In this research, BaTiO3 thick deposit has been successfully sprayed by air plasma spray. The microstructure and dielectric properties of thick films were investigated by secondary electron microscopy (SEM) and LCR meter respectively. XRD measurement was carried out on plasma sprayed BaTiO3. The results illustrate differences in the crystal structure between plasma sprayed coatings and feed stock powders. The as deposited films were mainly crystalline with small amount of an amorphous second phase. The amount of crystalline to amorphous phases was found to be critically dependent upon the degree of melting of feed stock powders. The as-deposited BaTiO3 films had maximum dielectric constant as high as 85 at room temperature. Upon annealing in air at 1050 oC, the dielectric constant increased to165. Increasing in dielectric constant was attributed to the crystallization of the amorphous phase. The dielectric constant of BaTiO3 thick films produced by plasma spray was lower than that of sintering ceramic. Reduction in dielectric properties of deposited films was related to splats interface and lamellar structure of plasma sprayed coatings. تفاصيل المقالة

چکیده در این مقاله برای سنتز نانو الیاف هسته – پوسته (اکسید قلع – اکسید روی)، از روش الکتروریسی یک مرحله ای استفاده شد. برای نیل به این هدف سوزن هم محور ساخته شده و پیش ماده های اکسیدی (کلرید قلع و استات روی) را در محلول آبی پلی وینیل الکل(PVA) حل نموده و توسط یک پمپ سرنگ دوتایی تزریق شدند. عملیات کلسینه نمودن، بر روی نانو الیاف هسته – پوسته سنتز شده صورت گرفت. مورفولوژی و ریز ساختار نانو الیاف با استفاده از میکروسکوپ الکترونی روبشی نشر میدانی (FE-SEM) ، میکروسکوپ الکترونی عبوری (TEM) و طیف سنجی انرژی اشعه ایکس(EDS) و پراش پرتو ایکس (XRD)شناسایی شدند. ساختار نهایی، شامل هسته SnO2 و پوسته ZnO میباشد. قطر هسته نانو لیف nm 45و ضخامت پوسته nm 25 می‌باشد. قطر متوسط نانو الیاف هسته – پوسته کلسینه نشده و کلسینه شده به ترتیب 175و nm79 می‌باشد. تفاصيل المقالة