Current efficiency and energy consumption are two important factors in sodium ferrate synthesis. In this article, sodium ferrate was produced by the electrochemical method and the effects of different synthesized parameters such as applied current density, sodium hydroxide concentration and temperature on current efficiency and energy consumption have been studied. Decomposition of sodium ferrate, anode passivation and deviations in anodic and cathodic reaction rates with time have been tested by weight loss test, potentiodynamic polarization, and UV-visible spectroscopy, respectively. Also, the impact of each one on current efficiency and its consequence on energy consumption rate were studied. The results showed that the optimum conditions were 3.94 mA/cm2, 16 M NaOH and 50 oC for applied current density, sodium hydroxide concentration, and temperature, respectively. In this situation, the current efficiency was calculated as 91.7% and the energy consumption reached 1.91 kW.h/kg. Keywords: Electrochemical method; Sodium ferrate; Alkaline solution; Current efficiency; Energy consumption. پرونده مقاله

راندمان تولید و انرژی مصرفی دو فاکتور مهم در تولید الکتروشیمیایی ذرّات فرات پتاسیم هستند. در این پژوهش تاثیر پارامترهای مختلف مانند دانسیته جریان اعمالی، غلظت الکترولیت KOH و دمای آن بر راندمان تولید و انرژی مصرفی بررسی شد. در دانسیته جریان 40 و الکترولیتM 13- KOH با دمای ℃ 70 شرایط بهینه تولید در مدت زمان 2 ساعت بدست آمد. در این شرایط راندمان تولید برابر % 63/84 و جریان مصرفی برابر kwh/kg05/5 بود. با بدست آمدن شرایط بهینه تولید، تاثیر گذشت زمان تولید بر راندمان تولید، خلوص، فازهای تشکیل شده و اندازه ذرّات فرات پتاسیم مورد بررسی قرار گرفت. با گذشت زمان در اثر تجزیه ذرّات فرات پتاسیم، ترکیبات هیدروکسیدی و اکسیدی آهن شکل میگیرند که باعث کاهش خلوص و راندمان تولید می‌گردد. اندازه ذرّات فرات پتاسیم به دو روش با استفاده از معادله دبای- شرر و شرر اصلاح شده اندازه گیری شد. با افزایش زمان تولید اندازه ذرّات فرات پتاسیم افزایش یافت. پرونده مقاله