Foam glass-ceramics are porous material with the desired strength. In this work, steel slag was mixed with soda lime glass in (20, 40, 50, 60, 70 wt. %,denoted by SG20,SG40,SG50,SG60,SG70) and 5 wt.% SiC. Giving to Hot stage microscopy images, glass-slag composite's contraction starts at 1050ºC. According to the SEM micrographs the tunnel-like pore porosity resulted from the decomposition of carbide phase were formed. The sizes of pors varies in 500 - 1000 μm range. More over by the 50 wt. % soda lime glass addition and sintering at 1200 ° C, the spherical porosity were formed and the size of the porosity were reduced to 50 μm in these composites. Also, by the the glassy phase increasing, the total porosity was increased to 80%, the density decreased to 0.8g / cm3in SG40. This composite as a porous material has 2 to 5 MPa bending strengths. Wollastonite phase was detected in these composite. پرونده مقاله

در این پژوهش عوامل موثر بر رفتار فومی شدن و تبلور شیشه انتخابی بر پایه فاز دایوپساید، با افزودن 2 درصد وزنی‌SiC به عنوان عامل فوم‌زا به روش زینتر‌مورد بررسی قرار گرفت.‌بررسی‌ها نشان داد بالا بودن دمای نرم شوندگی شیشه انتخابی و همچنین‌وقوع تبلور در آن یکی از عوامل اصلی در فومی نشدن آن می‌باشد. در این راستا تاثیر افزودن اکسید بور و سرب بر قابلیت فوم دار شدن ‌ شیشه‌ ها نیز موردارزیابی قرار ‌گرفت. ننایج حاصل نشان داد که با افزودن اکسید سرب به علت بهبود قابلیت تر شوندگی شیشه با ذرات SiC مورد نظر، افزایش بازیسیته نوری و افزایش فاصله دمایی بین دمای انتقال به شیشه و دمای شروع تبلور، فوم دار شدن بهبود یافت. زاویه تر شوندگی در فصل مشترک شیشه-SiC‌در مورد ترکیب فاقد اکسید سرب°85 و در مورد ترکیب حاوی 15 درصد وزنی اکسید سرب به°55 کاهش یافت. در صورتی که در شیشه های حاوی اکسید بور علی رغم وسیع شدن محدوده دمایی بین دمای شروع پیک تبلور و دمای انتقال به شیشه ، به علت کاهش پارامتر بازیسیته نوری فوم دار شدن به طور مطلوبی صورت نگرفت. پرونده مقاله

پرونده مقاله