In this work, ZnO/SiO2 nanoparticles were prepared using sol-gel method, and platinum particles were loaded on ZnO/SiO2 nanoparticles by photoreductive method. Samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and Fourier transform infrared spectroscopy (FT-IR). The XRD patterns showed that the zinc oxide samples have a wurtzite structure (hexagonal phase). The crystallite size calculated by Scheerer’s equation is ~ 32 nm. For photocatalytic test, decomposition of Rhodamine B (RB), as an organic pollutant, was carried out. A comparison of degradation between bare catalyst and platinum loaded ZnO/SiO2 nanoparticle under UV-Vis light irradiation shows that the Pt- ZnO/SiO2 photocatalyst is more efficient than ZnO/SiO2 nanoparticles. Also, the activity of ZnO/SiO2 nanoparticles in the visible light are minimal, while loading of Pt in zinc oxide network displaced the band gap toward longer wavelengths (visible light) and improved the photocatalysis activity of ZnO/SiO2 in the range of visible light. تفاصيل المقالة

نانو فتوکاتالیست‌های TiO2/SiO2و Pt- TiO2/SiO2 به روش سل- ژل سنتز شده اند برای بررسی ساختار و ویژگی‌های فتوکاتالیست‌ها از روش‌های .,XRD SEM ,ICP, ,FT-IR و UV-vis استفاده شده است. اندازه ذرات با استفاده از معادله شرر 7nm تعیین شده است. تصویر TEM و نتیجه‌های ICP حضور تیتانیم، سیلسیم و پلاتین را تایید می‌کنند. به منظور بررسی و مقایسه فعالیت فتوکاتالیتیکی TiO2/SiO2 و Pt- TiO2/SiO2 تخریب نوری رنگ رودامین بیی در محیط آبی تحت تابش پرتو فرابنفش و مرئی مطالعه شد. کاهش غلظت رودامین بی با استفاده از طیف‌بینی Uv-vis مورد بررسی قرار گرفت. نتیجه‌های این تخریب نشان دهنده‌ی این است که در نور مرئی Pt- TiO2/SiO2 در مقایسه با TiO2/SiO2 فعالیت فتوکاتالیتیکی بهتری دارد. تفاصيل المقالة