Fabrication of Na-W Co-Doped Exfoliated G-C3N4 Nanoparticles for Methylene Blue Removal

محورهای موضوعی : Composite materials

Mohammad Javad Hakimi-Tehrani ¹ (Advanced Materials Research Center, Department of Materials Engineering, Najafabad Branch, Islamic Azad University, Najafabad, Iran.)
Seyed Ali Hassanzadeh Tabrizi ² (Advanced Materials Research Center, Department of Materials Engineering, Najafabad Branch, Islamic Azad University, Najafabad, Iran.)
Narjes Koupaei ³ (Advanced Materials Research Center, Department of Materials Engineering, Najafabad Branch, Islamic Azad University, Najafabad, Iran.)
Ali Saffar ⁴ (Advanced Materials Research Center, Department of Materials Engineering, Najafabad Branch, Islamic Azad University, Najafabad, Iran.)
Mahdi Rafiei ⁵ (Advanced Materials Research Center, Department of Materials Engineering, Najafabad Branch, Islamic Azad University, Najafabad, Iran.)

تاریخ دریافت : 1401/04/17 تاریخ پذیرش : 1401/06/08 تاریخ انتشار : 1401/08/10

کلید واژه: Nanomaterials, Photocatalyst, doping, Carbon nitride,

چکیده مقاله :

Bulk g-C3N4 has very poor photocatalytic activity. Many methods have been utilized to increase the photocatalytic performance of this semiconductor. Here, a simple preparation was used to create exfoliated g-C3N4 that was co-doped with sodium and tungsten. The produced Na-W co-doped exfoliated g-C3N4 was characterized using X-ray diffraction (XRD), transmission electron microscopy (TEM), UV-vis spectroscopy, and Fourier transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS). The doping samples with Na and W changed the band structure of the g-C3N4 lattice, which increased light absorption and caused a reduction in the band gap. The samples had layered morphology. After exfoliation and sodium and tungsten co-doping of the samples, the methylene blue photodegradation was greatly enhanced. The doping of the samples also had an impact on the dye adsorption capacity. The dye removal activity of the Na-W co-doped exfoliated g-C3N4 sample is higher than those of pure bulk g-C3N4 and pure exfoliated g-C3N4. The rate reaction constant (k) of the Na-W co-doped exfoliated g-C3N4 is up to 3.3 times greater than that of bulk g-C3N4. The produced photocatalyst may be utilized for the treatment of wastewater comprising methylene blue as the pollutant agent.

منابع و مأخذ:

[1] S.R. Yousefi, H.A. Alshamsi, O. Amiri, M. Salavati-Niasari, "Synthesis, characterization and application of Co/Co₃O₄ nanocomposites as an effective photocatalyst for discoloration of organic dye contaminants in wastewater and antibacterial properties ", J. Mol. Liq., Vol. 337, 2021, pp. 116405.

[2] X. Liu, R. Ma, L. Zhuang, B. Hu, J. Chen, X. Liu, X. Wang, "Recent developments of doped g-C₃N₄ photocatalysts for the degradation of organic pollutants", Crit. Rev. Environ. Sci. Technol., Vol. 51, 2021, pp. 751–790.

[3] J. Fu, J. Yu, C. Jiang, B. Cheng, "g‐C₃N₄‐Based heterostructured photocatalysts", Adv. Energy. Mater. Vol 8, 2018, pp. 1701503.

[4] J. Wen, J. Xie, X. Chen, X. Li, "A review on g-C3N4-based photocatalysts",  Appl. Surf. Sci., Vol. 391, 2017,  pp. 72–123.

[5] S.A. Hassanzadeh-Tabrizi, C.C. Nguyen, T.O. Do, "Synthesis of Fe₂O₃/Pt/Au nanocomposite immobilized on g-C3N4 for localized plasmon photocatalytic hydrogen evolution", Appl. Surf. Sci., Vol 489, 2019, pp. 741–754.

[6] Y. Sheng, Z. Wei, H. Miao, W. Yao, H. Li, Y. Zhu, "Enhanced organic pollutant photodegradation via adsorption/photocatalysis synergy using a 3D g-C₃N₄/TiO₂ free-separation photocatalyst", Chem. Eng. J., Vol. 370, 2019, pp. 287–294.

[7] S. Ghattavi, A. Nezamzadeh-Ejhieh,  "A visible light driven AgBr/g-C₃N₄ photocatalyst composite in methyl orange photodegradation: focus on photoluminescence, mole ratio, synthesis method of g-C3N4 and scavengers", Compos. Part. B. Eng., Vol. 183, 2020, pp. 107712.

[8] M. Wu, H. Lv, T. Wang, Z. Ao, H. Sun, C. Wang, T. An, S. Wang, "Ag₂MoO₄ nanoparticles encapsulated in g-C₃N₄ for sunlight photodegradation of pollutants", Catal. Today., Vol. 315, 2018, pp. 205–212.

[9] H. Méndez, G. Heimel, A. Opitz, K. Suer, P. Barkowski, M. Oehzelt, J. Soeda, T. Okamoto, J. Takeya, J.B. Arlin, J.Y. Balandier, Y. Geerts, N. Koch, I. Salzmann, "Doping of organic semiconductors: impact of dopant strength and electronic coupling", Angew. Chemie., Vol. 125, 2013, pp. 7905–7909.

[10] S. Bera, D.I. Won, S.B. Rawal, H.J. Kang, W.I. Lee, "Design of visible-light photocatalysts by coupling of inorganic semiconductors", Catal. Today., Vol. 335, 2019, pp. 3–19.

[11] A.G. Akerdi, S.H. Bahrami, "Application of heterogeneous nano-semiconductors for photocatalytic advanced oxidation of organic compounds: a review", J. Environ. Chem. Eng., Vol. 7, 2019, pp. 103283.

[12] J. Wang, G. Wang, B. Cheng, J. Yu, J. Fan, "Sulfur-doped g-C₃N₄/TiO₂ Z-scheme heterojunction photocatalyst for Congo Red photodegradation", Chinese. J. Catal., Vol. 42, 2021, pp. 56–68.

[13] G. Liu, M. Liao, Z. Zhang, H. Wang, D. Chen, Y. Feng, "Enhanced photodegradation performance of Rhodamine B with g-C₃N₄ modified by carbon nanotubes", Sep. Purif. Technol., Vol. 244, 2020, pp. 116618.

[14] M.M. Fang, J.X. Shao, X.G. Huang, J.Y. Wang, W. Chen, "Direct Z-scheme CdFe₂O₄/g-C₃N₄ hybrid photocatalysts for highly efficient ceftiofur sodium photodegradation",  J. Mater. Sci. Technol., Vol. 56, 2020, pp. 133–142.

[15] D.S. Pattanayak, D. Pal, J. Mishra, C. Thakur, K.L. Wasewar, "Doped graphitic carbon nitride (g-C₃N₄) catalysts for efficient photodegradation of tetracycline antibiotics in aquatic environments", Environ. Sci. Pollut. Res., Vol. 64, 2022, pp. 1–8.

[16] A. Allahresani, B. Taheri, M.A. Nasseri, "Fe (III)@ g-C₃N₄ nanocomposite-catalyzed green synthesis of di-indolyloxindole derivatives", Res. Chem. Intermed., Vol. 44, 2018, pp. 6741–6751.

[17] J. Ma, Q. Yang, Y. Wen, W. Liu, "Fe-g-C₃N₄/graphitized mesoporous carbon composite as an effective Fenton-like catalyst in a wide pH range", Appl. Catal. B. Environ., Vol 201, 2017, pp. 232–240.

[18] J. Tian, Q. Liu, C. Ge, Z. Xing, A.M. Asiri, A.O. Al-Youbi, X. Sun, "Ultrathin graphitic carbon nitride nanosheets: a novel peroxidase mimetic, Fe doping-mediated catalytic performance enhancement and application to rapid, highly sensitive optical detection of glucose", Nanoscale, Vol. 5, 2013, pp. 11604–11609.

[19] L. Bi, D. Xu, L. Zhang, Y. Lin, D. Wang, T. Xie,  "Metal Ni-loaded g-C₃N₄ for enhanced photocatalytic H₂ evolution activity: the change in surface band bending", Phys. Chem. Chem. Phys., Vol. 17, 2015, pp. 29899–29905.

[20] J. Zhang, S. Hu, Y. Wang,  "A convenient method to prepare a novel alkali metal sodium doped carbon nitride photocatalyst with a tunable band structure", RSC. Adv., Vol. 4, 2014, pp. 62912–62919.

[21] B. Liu, X. Nie, Y. Tang, S. Yang, L. Bian, F. Dong, H. He, Y. Zhou, K. Liu, "Objective findings on the K-doped g-C₃N₄ Photocatalysts: The presence and influence of organic byproducts on K-doped g-C₃N₄ photocatalysis", Langmuir , Vol. 37, 2021, pp. 4859–4868.

[22] J. Zhao, L. Ma, H. Wang, Y. Zhao, J. Zhang, S. Hu, "Novel band gap-tunable K–Na co-doped graphitic carbon nitride prepared by molten salt method", Appl. Surf. Sci., Vol. 332, 2015, pp. 625–630.

[23] H. Wang, W. He, H. Wang, F. Dong, "In situ FT-IR investigation on the reaction mechanism of visible light photocatalytic NO oxidation with defective g-C₃N₄", Sci. Bull., Vol. 63, 2018, pp. 117–125.

[24] H. Yan, H. Yang, "TiO₂–g-C₃N₄ composite materials for photocatalytic H₂ evolution under visible light irradiation", J. Alloys. Compd., Vol. 509, 2011,  pp. 26–29.

[25] R. Pournajaf, S.A. Hassanzadeh-Tabrizi, "Polyacrylamide synthesis of nanostructured copper aluminate for photocatalytic application", J. Adv. Mater. Process., Vol. 5, 2018, pp. 12–19.

[26] K. Wang, Q. Li, B. Liu, B. Cheng, W. Ho, J. Yu, "Sulfur-doped g-C₃N₄ with enhanced photocatalytic CO₂-reduction performance, Appl. Catal. B. Environ., Vol. 176, 2015, pp. 44–52.

[27] Z. Huang, Q. Sun, K. Lv, Z. Zhang, M. Li, B. Li, "Effect of contact interface between TiO₂ and g-C₃N₄ on the photoreactivity of g-C₃N₄/TiO₂ photocatalyst: (0 0 1) vs (1 0 1) facets of TiO₂", Appl. Catal. B. Environ., Vol. 164, 2015, pp. 420–427.

[28] S. Park, C.H. Champness, I. Shih, "Characteristics of XPS Se 3d peaks in crystalline Bridgman CuInSe_2+x with added sodium in the melt", J. Electron. Spectros. Relat. Phenomena., Vol. 205, 2015, pp. 23–28.

[29] L.L. Lai, J.M. Wu, "A facile solution approach to W, N co-doped TiO₂ nanobelt thin films with high photocatalytic activity", J. Mater. Chem. A., Vol. 3, 2015, pp. 15863–15868.

[30] Z.A. Lan, G. Zhang, X. Wang, "A facile synthesis of Br-modified g-C₃N₄ semiconductors for photoredox water splitting", Appl. Catal. B. Environ., Vol. 192, 2016, pp. 116–125.

[31] F. Guo, L. Wang, H. Sun, M. Li, W. Shi, X. Lin,  "A one-pot sealed ammonia self-etching strategy to synthesis of N-defective g-C₃N₄ for enhanced visible-light photocatalytic hydrogen", Int. J. Hydrogen. Energy., Vol. 45, 2020, pp. 30521–30532.

[32] N. Al-Zaqri, A. Muthuvel, M. Jothibas, A. Alsalme, F.A. Alharthi, V. Mohana, "Biosynthesis of zirconium oxide nanoparticles using Wrightia tinctoria leaf extract: Characterization, photocatalytic degradation and antibacterial activities", Inorg. Chem. Commun., Vol. 127, 2021, pp. 108507.

[33] H.C. Yatmaz, A. Akyol, M. Bayramoglu, "Kinetics of the photocatalytic decolorization of an azo reactive dye in aqueous ZnO suspensions", Ind. Eng. Chem. Res., Vol. 43, 2004, pp. 6035–6039.

[34] Y. Li, X. Li, J. Li, J. Yin, "Photocatalytic degradation of methyl orange by TiO₂-coated activated carbon and kinetic study", Water. Res., Vol. 40, 2006, pp. 1119–1126.