The effect of different pHs, Surfactants and dialyses times on preparation of nano Rod Hydroxyapatite
محورهای موضوعی : Journal of Nanoanalysis
Fateme Mirjalili
1
(Department of Material Engineering, Maybod Branch, Islamic Azad University, Maybod, Iran)
کلید واژه: Nano HA rod, precipitation method, XRD analysis,
چکیده مقاله :
Nano HA rod was synthesized by precipitation method using Ca(NO3)24H2O and (NH4)2HPO4 as starting materials and ammonia solution as an agent for pH adjustment. The Ca/P molar ratio was maintained at 1.67. Then, the effect of different pH (4, 6, 8, 10, 11), different surfactants and different times for dialyses on nano HA rod were studied in this study. The samples were characterized by different techniques such as, X-ray diffraction, Fourier transform infrared spectra, and Transmission electron microscopies. The XRD analysis showed that the prepared HA nano rod is fully crystalline. The results showed that the best pH for nano HA rod was 11 and Span 20 as the surfactant had the better effect on dispersion and shape of nano rod. The HA nano-rods had an average diameter of 10 nm and length of 70-80 nm after 12 h of dialyses time.
1. A.I .Misions, T.C.Vaimakis, C.C. Trapalis, Ceram.Inter., 36, 623(2010).
2. C.Ergun, Z. Evis, T.J.Webster, F.C.Sahin , Ceram.Inter., 37, 971(2011).
3. F.N.Okatar, Matter. Let., 60, 2207 (2006).
4.F. Deravi , R. Sinatra, O.Christophe, P. Nesmith, H. Yuan, K. Deravi, A. Goss, A. MacQueen, R. Badrossamy, M. Gonzalez, D. Phillips, K. Parker, Mac. Mats. Eng.,1(2017).
5. H.Ji, P. M. Marquis, Bon.Min. Res.,13,744(1992).
6. A.Haider, S. Haider, S.Han ,I.Kang, R. Soc. Chem.,7,7442 (2017).
7. Z.E.Erkmen, Y. Gens , F.N.Oktar, J.A. Ceram. Soc., 90, 2885 (2007).
8.T.Stephanie ,C. Tang, A. Kennedy, S. Talwar,S. A. Khan, J.F.Hydo.,35,36(2014).
9. N.Bahlawane, T.Watanabe, J.A. Ceram. Soc., 9, 2324(2000).
10.Y.Zhao, Y.Qiu, H. Wang, Y.Chen, S. Jin, S. Chen, Inter.J. Poly. Sci.,2016,1(2016).
11. R.T.Franceschi ,B.S. Lyer , Bon. Min. Res.,7, 235(1992).
12. S.Assafi, N.Bruijn, M. Jumaily, W. J. N. Sci. Eng., 6, 58(2016).
13. R.Vaben , D. Stover , J.Mat. Pro. Tech.,92, 84(1999).
14.Y. Lee,S. Fu,C. Lin, 1st Global Conference on Biomedical Engineering & 9th Asian-Pacific Conference on Medical and Biological Engineering, Thailand , pp.9-12(2014).
15.S. Kunjalukkal Padmanabhan , A.Balakrishnan, J.Particulogy,7,466(2009).
16. S. Gao ,K. Sun , A.Li , H.Wang , Maters. Res. Bul, 48, 1003 (2013).
17.S.Tayyebi,F.Mirjalili,H.Samadi,J.Ceram.Pross.17,1034(2016).
18. S. Jadalannagari , S.More, M. Kowshik , S.Ramanan ,Maters .Sci. Eng., 31, 1534 (2011).
19. F. Mirjalili, M. Hasmaliza ,L. Chuah Abdullah, Ceram. Inter. , 36 ,1253(2010).
20. Z. Evis and R. Doremus , Maters. Res. Bul., 43, 2643 (2008).
21. P.Q. Franco, C.F.C. João, B.J.C.Silva , J.P.Borges , Maters.Let., 67, 233(2012).
22. A.Z.Zinchenko , R.H. Davis ,J.Phys. Fluids., 7, 2310(1995).
23. M. Mirjalili,S. Zohoori, J.Nanostruct.Chemis.,6,207(2016).
24. S. Ifuku H. Maeta , H. Izawa, M. Morimoto, H. Saimoto, RSC. Adv. ,44, 267(2015).
25. M. Maas, P. Guo, M. Keeney, F. Yang, T. M. Hsu, G. Fuller, R. Martin, R. N. Zare, Nano. Lett., 11, 1383(2011).
26. Y. Zhao, Y.Qiu, H.Wang, Y.Chen, S.Jin, S.Chen, Inter. J.Pol.Sci., 2016,17(2016).
27. J. Li, A.He, C. Han, D.Fang, S. Hsiao,B. Chu ,Macro. Molecul. Rap.Com., 27, 114(2006).
28. R.Anamarija, App.Sur. Sci., 296 , 221(2014).
29. W.Cui, Y.Zhou, J Chang, Sci. Technol. Adv. Mater.,11,1(2010).
30. J. Venugopal,S. Low, A.Choon, A. Bharath Kumar, S.Ramakrishna, Art.Org.,32,388(2008).
31. F. Ejaz Ahmed, B. Lalia, R.Hashaikeh, J.Desal., 356 ,15(2015).
32.H.Won,H.Lee,J.Knowless, Bio.M. Res.,79,643(2006).
33.N.Nega,T.Hoai,P.viet, Colls. Sur. B: Bio.Inter.,128,506(2015).