Investigation of Microstructure and Mechanical Properties of Ni-Cu-P Coatings Deposited by the Electroless Method
الموضوعات :Danial Davoodi 1 , Amir Hossein Emami 2 , Sayed Mahmoud Monir Vaghefi 3 , Mahdi Omidi 4 , Hamid Reza Bakhsheshi-Rad 5
1 - Advanced Materials Research Center, Department of Materials Engineering, Najafabad Branch, Islamic Azad University, Najafabad, Iran
2 - Advanced Materials Research Center, Department of Materials Engineering, Najafabad Branch, Islamic Azad University, Najafabad, Iran
3 - Department of Materials Engineering, Isfahan University of Technology, Isfahan 84156-83111, Iran.
4 - Advanced Materials Research Center, Department of Materials Engineering, Najafabad Branch, Islamic Azad University, Najafabad, Iran.
5 - Advanced Materials Research Center, Department of Materials Engineering, Najafabad Branch, Islamic Azad University, Najafabad, Iran.
الکلمات المفتاحية: TEM, Heat treatment, Microhardness, Electroless Ni-Cu-P, L80 steel,
ملخص المقالة :
In the current study, the effect of colloidal copper nanoparticles on the deposition rate and hardness of Ni-Cu-P coating deposited by electroless method on L80 steel substrate was investigated. Copper particle size, microstructure, chemical composition, and hardness of the coating before and after heat treatment at different temperatures were examined by transmission electron microscopy (TEM), X-ray diffraction (XRD), scanning electron microscopy (SEM) equipped with energy dispersive X-ray (EDS) analysis, and microhardness. The microstructure study by XRD showed that the Ni-Cu-P coating has an amorphous structure. The heat treatment at 400 °C transformed the structure from amorphous to crystalline and formed Niα, Ni3P, and Ni3.8Cu phases. The amount of copper nanoparticles in the coating 4.58 wt% was measured. The deposition rate of the Ni-Cu-P coating was 11 µm/h. Furthermore, the hardness of the coating increased from 738HV to 1300HV by performing heat treatment.
[1] Petroleum and natural gas industries—Steel pipes for use as casing or tubing for wells, Specification for Casing and Tubing API Specification 5CT Eighth Edition, ISO 11960. (2005).
[2] Robert Heidersbach, Metallurgy and Corrosion Control in Oil and Gas Production, John Wiley Sons, Inc. (n.d.), 2018.
[3] F. Bigdeli, M. Javidi, M. Pakshir, A. Khezrloo, M. Tayebi, Risk assessment of the corrosion resistance performances for epoxy coatings under drilling environments using AHP method, Int. J. Press. Vessel. Pip. 193 (2021) 104470.
[4] C. Sun, J. Li, S. Shuang, H. Zeng, J.-L. Luo, Effect of defect on corrosion behavior of electroless Ni-P coating in CO2-saturated NaCl solution, Corros. Sci. 134 (2018) 23–37.
[5] masoud soltani, A. Shafyei, K. Zarrin naghsh, R. Aliramezani, Effect of Ni-P electroless coating and heat treatment on tribological and corrosion properties of copper substrate, J. Adv. Mater. Process. 6 (2018) 3–13.
[6] D. Davoodi, R. Miri, A.H. Emami, M. Tayebi, S. Salahshour, The effect of NiO catalyst on reduction, synthesis and binder content of TiC-Ni nanocomposite, Int. J. Refract. Met. Hard Mater. 88 (2020) 105175.
[7] J. Sudagar, J. Lian, W. Sha, Electroless nickel, alloy, composite and nano coatings – A critical review, J. Alloys Compd. 571 (2013) 183–204.
[8] A. Chami, B. Nasiri Tabrizi, Effect of heating rate on morphological features of oxidized electroless nickel–boron coatings, J. Adv. Mater. Process. 3 (2015) 61–70.
[9] S.R. Anvari, S.M. Monirvaghefi, M.H. Enayati, Fabrication and characterization of nanostructured functionally graded Ni-P electroless coating, J. Adv. Mater. Process. 4 (2016) 19–29.
[10] I.R. Mafi, C. Dehghanian, Comparison of the coating properties and corrosion rates in electroless Ni–P/PTFE composites prepared by different types of surfactants, Appl. Surf. Sci. 257 (2011) 8653–8658.
[11] A. Arumugam, P. Lakshmanan, S. Palani, K. Parthiban, Wear behavior of Ni-P and Al2O3 electroless nano coating on aluminium alloy, Mater. Today Proc. 46 (2021) 1066–1070.
[12] M. Khodaei, A.M. Gholizadeh, SiC nanoparticles incorporation in electroless NiP-Graphene oxide nanocomposite coatings, Ceram. Int. 47 (2021) 25287–25295.
[13] C. Wang, Z. Farhat, G. Jarjoura, M.K. Hassan, A.M. Abdullah, Indentation and bending behavior of electroless Ni-P-Ti composite coatings on pipeline steel, Surf. Coatings Technol. 334 (2018) 243–252.
[14] J. Li, C. Sun, M. Roostaei, M. Mahmoudi, V. Fattahpour, H. Zeng, J.-L. Luo, Characterization and corrosion behavior of electroless Ni-Mo-P/Ni-P composite coating in CO2/H2S/Cl− brine: Effects of Mo addition and heat treatment, Surf. Coatings Technol. 403 (2020) 126416.
[15] S. Du, Z. Li, Z. He, H. Ding, X. Wang, Y. Zhang, Effect of temperature on the friction and wear behavior of electroless Ni–P–MoS2–CaF2 self-lubricating composite coatings, Tribol. Int. 128 (2018) 197–203.
[16] I. Rose, C. Whittington, Nickel Plating Handbook, Belgium, 2014.
[17] M. Czagany, P. Baumli, Effect of pH on the characteristics of electroless Ni-P coatings, J. Min. Metall. Sect. B Metall. 53 (2017) 20.
[18] F. Tabatabaei, K. Raeissi, A. Saatchi, M. Ürgen, Effect of sodium sulfate on the characteristics and corrosion behavior of high phosphorus Ni–P electroless coatings, Mater. Corros. 65 (2014) 926–930.
[19] S. Kundu, S.K. Das, P. Sahoo, Friction and wear behavior of electroless Ni-P-W coating exposed to elevated temperature, Surfaces and Interfaces. 14 (2019) 192–207.
[20] S. Elahinejad, H. Sharifi, M. Tayebi, A. Rajaee, The influence of nickel coating on the interface of pressureless infiltrated with vibration Al-SiC composites, Mater. Res. Express. 4 (2017) 116506.