The Effect of Power, Maximum Cutting Speed and Specific Point Energy on the Material Removal Rate and Cutting Volume Efficiency in CO2 Laser Cutting of Polyamide Sheets
محورهای موضوعی : Laser based manufacturing systemsMajid Hashemzadeh 1 , Reza Poorshaban 2
1 - Department of Mechanical Engineering, Najafabad Branch, Islamic Azad University, Najafabad, Iran
2 - Department of Mechanical Engineering, Najafabad Branch, Islamic Azad University, Najafabad, Iran
کلید واژه: CO2 Laser Cutting, material removal rate, Polyamide (PA), kerf width,
چکیده مقاله :
Material removal rate (MRR) and cutting volume efficiency (αVol) in laser cutting of commercial polyamide (Nylon) sheets have been studied in this research. A CO2 laser cutting machine with the power of 100 W was used to cut polyamide (PA) sheets with thicknesses of 2 to 8 mm. The beam spot size on the upper surface of the sheet was 0.1 mm. The maximum cutting speeds for a variety of powers and thicknesses were specified under the same other laser cutting parameters. The specific point energy (Esp) was calculated for every combination of maximum cutting speed and power. Results show that for a given power, the maximum cutting speed exponentially decreases with increasing sheet thickness. The MRR increases logarithmically with power and for a given power, it rises as the sheet thickness decreases. The αVol increases with power until it reaches the apex of efficiency, then it slightly reduces with increasing power. Overall, the αVol decreases with increasing sheet thickness and Esp.
[1] Petring, D., Schneider, F., Wolf, N. and Nazery, N. 2008. The relevance of brightness for high power laser cutting and welding. 27th International Congress on Applications of Lasers & Electro Optics (ICALEO): 95-103.
[2] Mahrle, A., Lutke, M. and Beyer, E. 2010. Fibre laser cutting: beam absorption characteristics and gas-free remote cutting. Proceedings of the Institution of Mechanical Engineers. Part C-Journal of Mechanical Engineering Science. 224 (C5): 1007-1018.
[3] Hashemzadeh, M., 2014. Investigation into fibre laser cutting. The University of Nottingham. PhD thesis.
[4] Riveiro, A., Quintero, F., Lusquiños, F., del Val, J., Comesaña, R., Boutinguiza, M. and Pou, J. 2012. Experimental study on the CO2 laser cutting of carbon fiber reinforced plastic composite. Composites Part A: Applied Science and Manufacturing. 43(8): 1400-1409.
[5] Caiazzo, F., Curcio, F., Daurelio, G. and Minutolo, F. M. C. 2005. Laser cutting of different polymeric plastics (PE, PP and PC) by a CO2 laser beam, J. Mater. Process. Technol. 159(3): 279-285.
[6] Powell, J., Al-Mashikhi, S.O., Kaplan, A.F.H. and Voisey, K.T. 2011. Fibre laser cutting of thin section mild steel: An explanation of the striation free effect. Optics and Lasers in Engineering. 49:1069-75.
[7] Hirano, K. and Fabbro, R. 2011. Experimental observation of hydrodynamics of melt layer and striation generation during laser cutting of steel. Physics Procedia. 12(Part A):555-64.
[8] Steen, W.M. 2005. Laser Material Processing, third edition: Springer.
[9] Hashemzadeh, M., Suder, W., Williams, S., Powell, J., Kaplan, A.F.H. and Voisey, K.T. 2014. The Application of Specific Point Energy Analysis to Laser Cutting with 1μm Laser Radiation. Physics Procedia. 56: 909-918
[10] Powell J. 1998. CO2 laser cutting, Second edition, Springer, London.
[11] Haddadi, E., Moradi, M., Karimzad Ghavidel, A., Karimzad Ghavidel, A. and Meiabadi, S. 2019. Experimental and Parametric Evaluation of Cut Quality Characteristics in CO2 Laser Cutting of Polystyrene. Optik. 184:103-114.
[12] Zhaia, Zh.,Wang, F. and Duan, H. 2019. Experimental study on 800 nm femtosecond laser cutting of polyamide in air. 194:163080.
[13] Riveiro, A., Quintero, F., Lusquiños, F., del Val, J., Comesaña, R., Boutinguiza, M. and Pou, J. 2012. Experimental study on the CO2 laser cutting of carbon fiber reinforced plastic composite. Composites Part A: Applied Science and Manufacturing. 43(8), 1400–1409.
[14] Davari, M. and Hashemzadeh, M. 2018. The effect of bronze particles on CO2 laser cutting of reinforced polytetrafluoroethylene. Int J Adv Manuf Technol. 96:4029–4039.
[15] Moradi, M., Mehrabi, O., Azdast, T. and Benyounis, K.Y. 2017. Enhancement of low power CO2 laser cutting process for injection molded polycarbonate. Optics & Laser Technology. 96:208–218.
[16] Moradi, M., Mehrabi, O., Azdast, T. and Benyounis, K.Y. 2017. The effect of low power CO2 laser cutting process parameters on polycarbonate cut quality produced by injection molding. Modares Mechanical Engineering. 17(2):93-100.
[17] Banerjee, S. S. and Bhowmick, A. K. 2015. Experimental study on the CO2 laser cutting of novel polyamide 6/fluoroelastomer thermoplastic elastomeric blends. Rubber Chemistry and Technology. 88(1):125-137.
[18] DeIorio, I., DiIlio, A. and Tagliaferri, V. 1987. Cut edge quality of GFRP by pulsed lasermaterial interaction analysis. Proceedings of LAMP, high Temperature Society of Japan. 279-284.
[19] Brydson, J. A. 1989. Plastic Materials, Fifth edition. Butterworth.
[20] Campo, E. A. 2006. The Complete Part Design Handbook for Injection Molding of Thermoplastics, Hanser.
[21] Schwartz, S. S. and Goodman, S. H. 1982. Plastic Materials and Processes, Van Norstrand Retnhold.
[22] Beyler, C.L. and Hirschler, M.M. 2002 Thermal Decomposition of Polymers. SFPE Handbook of Fire Protection Engineering, Chapter 7: 111-131.
[23] Hashemzadeh, M. and Mohammadi, M. 2020. The Effect of Power and Maximum Cutting Speed on the Material Removal Rate and Cutting Volume Efficiency in CO2 Laser Cutting of Polycarbonate Sheets. Journal of Modern Processes in Manufacturing and Production. 9(1):5-23.