Investigating the Reason for Compressor Gearbox Gear Failure in Arfa Iron and Steel Company using Analytical and Fracture Studies
الموضوعات :Mahdi Ebrahimzadeh 1 , Ali Galehdari 2
1 - Modern Manufacturing Technologies Research Center, Najafabad Branch, Islamic Azad University, Najafabad, Iran
2 - Modern Manufacturing Technologies Research Center, Najafabad Branch, Islamic Azad University, Najafabad, Iran
الکلمات المفتاحية: Fracture studies, Design analysis, Gear failure, Gearbox,
ملخص المقالة :
Given the application of gears in various industries including steel industries, studying the reasons for facture in gears before reaching the end of their lifetime is of great importance. In this study, a gearbox was investigated which included a gear and a pinion. After four years of use, the teeth of gear and pinion along with the shaft attached to the gear were fractured. The fracture had occurred suddenly and with a lot of noise. The fracture in gear and pinion were in the teeth while the fracture in shaft occurred in the keyway. At the beginning of the study, shaft and gear design equations were used to evaluate the suitability of each of the parts in the system using theoretical equations and then fracture type was determined using fracture studies and the accuracy of analytical results were determined. In the analytical study, the results showed that the fracture is due to improper design for the gear shaft leading to more than one million unites of load on the shaft leading to cracks in the keyway and misalignment between gears causing fracture. In the fracture studies, the fracture type (ductile and brittle) was determined and the accuracy of analytical results was confirmed. In the numerical results, the distribution of static strain in the fractured shaft and a redesigned shaft are investigated.
[1] Panwar, V., Mogal, S., A Case Study on Various Defects Found in a Gear System, International Research Journal of Engineering and Technology, Vol. 3, No. 3, 2015, pp. 425- 429.
[2] patel, J., Sahu, G., Sen, P., A Study on Common Failures of Gears, International Research Journal of Engineering and Technology, Vol. 2, No. 6, 2015, pp. 301- 307.
[3] Pandhal, D. K., Meshram, D. B., Analysis and Failure Improvement of Shaft of Gear Motor in CRM Shop, International Journal of Engineering and Science, Vol. 3, No. 4, 2013, pp. 17- 24.
[4] Lanzutti, A., Gagliardi, A., Raffaelli, A., Simonato, M., Furlanetto, R., Magnan, M., Andreatta, F., and Fedrizzi, L., Failure Analysis of Gears, Shafts and Keys of Centrifugal Washers Failed During Life Test, Engineering Failure Analysis, Vol. 79, No. 3, 2017, pp. 634-641.
[5] Yucel, S., Ozenli, L., Gencol, T., and Alanyalı, E., Flywheel Starter Ring Gear Failures and Hardness Variation Reduction in Surface Hardening Process, Engineering Failure Analysis, Vol. 4, 2015, pp. 8-19.
[6] Rossino, L., Castro, D., Moreto, J., Ruchert, C., pinelli, S., and Trapani, J., Surface Contact Fatigue of a Case-Hardened Pinion Shaft,Material Research, Vol. 3, No. 17, 2014, pp. 535- 541.
[7] Milutinovic, M., Trifkovic, S., Duric, A., and Vucetic, N., Gear Failures Embedded in Manual Gearboxes, Bulletin of Engineering, Vol. 1, No. 1, 2016, pp. 83- 84.
[8] Parey, A., Jain, N. K., Gencol, T., and Koria, S. C, Failure Analysis of Air Cooled Condenser Gearbox, Engineering Failure Analysis, Vol. 2, 2014, pp. 150-156.
[9] Shadravan, E., Mechanical Engineering Design, 9rd ed., Nopardazan, IRAN, 2011, pp. 780.
[10] Shadravan, E., Mechanical Engineering Design, 9nd ed., Nopardazan, IRAN, 2011, pp. 779.
[11] Peterson, R., Pilkey, W., and Pilkey, D., Stress Concentration Factors, 3rd ed., Wiley, New York, 2008, pp. 165-167.
[12] Shadravan, E., Mechanical Engineering Design, 9rd ed., Nopardazan, IRAN, 2011, pp. 309.
[13] Shadravan, E., Mechanical Engineering Design, 9rd ed., Nopardazan, IRAN, 2011, pp. 388.
[14] Valenejad, A., Tables and Standards in Design and Machine, 1nd ed., Tarrah, IRAN, 2009, pp. 241.