Effect of Filler Metal Type on the Microstructure of Welded Joints of HP Heat-Resistant Steel Modified by Niobium

Subject Areas : Welding

Jamal Hussain Mansoor ¹ , Reza Dehmolaei ² , Mostafa Eskandari ³ , Seyed Reza Alavi Zaree ⁴

1 - Department of Materials Science & Engineering, Faculty of Engineering, Shahid Chamran University of Ahvaz, Ahvaz, Iran.
2 - Department of Materials Science & Engineering, Faculty of Engineering, Shahid Chamran University of Ahvaz, Ahvaz, Iran.
3 - Department of Materials Science & Engineering, Faculty of Engineering, Shahid Chamran University of Ahvaz, Ahvaz, Iran.
4 - Department of Materials Science & Engineering, Faculty of Engineering, Shahid Chamran University of Ahvaz, Ahvaz, Iran.

Received: 2024-06-11 Accepted : 2024-08-20 Published : 2023-05-01

Keywords: filler metal, microstructure, interface, weld metal, unmixed zone, epitaxial growth ,

Abstract :

In this research, HP heat-resistant steel modified by niobium was welded using the GTAW process and ER NiCr-3, ER NiCrMo-3, and MF filler rods. The microstructure of the base metal, weld metals, heat-affected zone, and interface between the base and weld metals was studied using optical and electron microscopes (FESEM) equipped with an EDS point analysis system. The microstructure of HP steel base metal with an austenitic matrix and chromium-rich and niobium-rich precipitates on the grain boundary was observed. All three weld metal microstructures have a fully austenitic matrix that is dendritically solidified. In all weld metal produced by three different weld wires, precipitates rich in chromium (M₂₃C₆ carbide) and precipitates rich in niobium and titanium (MC carbide) were observed. The microstructural studies showed that the interfaces between the base metal and weld metals are fully continuous and free of cracks and voids. An unmixed zone (non-homogeneous zone) with a large width was formed at the interface between the base metal and the ERNiCr-3 weld metal. Any unmixed zone was not observed at the interface of the base metal and weld metals of the ERNiCrMo-3 and MF steel. Epitaxial growth was observed at the interface between the base metal and weld metals of ER NiCrMo-3 and MF steel.

References:

[1] Siqueira de NC, Arenas MP, de Almeida PD, Araújo LS, Eckstein CB, Nogueira Jr L, de Almeida LH, Pereira GR. Characterization of the aging state of modified HP steels by ultrasonic signal processing and the effect of creep voids in the interdendritic region. Journal of Materials Research and Technology. 2018;7(3):361-5.
[2] Shinozaki K, Kuroki H, Nakao Y, Nishimoto K, Inui M, Takahashi M. Deterioration of weldability of long-term aged HP heat-resistant cast steel containing Nb, Mo, and W. Welding international. 1999;13(1):39-48.
[3] Rampat K, Maharaj C. Creep embrittlement in aged HP-Mod alloy reformer tubes. Engineering Failure Analysis. 2019; 100:147-65.
[4] Almeida de Soares GD, de Almeida LH, da Silveira TL, Le May I. Niobium additions in HP heat-resistant cast stainless steels. Materials Characterization. 1992;29(3):387-96.
[ 5] Barbabela GD, de Almeida LH, da Silveira TL, Le May I. Role of Nb in modifying the microstructure of heat-resistant cast HP steel. Materials characterization. 1991;26(3):193-7.
[6] Hsieh CC, Lai CH, Wu W. Effect of vibration on microstructures and mechanical properties of 304 stainless steel GTA welds. Metals and materials international. 2013; 19:835-44.
[7] Kou SD. Welding Metallurgy, New Jersy. USA. 2003;431(446):223-5.
[8] Dehmolaei R, Shamanian M, Kermanpur A. Effect of electromagnetic vibration on the unmixed zone formation in 25Cr–35Ni heat resistant steel/Alloy 800 dissimilar welds. Materials characterization. 2008; 59(12):1814-7.
[9] Dehmolaei R, Shamanian M, Kermanpur A. Microstructural characterization of dissimilar welds between alloy 800 and HP heat-resistant steel. Materials Characterization. 2008;59(10):1447-54.
[10] Dehmolaei R, Shamanian M, Kermanpur A. Factors affecting weldability improvement of dissimilar welds of aged HP stainless steel and alloy 800. International Journal of Iron & Steel Society of Iran. 2008;5(1):15-21.
[11] Sireesha M, Shankar V, Albert SK, Sundaresan S. Microstructural features of dissimilar welds between 316LN austenitic stainless steel and alloy 800. Materials Science and Engineering: A. 2000;292(1):74-82.
[12] Cui Y, Xu CL, Han Q. Effect of ultrasonic vibration on unmixed zone formation. Scripta materialia. 2006; 55(11):975-8.
[13] Lu Q, Chen L, Ni C. Improving welded valve quality by vibratory weld conditioning. Materials Science and Engineering: A. 2007;457(1-2):246-53.
[14] Baeslack WA, Lippold JC, Savage WF. Unmixed zone formation in austenitic stainless steel weldments. Welding Journal. 1979 Jun;58(6):168.
[15] Garner A. Corrosion of high alloy austenitic stainless steel weldments in oxidizing environments. Mater Perform 1982;21:9–14.
[16] Tuthill AH. Problems involved in testing for corrosion susceptibility in stainless steel welds are reviewed, and guidance is offered. Weld J. 2005;84(5):36-40.
[17] Lippold JC, Kotecki DJ. Welding metallurgy and weldability of stainless steels Lippold JC, Kotecki DJ. Welding metallurgy and weldability of stainless steels, John Wiley & Sons, Inc, 2005.
[18] Lippold JC. Welding metallurgy and weldability. John Wiley & Sons; 2014 Nov 24.
[19] Lukkari J, Moisio T. The Effect of the Welding Method on the Unmixed Zone of the Weld. Microstructural Science. 1979; 7:333-44.
[20] Metals Handbook, Properties and Selection: Stainless Steels, Tool Materials and Special-Purpose Metals, Vol. 3, 9th Edition; 1980.