  1 - Investigation of Microstructure weld zone of Hastelloy X Pulsed Nd-YAG laser welds
  Farrokh Najafzadegan Hojatallah Mansori Morteza shamanian
  In the present study, the microstructure of welded zone of Hastelloy X sheets with thickness of 1 mm via pulsed Nd-YAG laser welding were studied. This welding process was done by autogenus and conductive method. Microstructure were observed by metallurgical OM and SEM. چکیده کامل

  In the present study, the microstructure of welded zone of Hastelloy X sheets with thickness of 1 mm via pulsed Nd-YAG laser welding were studied. This welding process was done by autogenus and conductive method. Microstructure were observed by metallurgical OM and SEM. Results shown Solidification of the weld metal is dendritic. The dendrites in the central zone of the welding are fine and equiaxed while they are larger and columnar in the fusion boundary. Epitaxial growth was observed in the interface of base metal and weld metal. Alloy elements Segregation did not occur during the solidification process and the fine cracks were not observed in the welding zone of the alloy. Micro hardness results indicated that the hardness of welded metal were more than base metal and cause to decrease grain size at welded metal more than base metal. This phenomenon was occurred due to more differences between heating and cooling rate in this welding process. پرونده مقاله
• دسترسی آزاد مقاله
  • صفحه چکیده
  • متن کامل
  
  2 - The Effect of Magnesium on the Microstructure and Stress Rupture Properties of Hastelloy X Supealloy
  Masumeh seifollahi Afagh panahi moghaddam seysd Mahdi Abbasi seyed Mahdi ghazi mir saeed
  In the present study, the effects of magnesium on the microstructural characteristics and stress-rupture properties of the Hastelloy X superalloy were investigated. In this regard, four alloys with different amounts of magnesium (0, 17, 33, 47 ppm) were cast via the vac چکیده کامل

  In the present study, the effects of magnesium on the microstructural characteristics and stress-rupture properties of the Hastelloy X superalloy were investigated. In this regard, four alloys with different amounts of magnesium (0, 17, 33, 47 ppm) were cast via the vacuum induction melting and then purified via the electro slag remelting. Microstructural observations were carried out through optical and scanning electron microscopes, and phase analysis was performed by X-ray diffraction. The stress rupture test was carried out at 815 °C/130 MPa. The results showed an almost significant effect of magnesium on decreasing grain size and sulfur content and increasing M6C carbides volume fraction. Magnesium changed the morphology of carbides from the course and continue to finely divide one. Mg segregated at the grain and carbide boundary decreases the lattice parameters of the matrix and changes the composition of M6C. Magnesium increased the rupture life by 46%. The most important causes for improving the rupture life of the Hastelloy X in the presence of magnesium are the increasing carbides volume fraction, improving its morphology, and decreasing sulfur content. پرونده مقاله
• دسترسی آزاد مقاله
  • صفحه چکیده
  • متن کامل
  
  3 - تأثیر نورد سرد و آنیل بر ریزساختار و خواص کششی سوپرآلیاژ Hastelloy X
  حمید فیض آبادی سید مهدی عباسی مریم مرکباتی رشید مهدوی محمدرضا توکلی
  هدف از پژوهش حاضر، بررسی اثر میزان نورد سرد به همراه آنیل میانی و آنیل نهایی بر ریزساختار و خواص کششی سوپرآلیاژ Hastelloy X است. بدین منظور تسمه نورد گرم و آنیل انحلالی شده این آلیاژ به ضخامت 10 میلی‌متر تحت سه مرحله نورد سرد (در هر مرحله 50 درصد) همراه با آنیل میانی در چکیده کامل

  هدف از پژوهش حاضر، بررسی اثر میزان نورد سرد به همراه آنیل میانی و آنیل نهایی بر ریزساختار و خواص کششی سوپرآلیاژ Hastelloy X است. بدین منظور تسمه نورد گرم و آنیل انحلالی شده این آلیاژ به ضخامت 10 میلی‌متر تحت سه مرحله نورد سرد (در هر مرحله 50 درصد) همراه با آنیل میانی در دمای C°1175 به مدت نیم ساعت قرار گرفت تا این‌که ضخامت آن به 25/1 میلی‌متر رسید. سپس نمونه‌های آماده شده جهت آزمون کشش در محدوده‌ی دمایی C° 860-660، تحت عملیات آنیل در محدوده دمایی C°1200-1100 به مدت یک ساعت قرار گرفتند. خواص کششی دمای محیط و دمای بالا همراه با ریزساختار تسمه‌‌ها مورد بررسی قرار گرفت. نتایج بررسی ریزساختار نمونه آنیل انحلالی شده در دمای C°1175 به مدت یک ساعت نشان داد که فاز زمینه آستنیت و ذرات موجود کاربیدM6C غنی از مولیبدن می‌باشند. نتایج آزمون کشش گرم نمونه‌های آنیل شده در دماهای 1100، 1150 و C°1200 نشان داد که حداقل داکتیلیته به ترتیب در دماهای 760، 760 و C°860 به دست آمد. همچنین مشخص شد که استحکام تسلیم در سوپرآلیاژ Hastelloy X برای محدوده‌ی دمایی C°660 تا C°860 مستقل از دما است که دلیل آن می‌تواند رسوب کاربیدهای M6C غنی از مولیبدن باشد. پرونده مقاله