Functionalization of carbon nanotube (CNT) was performed, during preparation of Fischer–Tropsch synthesis (FTS) via cobalt nanocatalysts, to modify the surface properties of CNT support. Common and functionalized CNT supported cobalt nanocatalysts were prepared using impregnation wetness method with cobalt loading of 15 wt.%. The catalysts were characterized by Brunauer–Emmett–Teller (BET), Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), temperature program reduction (TPR), H2 chemisorption, and transmission electron microscopy (TEM) technique. Most of the cobalt particles were homogeneously distributed inside the tubes and the rest on the outer surface of the functionalized CNT. Functionalization of CNT shifted the TPR reduction peaks to lower temperatures, improved the reduction degree, and increased the dispersion of cobalt particles and stability of catalysts. The proposed cobalt catalyst supported on functionalized CNT- (N-doped functionalized CNT) increased the FTS rate (g HC/gcat./hr), and CO conversion (%) from 0.1347, and 30 to 0.235, and 47 respectively, compared to that of the catalyst prepared by impregnation wetness method on common CNT. Catalysts supported on functionalized CNT also showed better stability. پرونده مقاله

Bagasse as a real biomass was converted to hydrogen rich gas via catalytic supercritical water gasification process. To find the effect of Cu on selectivity of products, Cu promoted Ni-γAl2O3catalysts were prepared with 1 to 20wt% Ni and 0.5 to 10wt% Cu loadings via impregnation method. Catalysts were characterized by ICP, BET, XRD, H2chemisorption and TEM technique as well CHNS analysis was carried out for elemental analysis of bagasse. The biomass supercritical water gasification process was performed in a batch micro-reactor at 400oC and 240 bars. The total gas yield increased with increasing in Ni and Cu loadings up to 15wt% Ni and 7.5 wt% Cu and became approximately constant. The catalytic process increased hydrogen yield to 9.5, CO yield to 2.2 and light hydrocarbons to 0.59 mmol/g bagasse. Total H2selectivity (THS) ratio increased with increasing in Ni and Cu loading reached a maximum at 15%wt Ni and 7.5%wt Cu and then began to decrease. پرونده مقاله

در مطالعه حاضر، یک روش پردازش تصویر با یک رنگ‌سنج دست‌ساز برای اندازه‌گیری مقادیر اندک نیتریت در نمونه‌های آبی متفاوت ارائه شده است. روش پیشنهادی مبتنی بر یک تلفن همراه هوشمند برای به‎دست آوردن مقادیر فضای رنگی RGB مربوط به تصاویر دیجیتالی است. برای تبدیل نیتریت به یک فراورده رنگی از 4-‎نیتروآنیلین و ‎-αنفتول استفاده شد. سپس، استخراج فاز جامد مغناطیسی برای استخراج رنگ آزو ‎به‎دست آمده، مورداستفاده قرار گرفت. در استخراج فاز جامد مغناطیسی، گرافن مغناطیسی به‌عنوان جاذب و استون به‌عنوان حلال شوینده به‌کار برده شد. پس از تهیه تصاویر دیجیتالی فاز استخراجی با یک گوشی تلفن همراه و آزمون آن‎ها با استفاده از نرم‌افزار Color Grab، مقادیر R در به‌دست آوردن نشانک تجزیه‌ای مرتبط با غلظت نیتریت مورد استفاده قرار گرفت. عامل‎های تجربی موثر بر واکنش و بازده استخراج نیز بررسی شد. تحت شرایط بهینه، حد تشخیص و حد کمی روش به ترتیب 2/1 و 4 میکروگرم بر لیتر به‎دست آمدند. نمودار معیارگیری در گستره 10 تا 300 میکروگرم بر لیتر با ضریب همبستگی 0/993 خطی شد. انحراف استاندارد نسبی برای غلظت‌های 100 و 30 میکروگرم بر لیتر به ترتیب 2/2 و 3/9 به‌دست آمد. روش پیشنهادی با موفقیت برای اندازه‌گیری نیتریت موجود در نمونه‌های آبی متفاوت به‎کار برده شد. پرونده مقاله