Process Optimization and Kinetic study of Wet Peroxide Oxidation of Phenol in Wastewater over Mg-Al Nano Mixed Oxide

الموضوعات : Iranian Journal of Catalysis

Masoud Samandari ¹ (Department of Chemistry, Central Tehran Branch, Islamic Azad University, Tehran, Iran)
Afshin Taghva Manesh ² (Department of Chemistry, Central Tehran Branch, Islamic Azad University, Tehran, Iran)
Seyed Ali Hosseini ³ (Department of Applied Chemistry, Urmia University, Urmia, Iran)
Sakineh Mansouri ⁴ (Department of Chemistry, Central Tehran Branch, Islamic Azad University, Tehran, Iran)

تاريخ الإرسال : 28 الثلاثاء , جمادى الأولى, 1442 تاريخ التأكيد : 04 الأحد , شوال, 1442 تاريخ الإصدار : 20 الثلاثاء , شوال, 1442

الکلمات المفتاحية: phenol, activation energy, Kinetic studies, Wet peroxide oxidation, Mg-Al mixed nanooxide,

ملخص المقالة :

The wet peroxide oxidation (CWPO) of phenol in the polluted water on Mg-Al nano mixed oxide was investigated and the optimization and kinetic of the process were studied. The nanocatalyst was characterized by XRD, FESEM, EDS and BET. The average crystallite size of 25 nm was estimated using Scherrer formula.FESEM images approved the catalyst comprised of spherical nanoparticles in the range of 94-130 nm. BET results indicated the mesoporous nanocatalyst (dpore=21 nm) has a specific surface area of 86.3 m2.g-1. The optimized conditions of the process resulted at initial concentration of phenol, reaction temperature, reaction time and hydrogen peroxide volume of 100 ppm, 60ºC, 55 min and 3 mL, respectively. The phenol degradation under the optimal conditions reached 85%. The result of the kinetic study indicated that the oxidation of phenol over Mg-Al nano mixed oxide follows the pseudo-first-order kinetics with a correlation factor of 0.94. The activation energy of phenol oxidation over the catalyst was determined to be 19.07 kJ.mol-1. The Mg-Al mixed oxide is a cheap and green catalyst and could be prove to promising for the CWPO process.

المصادر:

[1] B. Bagheri, S.A. Hosseini, H. Mehrizadeh.  J. Water Environ. Nanotechnol., 5 (2020) 139-146.

[2] S. A. Hosseini, M. Davodian, A. R. Abbasian, J. Taiwan Inst. Chem. Eng, 75 (2017) 97-104.

[3] A. Nezamzadeh-Ejhieh, M. Bahrami, Desal. Water Treat. 55 (2015) 1096–1104.

[4] Zarifeh-Alsadat Mirian, Alireza Nezamzadeh-Ejhieh, Desal. Water Treat. 57 (2016) 16483–16494.

[5] N. Pourshirband, A. Nezamzadeh-Ejhieh, S. N. Mirsattari, Chem. Phys. Lett. 761 (2020) 138090-138099.

[6] B. Divband; A. Jodaei; M. Khatamian, Iran. J. Catal. 9 (2019) 63-70.

[7] S. Esplugas, J. Gimenez, S. Contreras, E. Pascual, M. Rodrı´guez, Water Res. 36 (2002) 1034–1042

[8] R. Surkatti, M. H. El-Naas, M. C. M. Van Loosdrecht, A. Benamor, F. Al-Naemi, U. Onwusogh, Biotechnology for Gas-to-Liquid (GTL) Wastewater Treatment: A Review, Water  12(8) (2020) 2126-2152

[9] S Mohammadi, A Kargari, H Sanaeepur, K Abbassian, A Najafi, E. Mofarrah, Desalin Water Treat. 53 (2015) 2215–34.

[10] F. Soori, A. Nezamzadeh-Ejhieh, J. Molecul. Liq. 255 (2018) 250–256.

[11] I. Nowak, I. Rykowska, J. Ziemblińska-Bernart, J. Iranian Chem Soc., 17, (2020) 825–838.

[12] C.E. Bekkali , H. Bouyarmane , S. Laasri, A. Laghzizil, A. Iran J. Catal. 8 (2018) 241-247.

[13] M. Giahi; A. Hoseinpour Dargahi, Iran J. Catal, 6 ( 2016) 381-387.

[14] A. Nezamzadeh Ejhieh, M. Khorsandi, J. Hazard. Mater. 176 (2010) 629–637

[15] H. Derikvandi, A. Nezamzadeh-Ejhieh, J. Colloid Interf. Sci. 490 (2017) 314–327.

[16]    O. Gholipoor, S. A. Hosseini,  New J. Chem.,  45 (2020)   2536-2549.

[17] K. Maduna, N. Kumar, A. Aho, J. Wärnå, S. Zrnčević, D. Yu. Murzin, ACS Omega  3, 7 (2018) 7247–7260

[18] A. Santos, P. Yustos, B. Durban, F. Garcia-Ochoa, Ind. Eng. Chem. Res.  40, 13 (2001) 2773–2781

[19] J.G Li, T. Ikegami, J.H. Lee, T. Mori, Y. Yajima,  J. Europe Ceram. Soc. 21 (2001) 139-148

[20 ] M. Balakrishnan, R. John, Iran. J. Catal. 10(1) (2020) 1-16.

[21] P. Massa, F. Ivorra, P. Haure, R. Fenoglio, J Hazard Mater 190 (2011) 1068–1073. 

[22] J.A. Zazo, J.A. Casas, A.F. Mohedano, J.J. Rodrı´guez, Appl Catal B, 65 (2006) 261–268.

[23] H.  Li, X. Yu, H. Zheng, Y.  Li, X.  Wang, M. Huo, RSC Adv. 4 (2014) 7266-7274.

[24]   T. Kumar, R. Mohsin, Z.A. Majid, M.F.A. Ghafir, A.M. Wash,  Appl Energy, 259 (2019) 114150-114172. 

[25] E. V. Rokhina, E. Repo, J. Virkutyte, Ultrasonic Sonochem 17 (2010) 541–546.

[26] A.Pintar, J.Levec, J. Catal.,  135(2) (1992) 345-357