مولایت (YSZ/Mullie) بر روی سوپر آلیاژ پایه نیکل اینکونل 738 کم کربن به همراه لایه میانی پوشش داده شده با روش اسپری پلاسمایی مقایسه شد. با استفاده از میکروسکوپ الکترونی روبشی(SEM)، و پراش اشعه ایکس(XRD)، بررسی ریزساختار و آنالیز فازی انجام شد. درصد تخلخل و شوک پذیری پوششها در دمای °C1100 مورد بررسی و مقایسه قرار گرفت. نتایج نشان داد که با افزایش مولایت به صورت لایهای و گرادیانی بر روی پوشش YSZ از میزان حفرات و تخلخل ها کاسته میشود که این پدیده به علت افزایش مقادیر ذرات ذوب شده مولایت میباشد. درصد تخلخل مربوط به پوشش لایهای و گرادیانی از مولایت به ترتیب برابر با 8 و 5/3 درصد به دست آمد. با استفاده از نتایج آزمون شوک حرارتی مشخص شد طول عمر پوشش لایهای از مولایت از پوشش گرادیانی مولایت و پوششYSZ بیشتر است. بیشینه طول عمر پوشش لایهای از مولایت هفتاد سیکل ده دقیقه ای در کوره با دمای °C1100 ثبت شد. در شرایط آزمون شوک حرارتی طول عمر پوششهای گرادیانی و YSZ به ترتیب 60 و 25 سیکل اندازه گیری شد. پوششهای گرادیانی از مولایت در شوک حرارتی درصد انقباض بیشتری را نسبت به پوشش لایهای مولایت از خود نشان دادند.