Influence of Friction Stir Welding Parameters on Mechanical and Metallurgical Properties in Lap Joints of 5456Aluminum Alloy

Subject Areas : journal of New Materials

منصور مردعلی زاده ¹ (دانشجوی دکتری مهندسی مکانیک، دانشگاه صنعتی مالک اشتر، مجتمع دانشگاهی مواد و فناوری ساخت، تهران)
محمد علی صفرخانیان ² (استادیار، دانشگاه صنعتی مالک اشتر، مجتمع دانشگاهی مواد و فناوری ساخت، تهران)
محمد رضا سلیمانی یزدی ³ (دانشیار، مهندسی مکانیک، دانشگاه امام حسین(ع)، دانشکده مهندسی مکانیک، تهران)

Received: 2015-09-09 Accepted : 2019-06-23 Published : 2019-06-22

Keywords: mechanical properties, Friction Stir Welding, 5456 Aluminum Alloy, Lap Joint,

Abstract :

The research is based on experimental tests, lap joint welding of 5456 aluminum alloy was carried, so that the hard working H321 sheet with the thickness of 5 mm was placed on an annealed sheet with the thickness of 2.5 mm and has been investigating the simultaneous effects of parameters such as rotation speed and welding speed on metallurgical and mechanical properties in friction stir welding process. The results showed that increasing of rotation speed and reducing of welding speed (increase of welding step) causes increased heat input, increase vertical flux, increase hook height and reduction in effective Sheet thickness and it is causing the failure from the thermomechanical zone where the maximum heat input applied also, increasing of welding speed causes reduction in the material mixing and hook height and it causes an interface failure. It was observed with an examination of the results due to the differences in thickness of the sheets, existence of hook defect and its appropriate height and orientation is useful in this joint and causes an increase in strength and failure was in the base metal of the sheet with a thickness 2.5 mm in a tensile test.

References:

References:

[1]               W.M. Thomas, E.D. Nicholas, J.C. Needham, M.G. Murch, P. Templesmith, C.J. Dawes, Patent Application, No. 9125978.8, 1991.

[2]               H. Lombard, D.G. Hattingh, A. Steuwer, M.N. James, Optimising FSW process parameters to minimize defects and maximize fatigue life in 5083-H321 aluminium alloy, Engineering Fracture Mechanics 75 ,pp. 341-354, 2008.

[3]               R.S. Mishraa, Z.Y. Mab, Friction stir welding and processing, Materials Science and Engineering, Vol. 50, pp. 1–78, 2005.          

[4]               Mats Ericsson, Lai-Zhe Jin, Rolf Sandstrom, Fatigue properties of friction stir overlap welds, International Journal of Fatigue, pp. 57-69, 2007.  

[5]               D. Fersini, A.Pirondi, Fatigue behavior of Al2024-T3 fricyion stirs welded lap joints, Engineering Facture Machanics, 2006.

 

 

[6]               L. Dubourg, A. Merati, M. Jahazi, Process optimization and mechanical properties of friction stir lap welds of 7075-T6 stringers on 2024-T3 skin,
Materials and Design, pp. 3324-3330, 2010.

[7]               X. Cao, M. Jahazi, Effect of tool rotational speed and probe length on lap joint quality of a friction stir welded magnesium alloy, Materials and Design, pp. 32, 1-11, 2011.           

[8]               American Welding Society Committee D17.3, Specification for Friction Stir Welding of Aluminum Alloys for Aerospace Hardware, American Welding Society (AWS), Miami, Edition.1, No. 17.3, 2010.  

[9]               M. Kathleen, et. al., Metals Handbook: Metallography and Microstructure, American Society for Metals (ASM), Vol.9, Ninth edition, pp. 352-354, 1985.     

[10]           M. Ericsson, L.Z. Jin, R. Sandstrom, Fatigue properties of friction stir overlap welds, International Journal of Fatigue, pp. 57-69, 2007.       

[11]           G. Buffa, G. Campanile, L. Fratini, Friction stir welding of lap joints: Influence of process parameters on the metallurgical and mechanical properties, Materials Science and Engineering a 519, pp. 19–26, 2009.        

[12]           H.B. Chen, K. Yan, T. Lin, S.B. Chen, C.Y. Jiang, The investigation of typical welding defects for 5456 aluminum alloy friction stirs welds, Materials Science and Engineering A, pp.64-69, 2006.           

[13]           Y.C. Chen, K. Nakata, Friction stir lap joining aluminum and magnesium alloys, Scripta Matrialia 68,pp. 433-436, 2008.

[14]    م. عزیزیه، ع. صادقی،ا.ح. کوکبی،" بررسی ریزساختار و ویژگی‌های مکانیک اتصال اصطکاکی اغتشاشی آلومینیوم 1100 به ZA31"، مجله مواد نوین، دوره 2، شماره 6، ص. 1 تا 12، زمستان 1390.