Effect of Processing Parameters on Properties of Friction Stir Welded Joints of Aluminium Alloys AA7075- T651 and AA6061-T6
محورهای موضوعی : Mechanical Engineering
H. S. Patil
1
(Mechanical Department, GIDC Degree Engineering College
Abrama, Gujarat, India)
Neelsai Sharma Kairav Patel
2
(UG Students, Mechanical Department,
GIDC Degree Engineering College, Abrama, Gujarat, India)
Abhishek Patel Viral Patel
3
(UG Students, Mechanical Department,
GIDC Degree Engineering, Abrama, Gujarat, India)
Chetan Patil
4
(Mechanical Department, PSE, Saki-Palsana, Gujarat, India)
کلید واژه: Mechanical Properties, Microstructures, AA7075 and AA6061, FSW,
چکیده مقاله :
In the present investigation the mechanical behaviour of AA7075T651 and AA6061T6 aluminium alloys plates joined by friction stir welding (FSW) were evaluated. The effects of weld process parameter like tool rotation speed 650-1000 rpm and weld speed 30-40mm/min with square trapezoidal pin profile on mechanical properties were investigated. The welded joints were tested by means of by X-ray radiography, tensile, hardness and optical microscopy testing. The radiography revealed the presence of internal in FS welds and observed that increasing transverse speed increases the occurrence of weld defects. The hardness was found to be mixed effect with respect to tool rotations and transverse speed for similar FSW joints. But in dissimilar FSW joints, hardness decreases with increasing tool speed and weld speed and it was strongly affected by precipitate distribution. Difference in grain size and distribution was observed for different ranges of rotation and weld speed.
Thomas, W.M., “Friction stir butt welding, International patent application” PCT/GB92, Patent Application GB9125978.8, 6, 1991.
[2] A. Ali, X. An, C. A. Rodopouls, M. W. Brown, P. O. “Hara, The effect of controlled shot peening on the fatigue behaviour of 2024-T3 aluminium friction stir welds”, International Journal of Fatigue 29, 2006, pp.1531-1545
[3] C. G. Rhodes, M. W. Mahoney, W. H. Bingel, R. A. Spurling and C. C. Bampton, “Effects of friction stir welding on microstructure of 7075 aluminium”, Scripta Materialia 36, 1997, pp.69–75.
[4] W. Xunhonga, W. Kuaishe, “Microstructure and properties of friction stir butt-welded AZ31 magnesium alloy”, Material Science Engineering A431, 2006, pp.114-117.
[5] H.S. Park, T. Kimura, T. Murakami, Y. Nagano, K. Nakata, M. Ushio, “Microstructures and mechanical properties of friction stir welds of 60% Cu–40% Zn copper alloy”, Materials Science Engineering A371,2004, pp.160-169.
[6] H. Fujii, L. Cui, N. Tsuji, M. Maeda, K. Nakata and K. Nogi, “Friction stir welding of carbon steels”, Materials Science Engineering, A429,2006, pp.50–57
[7] X. Cao, M. Jahazi, “Effect of welding speed on the quality of friction stir welded butt joints of a magnesium alloy”, Materials and Design 30, 2009, pp.2033–2042.
[8] H. S. Patil, S. N. Soman, “Effect of weld parameter on mechanical and metallurgical properties of dissimilar joints AA6082–AA6061 in T6 condition produced by FSW”, Frattura ed Integrità Strutturale, 24, 151-160 (2013).
[9] H. S. Patil, S. N. Soman, “Influence of weld-process parameters on the material characterization of the friction-stir-welded joints of the AA6061-T6 aluminium alloy”, MTAEC9, 47(5), 2013, pp.639.
[10] H. S. Patil1, P. D. Ahir, S. N. Soman, “Influence of process parameter on tensile properties of friction stir welded butt joints in 6082 aluminium alloy”, Elixir Mec. Eng. 30, 2011, pp.1823-1825.
[11] Caroline J., Bruno D., Anne D., Aude S., “Torque, temperature and hardening precipitation evolution in dissimilar friction stir welds between 6061-T6 and 2014-T6 aluminium alloys”, Journal of Materials Processing Tech. 213, 2013, pp.826– 837.
[12] Zhikangshen, Xinqi, Y., Zhang, Z., Cui, L., Li, T., “Microstructure and failure mechanisms of refill friction stir spot welded 7075-T6 aluminium alloy joints”, Materials and Design 44, 2013, pp.476–486.
[13] Vladvoj, M., Jorge F. P., “Microstructure and Properties of Friction Stir Welded Aluminium Alloys”, Metals, 2005, pp1-8.