The effect of Mn doping on structural, magnetic and optical properties of TiO2 nanoparticles
alireza razeghizadeh
1
(
department of physics, faculty of science payamenoor university, Tehran, Iran.
)
elham elahi
2
(
Department Physics, Faculty of science, Payamenoor University, IRAN
)
vahdat rafee
3
(
department of physics, faculty of science, payamenoor university, tehran, iran
)
Keywords: Sol-gel method, Magnetic properties, Mn-doped, TiO2 Nano-powders,
Abstract :
The aim of this paper is to study the effect of Mn concentration on the structural, magnetic and optical properties of TiO2 nanoparticles. TiO2 nano powders with Mn concentration of 0%, 0.2%, 1% and 5% were synthesized by the sol-gel method. The structural, surface morphology and average crystal grain size, optical, magnetic properties and chemical compounds of the samples are studied using XRD, FE-SEM, Uv-Vis, VSM and EDX analysis respectively. The results indicate that the samples are crystallized at anatase phase. Also, the average size of the nanoparticles is decreased by increasing Mn doping percent. The study of the optical properties shows that the absorption maximum dislocates toward higher wavelengths by adding Mn to the sample. This shift may be ascribed to the enhanced trapped electron absorption caused by the Mn-doped ions. The optical energy band gap of the doping samples shows significant reduction rather the pure state. The samples show significant paramagnetic behavior when the Mn concentration is 5%.
The effect of Mn doping on structural, magnetic and optical properties of TiO2 nanoparticles
Abstract:
The aim of this paper is to study the effect of Mn concentration on the structural, magnetic and optical properties of TiO2 nanoparticles. TiO2 nano powders with Mn concentration of 0%, 0.2%, 1% and 5% were synthesized by the sol-gel method. The structural, surface morphology and average crystal grain size, optical, magnetic properties and chemical compounds of the samples are studied using XRD, FE-SEM, Uv-Vis, VSM and EDX analysis respectively. The results indicate that the samples are crystallized at anatase phase. Also, the average size of the nanoparticles is decreased by increasing Mn doping percent. The study of the optical properties shows that the absorption maximum dislocates toward higher wavelengths by adding Mn to the sample. This shift may be ascribed to the enhanced trapped electron absorption caused by the Mn-doped ions. The optical energy band gap of the doping samples shows significant reduction rather the pure state. The samples show significant paramagnetic behavior when the Mn concentration is 5%.
Keywords: Mn-doped, TiO2 Nano-powders, sol-gel method, magnetic properties
PACC: 8120E, 6116D, 7550P, 6170T
1- Introduction
TiO2 is a safe substance for human and environment. This material has industrial importance because of having the energy band gap 3.2 e V (at anatase phase), considerable chemical resistance, and the high number of the solvents in a wide range of PH, transmittance and the high refraction coefficient [1-3]. TiO2 exists in three crystallite forms: anatase, rutile, and brookite [4]. Anatase type TiO2 is a crystalline structure as the tetragonal system and is photochemically more active than the others. Rutile type structural of TiO2 also is a tetragonal crystal structure and this type used as white pigment in paint. Brookite type structural of TiO2 is an orthorhombic crystalline structure. Therefore, TiO2 is has applications in various products such as solar cells, capacitors, paint pigments, sunscreen lotions and electrochemical electrodes [5]. TiO2 is usually better in the anatase phase because of its high photocatalytic activity. Also, TiO2 at anatase phase was found to be a superior photocatalytic material for purification and disinfection of water and air, as well as remediation of hazardous waste [6].
This material has been drawing quickly increasing attention from researchers because of its potential in magneto-electronic applications [7-9]. TiO2 doped with Fe, [10] Co, [11] Mn, [12] and other elements have been prepared by hydrothermal [13], synthesis spray under heat [14], sol-gel of spin coating [15], dip-coating [16], magnetron sputtering RF [17] and other methods. [18-20]
Recently, dilute magnetic semiconductor (DMS) is the main subject in the magnetic semiconductor field. This is made based on semiconductors that were doped with transitional metals. They are semiconductor substances that present good magnetic and semiconductor properties and they have been used widely for spintronic device [21]. Also, TiO2 -based diluted magnetic semiconductor (DMS) with room temperature ferromagnetism was successfully prepared by Matsumoto et al. [22]
In this paper, we investigated the effect of doping percent on structural, optical and magnetic properties of the nanoparticles by preparing TiO2 nanoparticles prepared by the sol-gel method at anatase phase and then these doped with the various percent of Mn.
2- Experimental
2-1- Preparation of Sol-gel TiO2 and Mn-doped TiO2 nano powders
Sol-gel method and thermal treatment at 5000C were used to make Mn-doped TiO2 nano powder for 2hrs. Titanium isopropoxide (Merck, 99% Ti [OCH (CH3)2]4) was used as a precursor. The process was as follow. First, we added 4.23 ml titanium isopropoxide to 20 ml ethanol and kept it for 30 min at room temperature under magnetic stirring (magnetic magnet and stirrer Hot Plate Model Genway 1000) to obtain initial precursor solution. Then we combined.0.26 ml distilled water, 3.4ml Acetic acid (Merck, 99.9%) and 5 ml ethanol and added it to the initial solution with the rate one drop per second while it was under constant magnetic stirring. After that we added a predetermined quantity of Mn (NO3)2 to TiO2 sol and stir it for one hour to obtain Mn-doped TiO2 anatase nano powder. The quantity of the additive matter is estimated as follows [23]:
(1)
Where, NTi and NMn are mole values of Ti and Mn respectively.
In the following, the prepared samples were transmitted to the furnace (electric furnace with the maximum operating temperature 1100°C model Thermal Defign, Lenton) and kept under thermal treatment at 500°C for 2hrs because in this temperature the dominant phase is Anatase [24].
Regarding that anatase phase of TiO2 is the desired phase and it is dominated at 500°C and when the temperature of annealing is increased the anatase phase changes to rutile phase [25], therefore maximum temperature remains constant at 500°C.
3- Results and discussion
3-1- The structure of Mn-doped TiO2 nano powders
X-ray power diffraction analysis (XRD) was done to study crystallite and phase structure of Mn-doped TiO2 anatase, powder samples Ti1-X MnxO2 in which Mn is transition metal and x is the concentration of the additive matter (x=0%, 0.2%, 1%, 5%). This analysis was done using XRD analysis (model X pert, made by Philips Company doping and model Seifert 3003). Since the anatase phase was dominated at 500°C, the diffraction pattern of all samples confirm the presence of TiO2 anatase phase as a dominate phase in the system which was in good agreement with Standard Card 1272-021-00 related to TiO2 anatase phase and there is no additive peak related to another phase next to this phase [26]. This agreement is well seen in Fig. 1-a.
As it known from XRD results, XRD peaks have become broader by increasing concentration additive from 0.2% to 5%. In the most of the cases, broadening is due to decrease the grain size and structure disordering [27-28]. The size of the crystallites estimated by using Debye-Scherer's relationship [29].
(2)
Figure 1. X-ray diffraction spectrum,(a) Standard Card of TiO2 anatas phase, Mn and peaks of C4 sample (b)Ti1-xMnxO2 nano powder annealed at 500°C related to the samples with different percent Mn, sample C1: x=0%, sample C2: x=0.2%, sample C3: x= 1%, sample C4: x= 5%. (c) The shift of peaks via Mn percent
The Fig. 1-a shows that the position of the peaks in the pure and Mn doped of the XRD pattern slightly shifted by changes in Mn percent of the sol. Also, the results are given in Tab.1.
Also, crystal lattice constants for planes 004 and 101 are measured as fallows [30].
(3)
Table1: the lattice constants and the average size of the sample crystallites.
D(nm) | Lattice constants (Å) | Mn –doped (%) | Sample | |
c | a=b | |||
13.38 | 9.4992 | 3.7689 | 0 | C1 |
13.03 | 9.4548 | 3.7623 | 0.2 | C2 |
12.16 | 9.3251 | 3.7621 | 1 | C3 |
11.36 | 9.2125 | 3.7620 | 5 | C4 |
Where, d is distance between continuous crystal planes, (hkl) is Miller index which shows crystal growth direction and a,b,c are lattice constants that are as follow for anatase: a=b≠c
The average size of the crystallite was 13.38nm, 13.03nm, 12.16nm and 11.36nm for samples C1, C2, C3 and C4 respectively. By comparing the average size of the crystallites, we find that increasing the percent of Mn leads to decrease the size of the crystallites.
The ionic radius of the Mn4+ (0.670) as an addative in the octahedral site is smaller than the ionic radius Ti4+(0.745), so Ti4+ can replace with the Mn4+ cation in the TiO2 lattice. As a result, the decrease of the lattice constant C in the Mn-doped sample lattice can be due to the smaller ionic radius of Mn [31].
The X-pert analysis of X-ray diffraction spectrum of sample C4 shows at Fig. 2. The presence of manganese is well confirmed by Fig. 2.
Figure 2. X-ray diffraction spectrum of Ti1-xMnxO2 nano powder annealed at 500°C related to the samples with Mn, sample C4: x= 5%.
Considering XRD spectrums, it is clear observable that when the percent of Mn increase, the anatase peaks move toward to decrease 2θ [32].
3-2- morphology of Mn-doped TiO2 nano powders
SEM analysis was used to study morphological properties of the surface and also calculate the average size of the nano particles (scanning electron microscope SEM, Model S4160, made by Hitachi Company). Fig. 3 shows SEM results.
(c2) |
(c1) |
(c4) |
(c3) |
Figure. 3: SEM images of the annealed Ti1-xMnxO2 at 500°C and with different concentrations of the Mn: C1=0%, C2=0.2%, C3= 1% and C4=5%.
As can be seen, the grain size is influenced by changing of a percent of Mn. The average size of the grain is 20, 25, 28 and 30nm for C1, C2, C3 and C4 respectively. These results show that the decrease grain size is due to the increase of the percent of Mn which is in agreement with the results of the obtained crystallites size by the XRD.
Fig. 4 show the approximated average size of the particles using SEM device based on the percent of Mn respectively.
Figure. 4: the average size of the nanoparticles with different Mn content.
3-3-Optical properties of Mn-doped TiO2 nano powders
UV-Vis spectrophotometer (Model Varian-Cary 500Scan) was used to calculate the optical energy band gap of the samples.
Figure. 5: the UV-Vis absorption spectra of (a) TiO2 pure nano powder (b) Ti1-x MnxO2 nano powder with the percent of Mn equal to 5% annealed at 500°C.
Fig. 5 shows the absorption of the TiO2 pure and Ti1-x MnxO2 nano powders (Mn-doped TiO2 nano powder) with the percent of Mn equal to 5%. These samples annealed at 500°C. As you see TiO2 pure nano powder shows the absorption maximum at 380-390nm of the absorption area while TiO2 nano powder synthesized with Mn with the 5% concentration has an absorption maximum at the 480-490nm.
The optical energy band gap of the samples calculated as fallowing relation [33]:
(4)
Where, h is the plank constant (h=6.62 ×10 -34), c is the light speed (c= 3× 108 m/s) and λ is the wavelength maximum. The amount of estimated energy gap for the TiO2 pure nano powder based on λ=388nm is E=2.3Ev while it is E=6.2 eV for the synthesized TiO2 nano powder with 5% concentration of the Mn based on λ= 480nm. This show that by doping Mn ions at samples and by considering the different ionic radius of the Mn and TiO2, the variation between valance band and the conduction band of TiO2 lead to change the band gap and shift the absorption edge toward the visible area [34]. A number of band gap decreases [35-37] and this change lead to increase the photocatalytic sensitivity of the TiO2 [36].
3-4- Magnetic properties of Mn-doped TiO2 nano powders
After investigating the magnetic behavior of the samples using VSM, we reported that Ti1-x MnxO2 nano powder samples with the Mn concentrations 1%, 0.2% and 0%, annealed at 500°C do not show reasonable magnetic behavior, while the sample show paramagnetic behavior by increasing the Mn concentration to 5%. Fig. 6 describes the magnetic hysteresis (M-H) for Ti1-x MnxO2 nano powder with the Mn concentration at %5 and annealed at 500°C. This sample has effective field HC 20.43Oe and its hysteresis is
. Since The TiO2 do not show the magnetic properties, so the observed paramagnetic can be due to the bond of the Mn ions to TiO2 lattice. According to the obtained results from XRD spectrum of the samples in this research that show the Ti+4 replaced with Mn+4 at TiO2 lattice, it can be concluded that Mn ions substitution in TiO2 lattice can be the reason for the paramagnetic behavior. Also not observing magnetic behavior with the concentration less than 5% can be due to the little Mn concentration because it cannot create the magnetic order for the samples.
Figure. 6: The chart of the magnetization variations as a function of M-H forcing of the Ti1-x MnxO2 nano powder with x=5% at the room temperature.
3-5- The composition of Mn-doped TiO2 nano powders
EDX was used to study chemical composition and chemical analysis energy. The Mn concentration was measured using EDX analysis. Fig. 7 shows the typical spectrum of the EDX analysis for the powder sample with 5% concentration. This confirms the presence of Mn in the structure which indicates Ti+4 replaced by Mn+4 in the TiO2 lattice.
Figure. 7: EDX image of Ti1-x MnxO2 nano powder with 5% of the Mn concentration and annealed at 500°C.
4- Conclusions
In this paper, structural, magnetic and optical properties of TiO2 nanoparticles are studied by preparing them with doping percent 0, 0.2, 1 and 5% using the sol-gel method. The results of the X-ray diffraction analysis confirm the anatase phase of the samples and show that when the doping percent increases, the size of nanoparticles significantly decreases because the ionic radius of the Mn is smaller than that of the Ti. Also SEM results show that as the doping percent increases, the surfaces are more smother and they will have a thinner gradation. The increase in the average size of the particles confirms the X-ray diffraction results. In the following, EDX results confirm Mn-doping at the samples. The analysis of the absorption spectrum of the spectrophotometry for the samples with %5 Mn-doping and samples without doping show the displacement at the absorption maximum of the pure nano powder from 380-390nm than to the doped samples with 5% Mn concentration at 480-490nm. Also, results related to the energy gap estimation show the decrease band gap from 2.3 eV to 2.6 eV for the pure sample and the doped sample with 5% Mn, respectively. At last, as the VSM show that the samples without doping and the samples with doping do not indicate significant paramagnetic properties at 0, 0.2 and 1%. But the doping with 5% of the sample not only show good paramagnetic properties but also it has effective field HC 20.43Oe and magnetic hysteresis is 
emu.
References
[1]. Hsu, J. P, and Nacu, A., On the factors influencing the preparation of nanosized titania sols, Langmuir 19(10), 4448-4454 (2003).
[2]. Irie, H., Watanabe. Y., and Kazuhito Hashimoto, K., Carbon-doped anatase TiO2 powders as a visible-light sensitive photocatalyst, Chemistry Letters 32(8), 772-773 (2003).
[3]. Nezameddin, D., Salari, D., and Behnasuady, M. A., Decomposition of Anionic Sodium Dodecylnemzene Sulfonate by UV/TiO2 and UV/H2O2 Processes a-Comparison of Reaction Rates., Iranian Journal of Chemistry and Chemical Engineering (IJCCE), 21(1): 55-65 (2002).
[4]. Puma, G.L., Bono, A., Krishnaiah, D. and Collin, J.G., 2008. Preparation of titanium dioxide photocatalyst loaded onto activated carbon support using chemical vapor deposition: a review paper. Journal of hazardous Materials, 157(2-3), pp.209-219.
[5]. Meacock, G., Taylor, K.D., Knowles, M.J. and Himonides, A., 1997. The improved whitening of minced cod flesh using dispersed titanium dioxide. Journal of the Science of Food and Agriculture, 73(2), pp.221-225.
[6]. Yu, H.F., Zhang, Z.W. and Hu, F.C., 2008. Phase stabilities and photocatalytic activities of P/Zn–TiO2 nanoparticles able to operate under UV–vis light irradiation. Journal of Alloys and Compounds, 465(1-2), pp.484-490.
[7]. Nam, J.E., Jo, H.J., Son, D.H., Kim, D.H. and Kang, J.K., February. Effect of Anti-Reflective Layer in Dye-Sensitized Solar Cells., In Applied Mechanics and Materials, 705, 320-323 (2015).
[8]. Weng, W., Higuchi, T., Suzuki, M., Fukuoka, T., Shimomura, T., Ono, M., Radhakrishnan, L., Wang, H., Suzuki, N., Oveisi, H. and Yamauchi, Y.,A High‐Speed Passive‐Matrix Electrochromic Display Using a Mesoporous TiO2 Electrode with Vertical Porosity., Angewandte Chemie,122(23),4048-4051(2010).
[9]. Chen, W., Tao, X., Zhang, J., Fang, Q. and Yang, J., Sol–Gel‐Processed SiO2/TiO2/ Methylcellulose Composite Materials for Optical Waveguides. Journal of the American Ceramic Society, 88(11), 2998-3002(2005).
[10]. Firooz AA, Nia BH, Beheshtian J, Ghalkhani M. 2017, Voltammetric Sensor Based on Fe-doped ZnO and TiO2 Nanostructures-modified Carbon-paste Electrode for Determination of Levodopa. Journal of Electronic Materials.;46(10):5657-63.
[11]. Eslami, A., Amini, M.M., Yazdanbakhsh, A.R., Mohseni‐Bandpei, A., Safari, A.A. and Asadi, A., 2016. N, S co‐doped TiO2 nanoparticles and nanosheets in simulated solar light for photocatalytic degradation of non‐steroidal anti‐inflammatory drugs in water: a comparative study. Journal of Chemical Technology and Biotechnology, 91(10), pp.2693-2704.
[12]. Ning, X., Wang, X., Yu, X., Zhao, J., Wang, M., Li, H. and Yang, Y., 2016. Outstanding supercapacitive properties of Mn-doped TiO2 micro/nanostructure porous film prepared by anodization method. Scientific reports, 6, p.22634.
[13]. Yang, Z., Wang, B., Cui, H., An, H., Pan, Y. and Zhai, J., 2015. Synthesis of crystal-controlled TiO2 nanorods by a hydrothermal method: rutile and brookite as highly active photocatalysts. The Journal of Physical Chemistry C, 119(29), pp.16905-16912.
[14].Dhanapandian, S., Arunachalam, A. and Manoharan, C., 2016. Effect of deposition parameters on the properties of TiO2 thin films prepared by spray pyrolysis. Journal of Sol-Gel Science and Technology, 77(1), pp.119-135.
[15]. Affendi, H., Hidayanti, I., Azhar, A., Ezira, N., Saad, M., Sarah, P. and Rusop, M., 2015. Nanostructured TiO2 Thin Film by Sol-Gel Spin Coating with Different Concentration. In Advanced Materials Research (Vol. 1109, pp. 529-533). Trans Tech Publications.
[16]. Ali, F.H., Twej, W.A. and Al-Khafaji, A., 2015. Structural and Optical Properties of Al-doped TiO2 Thin Films Prepared by Dip-Coating Method. Journal of Spectroscopy and Molecular Physics, 10(10), pp.91-96.
[17]. Safeen, K., Micheli, V., Bartali, R., Gottardi, G. and Laidani, N., 2015. Low temperature growth study of nano-crystalline TiO2 thin films deposited by RF sputtering. Journal of Physics D: Applied Physics, 48(29), p.295201.
[18]. Mazzolini, P., Russo, V., Casari, C.S., Hitosugi, T., Nakao, S., Hasegawa, T. and Li Bassi, A., 2016. Vibrational–Electrical Properties Relationship in Donor-Doped TiO2 by Raman Spectroscopy. The Journal of Physical Chemistry C, 120(33), pp.18878-18886.
[19]. Bahramian, A.R., 2016. Enhanced Photocatalytic Activity of Sol-Gel Derived Coral-like TiO2 Nanostructured Thin Film. Iranian Journal of Chemistry and Chemical Engineering (IJCCE), 35(2), pp.27-41.
[20]. Allafchian, A.R., Jalali, S.A.H., Amiri, R. and Shahabadi, S., 2017. Antibacterial activity of new magnetic Ag/TiO2 nanocomposite in silane sol–gel matrix. Journal of Materials Science: Materials in Electronics, pp.1-8.
[21]. Dietl, T. and Ohno, H., 2014. Dilute ferromagnetic semiconductors: Physics and spintronic structures. Reviews of Modern Physics, 86(1), p.187.
[22]. Matsumoto, Y., Murakami, M., Shono, T., Hasegawa, T., Fukumura, T., Kawasaki, M., Ahmet, P., Chikyow, T., Koshihara, S.Y. and Koinuma, H., 2001. Room-temperature ferromagnetism in transparent transition metal-doped titanium dioxide. Science, 291(5505), pp.854-856.
[23].P. I. Gauma and M. J. Mills, “Anatase-to-Rutile Transformation in Titania Powders”, J. Am. Ceram. Soc., Vol. 84, (2001), 619-622.
[24].O. Ergün, O. Karslioĝlu, A. Yilmaz and D. Üner, “Preparation and Characterization of Ordered TiO2 Photocatalysts: Films and Mesoporous Structures”, Turk. J. Chem., Vol. 31, (2007), 501-508.
[25]. P. I. Gauma and M. J. Mills, “Anatase-to-Rutile Transformation in Titania Powders”, J. Am. Ceram. Soc., Vol. 84, (2001), 619-622.
[26]. Lin H, Huang C P, Li W, Ni C, Shah S I and Tseng Y H 2006 Appl. Catal. B 68 1.
[27]. P. Sahu, M. De and M. Zdujić, “Microstructural Characterization of the Evoluted Phases of Ball-Milled a-Fe2O3 Powder in Air and Oxygen Atmosphere by Rietveld Analysis”, J. Mater. Chem. Phys., Vol. 82, (2003), 864-876.
[28]. V. Sepelák, U. Steinike, D. Chr. Uecker, S. Wibmann and K. D. Becker, “Structural Disorder in Mechanosynthesized Zinc Ferrite”, J. Sol. St. Chem., Vol. 135, (1998), 52-58.
[29]. Razeghizadeh, A., Mahmoudi Ghalvandi, M., Sohillian, F. and Rafee, V., 2017. The Effect of Substrate on Structural and Electrical Properties of Cu3N Thin Film by DC Reactive Magnetron Sputtering. Physical Chemistry Research, 5(3), pp.497-504.
[30]. Saha, J.K. and Podder, J., 2011. Crystallization of zinc sulphate single crystals and its structural, thermal and optical characterization. Journal of Bangladesh Academy of Sciences, 35(2), pp.203-210.
[31]. Peng, D., Fa-Min, L., Xin-An, Y. and Jian-Qi, L., 2008. Preparation, structure and ferromagnetic properties of the nanocrystalline Ti1-xMnxO2 thin films grown by radio frequency magnetron co-sputtering. Chinese Physics B, 17(2), p.721.
[32]. C. R. Estrellan , C. Salim and H. Hinode, "Photocatalytic activity of sol–gel derived TiO2 co-doped with iron and niobium", React Kinet Catal Lett. 98, (2009), p. 187-192.
[33]. A. Linsebigler , G. Lu , and J. T. Yates, Photo catalysis on TiO2 Surfaces: Principles, Mechanisms, and Selected Results, Chemical reviews, 95 (3) (1995) 735–758.
[34]. Dong Y.L., Won J.L., Jae Sung S. et al. Electronic surface state of TiO2 electrode doped with transition metals, studied with cluster model and DV-X method, Comput. Mater. Sci. -V. 30, 383-388 (2004).
[35]. Gomathi D. L., Nagaraju K., Narasimha M. B., Girish K. S., Enhanced photocatalytic activity of transition metal ions Mn2+, Ni2+ and Zn2+ doped polycrystalline titania for the degradation of aniline blue under UV/Solar light, J. Molec. Catal. A: Chem. -2010. - V. 328. - P. 44-52.
[36]. Umebayashi T., Yamaki T., Itoh H., Asai K. Analysis of electronic structures of 3d transition metal-doped TiO2 based on band calculations, J. Phys. Chem. Solids – 2002. – V. 63. – P. 1909–1920.
[37]. Choi W., Termin A., Hoffmann M.R. The role of metal ion dopants in quantum-sized TiO2: correlation between. photoreactivity and charge carrier recombination dynamics, J. Phys. Chem. – 1994. – V. 98. – P. 13669–13679.