The ZnO/SiO2 semiconductor nanophotocatalysis was synthesized via sol-gel method. Also, theplatinum particles were loaded on the ZnO/SiO2 nanoparticles by photoreductive method. Thestructure of catalyst was confirmed by X-ray diffraction (XRD), scanning electron microscopy(SEM) andfourier transform infrared spectroscopy (FT-IR). The XRD patterns of ZnO particlesdisplayed the nanoparticles have a wurtzite structure (hexagonal phase). The crystallite sizes werecalculated using Scheerer’s equation and were around 32nm. For photocatalytic test, decompositionof Malachite Green oxalate (MG), as an organic pollutant was carried out by synthesized catalyst. Acomparison of degradation between bare catalyst and platinum loaded ZnO/SiO2nanoparticle underUV-Vis light irradiation shows that the Pt-ZnO/SiO2 photocatalyst is more efficient than ZnO/SiO2nanoparticles. Also, the activity of ZnO/SiO2nanoparticles in the visible light are minimal, whileloading of Pt in zinc oxide network displaced the band gap toward longer wavelengths (visiblelight) and increased the photocatalysis activity of ZnO/SiO2 in the range of visible light. تفاصيل المقالة

In this work, ZnO/SiO2 nanoparticles were prepared using sol-gel method, and platinum particles were loaded on ZnO/SiO2 nanoparticles by photoreductive method. Samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and Fourier transform infrared spectroscopy (FT-IR). The XRD patterns showed that the zinc oxide samples have a wurtzite structure (hexagonal phase). The crystallite size calculated by Scheerer’s equation is ~ 32 nm. For photocatalytic test, decomposition of Rhodamine B (RB), as an organic pollutant, was carried out. A comparison of degradation between bare catalyst and platinum loaded ZnO/SiO2 nanoparticle under UV-Vis light irradiation shows that the Pt- ZnO/SiO2 photocatalyst is more efficient than ZnO/SiO2 nanoparticles. Also, the activity of ZnO/SiO2 nanoparticles in the visible light are minimal, while loading of Pt in zinc oxide network displaced the band gap toward longer wavelengths (visible light) and improved the photocatalysis activity of ZnO/SiO2 in the range of visible light. تفاصيل المقالة

نانو فتوکاتالیست‌های TiO2/SiO2 و V2O5/ TiO2/SiO2 به روش سل- ژل تهیه شده‌اند.,XRD SEM ,FT-IR و UV-Vis برای بررسی ساختار و ویژگی‌های فتوکاتالیست‌ها استفاده شده‌اند. اندازه ذرات با استفاده از معادله شرر 7nm به دست آمده است. نتایج XRD و FT-IR حضور V2O5، TiO2 و SiO2 را تایید می‌کنند. به منظور بررسی و مقایسه فعالیت فتوکاتالیستی TiO2/SiO2 و V2O5/ TiO2/SiO2 تخریب نوری منو و دی کلرو بنزن در محیط آبی تحت تابش نور فرابنفش و مرئی انجام شد. کاهش غلظت منو و دی کلرو بنزن با استفاده از طیف سنجی UV-Vis مورد بررسی قرار گرفت. نتایج این تخریب نشان دهنده این است که در نور مرئی V2O5/ TiO2/SiO2 در مقایسه با TiO2/SiO2 فعالیت فتوکاتالیستی بهتری دارد. تفاصيل المقالة

نانو فتوکاتالیست‌های TiO2/SiO2و Pt- TiO2/SiO2 به روش سل- ژل سنتز شده اند برای بررسی ساختار و ویژگی‌های فتوکاتالیست‌ها از روش‌های .,XRD SEM ,ICP, ,FT-IR و UV-vis استفاده شده است. اندازه ذرات با استفاده از معادله شرر 7nm تعیین شده است. تصویر TEM و نتیجه‌های ICP حضور تیتانیم، سیلسیم و پلاتین را تایید می‌کنند. به منظور بررسی و مقایسه فعالیت فتوکاتالیتیکی TiO2/SiO2 و Pt- TiO2/SiO2 تخریب نوری رنگ رودامین بیی در محیط آبی تحت تابش پرتو فرابنفش و مرئی مطالعه شد. کاهش غلظت رودامین بی با استفاده از طیف‌بینی Uv-vis مورد بررسی قرار گرفت. نتیجه‌های این تخریب نشان دهنده‌ی این است که در نور مرئی Pt- TiO2/SiO2 در مقایسه با TiO2/SiO2 فعالیت فتوکاتالیتیکی بهتری دارد. تفاصيل المقالة