Investigation of enamel surface hardness using remineralization of white spot lesions with CPP-ACP, fluoride, and CPP-ACPF
محورهای موضوعی : Journal of NanoanalysisFarzaneh Shirani 1 , Shirin Rostami 2 , Parastoo Afghari 3
1 - Dental Materials Research Center, Dental Research Institute, Department of operative Dentistry, School of Dentistry, Isfahan University of Medical Sciences, Isfahan, Iran
2 - Department of Periodontics, School of Dentistry, Isfahan University of Medical Sciences, Isfahan, Iran
3 - Oral and Maxillofacial Radiologist, Self-employed Researcher, Toronto, Canada
کلید واژه: Hardness, fluoride, Casein phosphopeptide-amorphous calcium phosphate nanocomplex, Dental enamel, Tooth remineralization,
چکیده مقاله :
Abstract: The enamel surface hardness determination plays a key role in surface abrasion a resin composite bond strength. The aim of this study was to investigate the enamel surface hardness after remineralization of white spot lesions using casein phosphopeptide amorphous calcium phosphate (CPP-ACP), fluoride and casein phosphopeptide amorphous calcium phosphate fluoride (CPP-ACPF). Materials and Methods: A 36 bovine anterior teeth were chosen and after decoronization, the teeth were mounted in acrylic resin and their baseline surface hardness was measured. Samples were then demineralized and their surface hardness was measured. The teeth were then divided into three groups and subjected to surface treatment with CPP-ACP, CPP-ACPF and fluoride mouthwash. The surface hardness was measured and the data were analyzed using SPSS software. Results: Paired t-test showed that surface hardness significantly changed after demineralization (P<0.001) and after treatment with CPP-ACPF (P<0.001) and fluoride (P=0.005), however: the change was not significant after treatment with CPP-ACP (P=0.155). Conclusions: The obtained results indicated that treatment with fluoride and CPP-ACPF may increase the surface hardness of demineralized enamel.
Abstract: The enamel surface hardness determination plays a key role in surface abrasion a resin composite bond strength. The aim of this study was to investigate the enamel surface hardness after remineralization of white spot lesions using casein phosphopeptide amorphous calcium phosphate (CPP-ACP), fluoride and casein phosphopeptide amorphous calcium phosphate fluoride (CPP-ACPF). Materials and Methods: A 36 bovine anterior teeth were chosen and after decoronization, the teeth were mounted in acrylic resin and their baseline surface hardness was measured. Samples were then demineralized and their surface hardness was measured. The teeth were then divided into three groups and subjected to surface treatment with CPP-ACP, CPP-ACPF and fluoride mouthwash. The surface hardness was measured and the data were analyzed using SPSS software. Results: Paired t-test showed that surface hardness significantly changed after demineralization (P<0.001) and after treatment with CPP-ACPF (P<0.001) and fluoride (P=0.005), however: the change was not significant after treatment with CPP-ACP (P=0.155). Conclusions: The obtained results indicated that treatment with fluoride and CPP-ACPF may increase the surface hardness of demineralized enamel.
1) Perdigão J. Resin infiltration of enamel white spot lesions: An ultramorphological analysis. J Esthet Restor Dent. 2020 Apr;32(3):317-324.
2) Chambers C, Stewart S, Su B, Sandy J, Ireland A. Prevention and treatment of demineralisation during fixed appliance therapy: a review of current methods and future applications. Br Dent J. 2013 Nov;215(10):505-11.
3) Ghadirinejad, N., Nejad, M. G., & Alsaadi, N. (2021). A fuzzy logic model and a neuro-fuzzy system development on supercritical CO2 regeneration of Ni/Al2O3 catalysts. Journal of CO2 Utilization, 54, 101706.
4) Nejad, M. G., & Kashan, A. H. (2019). An effective grouping evolution strategy algorithm enhanced with heuristic methods for assembly line balancing problem. Journal of Advanced Manufacturing Systems, 18(03), 487-509.
5) Ghasemi, M., Nejad, M. G., & Aghaei, I. (2021). Knowledge management orientation and operational performance relationship in medical tourism (overview of the model performance in the COVID-19 pandemic and post-pandemic era). Health Services Management Research, 34(4), 208-222.
6) Ghadiri Nejad, M., & Banar, M. (2018). Emergency response time minimization by incorporating ground and aerial transportation. Annals of Optimization Theory and Practice, 1(1), 43-57.
7) Davani, P. P., Kloub, A. W. M., & Ghadiri Nejad, M. (2020). Optimizing the first type of U-shaped assembly line balancing problems. Annals of Optimization Theory and Practice, 3(4), 65-82.
8) Khandan, A., Abdellahi, M., Ozada, N., & Ghayour, H. (2016). Study of the bioactivity, wettability and hardness behaviour of the bovine hydroxyapatite-diopside bio-nanocomposite coating. Journal of the Taiwan Institute of Chemical Engineers, 60, 538-546.
9) Karamian, E., Motamedi, M. R. K., Khandan, A., Soltani, P., & Maghsoudi, S. (2014). An in vitro evaluation of novel NHA/zircon plasma coating on 316L stainless steel dental implant. Progress in Natural Science: Materials International, 24(2), 150-156.
10) Nejad, M. G., Güden, H., & Vizvári, B. (2019). Time minimization in flexible robotic cells considering intermediate input buffers: a comparative study of three well-known problems. International Journal of Computer Integrated Manufacturing, 32(8), 809-819.
11) Najafinezhad, A., Abdellahi, M., Ghayour, H., Soheily, A., Chami, A., & Khandan, A. (2017). A comparative study on the synthesis mechanism, bioactivity and mechanical properties of three silicate bioceramics. Materials Science and Engineering: C, 72, 259-267.
12) Ghayour, H., Abdellahi, M., Ozada, N., Jabbrzare, S., & Khandan, A. (2017). Hyperthermia application of zinc doped nickel ferrite nanoparticles. Journal of Physics and Chemistry of Solids, 111, 464-472.
13) Kazemi, A., Abdellahi, M., Khajeh-Sharafabadi, A., Khandan, A., & Ozada, N. (2017). Study of in vitro bioactivity and mechanical properties of diopside nano-bioceramic synthesized by a facile method using eggshell as raw material. Materials Science and Engineering: C, 71, 604-610.
14) Khandan, A., & Ozada, N. (2017). Bredigite-Magnetite (Ca7MgSi4O16-Fe3O4) nanoparticles: A study on their magnetic properties. Journal of Alloys and Compounds, 726, 729-736.
15) Khandan, A., Jazayeri, H., Fahmy, M. D., & Razavi, M. (2017). Hydrogels: Types, structure, properties, and applications. Biomat Tiss Eng, 4(27), 143-69.
16) Prabhakar Attiguppe , Neetu Malik , Shivani Ballal , Saraswathi V Naik. CPP-ACP and Fluoride: A Synergism to Combat Caries. . Int J Clin Pediatr Dent.Mar-Apr 2019;12(2):120-125.
17) Mehta R, Nandlal B, Prashanth S. Comparative evaluation of remineralization potential of casein phosphopeptide-amorphous calcium phosphate and casein phosphopeptide-amorphous calcium phosphate fluoride on artificial enamel white spot lesion: an in vitro light fluorescence study. Indian J Dent Res. 2013 Nov-Dec;24(6):681-9.
18) Li X, Wang J, Joiner A, Chang J. The remineralisation of enamel: a review of the literature. J Dent. 2014 Jun; 42 Suppl 1(1):S12-20.
19) Al-Mullahi AM, Toumba KJ. Effect of slow-release fluoride devices and casein phosphopeptide/amorphous calcium phosphate nanocomplexes. on enamel remineralization in vitro. Caries Res. 2010;44(4):364-71.
20) Yamaguchi K, Miyazaki M, Takamizawa T, Inage H, Moore BK. Effect of CPP-ACP paste on mechanical properties of bovine enamel as determined by an ultrasonic device. J Dent. 2006 Mar; 34(3):23.
21) Panich M, Poolthong S. The effect of casein phosphopeptide-amorphous calcium phosphate and a cola soft drink on in vitro enamel hardness. J Am Dent Assoc. 2009 Apr; 140(4):455-60.
22) Tantbirojn D, Huang A, Ericson MD, Poolthong S. Change in surface hardness of enamel by a cola drink and a CPP-ACP paste. J Dent. 2008 Jan;36(1):74-9.
23) Ranjitkar S, Kaidonis JA, Richards LC, Townsend GC. The effect of CPP-ACP on enamel wear under severe erosive conditions. Arch Oral Biol. 2009 Jun;54(6):527-32.
24) Srinivasan N, Kavitha M, Loganathan SC. Comparison of the remineralization potential of CPP-ACP and CPP-ACP with 900 ppm fluoride on eroded human enamel: An in situ study. Arch Oral Biol. 2010 Jul;55(7):541-4.
25) Elsayad I, Sakr A, Badr Y. Combining casein phosphopeptide-amorphous calcium phosphate with fluoride: synergistic remineralization potential of artificially demineralized enamel or not? J Biomed Opt. 2009 Jul-Aug;14(4):044039.
26) Hamba H, Nikaido T, Inoue G, Sadr A, Tagami J. Effects of CPP-ACP with sodium fluoride on inhibition of bovine enamel demineralization: a quantitative assessment using micro-computed tomography. J Dent. 2011 Jun;39(6):405-13.
27) Lata S, Varghese NO, Varughese JM. Remineralization potential of fluoride and amorphous calcium phosphate-casein phospho peptide on enamel lesions: An in vitro comparative evaluation. J Conserv Dent. 2010 Jan;13(1):42-6.
28) Oshiro M, Yamaguchi K, Takamizawa T, Inage H, Watanabe T, Irokawa A, et al. Effect of CPP-ACP paste on tooth mineralization: an FE-SEM study. J Oral Sci. 2007 Jun;49(2):115-20.
29) Poggio C, Lombardini M, Dagna A, Chiesa M, Bianchi S. Protective effect on enamel demineralization of a CPP-ACP paste: an AFM in vitro study. J Dent. 2009 Dec;37(12):949-54.
30) Vashisht R, Indira R, Ramachandran S, Kumar A, Srinivasan MR. Role of casein phosphopeptide amorphous calcium phosphate in remineralization of white spot lesions and inhibition of Streptococcus mutans? J Conserv Dent. 2013 Jul;16(4):342-6.
31) Rehder Neto F.C, Maeda F.A, Turssi C.P, Serra M.C. Potetial agents to control enamel caries-like lesions. J Dent. 2009 Jun;37(2):786-790
32) Wu D, Yang J, Li J, Chen L, Tang B, Chen X, et al. Hydroxyapatite-anchored dendrimer for in situ remineralization of human tooth enamel. Biomaterials. 2013 Jul;34(21):5036-47
33) Mosallaeipour, S., Nejad, M. G., Shavarani, S. M., & Nazerian, R. (2018). Mobile robot scheduling for cycle time optimization in flow-shop cells, a case study. Production Engineering, 12(1), 83-94.
34) Honorio HM, Rios D, Santos CF, Magalhaes AC, Delbem AC, Buzalaf MA, et al. Cross-sectional microhardness of human enamel subjected to erosive, cariogenic or combined erosive/cariogenic challenges. Caries Res. 2010;44(1):29-32.
35) Karla Miyahira, Thereza Coutinho, Eduardo Silva, André Pereira, Monica Tostes. Evaluation of CPP-ACP and Fluoride on Inhibition of Human Enamel demineralisation: Cross-sectional Hardness and MicroCT Studies. Oral Health Prev Dent. . 2017;15(6):549-555.
36) Heshmat H, Hoorizad Ganjkar M , Miri Y, Kharrazi Fard MJ. The effect of two remineralizing agents and natural saliva on bleached enamel hardness. Dent Res J (Isfahan). Jan-Feb 2016;13(1):52-7.
37) DA , Abdelrahman AA , Abdelaziz RH , Nagy Dina. Effect of Two Remineralizing Agents on Initial Caries-like Lesions in Young Permanent Teeth: An in Vitro Study. J Contemp Dent Pract. 2018 Oct 1;19(10):1181-1188.
38) Rana Alkattan , Frank Lippert , Qing Tang , George J Eckert , Masatoshi Ando . The influence of hardness and chemical composition on enamel demineralization and subsequent remineralization .J Dent. . 2018 Aug;75:34-40.
39) Indrapriyadharshini K, Madan Kumar PD, Sharma K, Iyer K. Remineralizing potential of CPP-ACP in white spot lesions - A systematic review. Indian J Dent Res. 2018 Jul-Aug;29(4):487-496.
40) Sharafabadi, A. K., Abdellahi, M., Kazemi, A., Khandan, A., & Ozada, N. (2017). A novel and economical route for synthesizing akermanite (Ca2MgSi2O7) nano-bioceramic. Materials Science and Engineering: C, 71, 1072-1078.
41) Khandan, A., Abdellahi, M., Ozada, N., & Ghayour, H. (2016). Study of the bioactivity, wettability and hardness behaviour of the bovine hydroxyapatite-diopside bio-nanocomposite coating. Journal of the Taiwan Institute of Chemical Engineers, 60, 538-546.
42) Shayan, A., Abdellahi, M., Shahmohammadian, F., Jabbarzare, S., Khandan, A., & Ghayour, H. (2017). Mechanochemically aided sintering process for the synthesis of barium ferrite: Effect of aluminum substitution on microstructure, magnetic properties and microwave absorption. Journal of Alloys and Compounds, 708, 538-546
43) Heydary, H. A., Karamian, E., Poorazizi, E., Khandan, A., & Heydaripour, J. (2015). A novel nano-fiber of Iranian gum tragacanth-polyvinyl alcohol/nanoclay composite for wound healing applications. Procedia Materials Science, 11, 176-182.
44) Khandan, A., Karamian, E., & Bonakdarchian, M. (2014). Mechanochemical synthesis evaluation of nanocrystalline bone-derived bioceramic powder using for bone tissue engineering. Dental Hypotheses, 5(4), 155.
45) Karamian, E., Khandan, A., Kalantar Motamedi, M. R., & Mirmohammadi, H. (2014). Surface characteristics and bioactivity of a novel natural HA/zircon nanocomposite coated on dental implants. BioMed research international, 2014.
46) Jabbarzare, S., Abdellahi, M., Ghayour, H., Arpanahi, A., & Khandan, A. (2017). A study on the synthesis and magnetic properties of the cerium ferrite ceramic. Journal of Alloys and Compounds, 694, 800-807.
47) Razavi, M., & Khandan, A. (2017). Safety, regulatory issues, long-term biotoxicity, and the processing environment. In Nanobiomaterials Science, Development and Evaluation (pp. 261-279). Woodhead Publishing.
48) Khandan, A., Ozada, N., & Karamian, E. (2015). Novel microstructure mechanical activated nano composites for tissue engineering applications. J Bioeng Biomed Sci, 5(1), 1.
49) Ghayour, H., Abdellahi, M., Bahmanpour, M., & Khandan, A. (2016). Simulation of dielectric behavior in RFeO $$ _ {3} $$3 orthoferrite ceramics (R= rare earth metals). Journal of Computational Electronics, 15(4), 1275-1283.
50) Saeedi, M., Abdellahi, M., Rahimi, A., & Khandan, A. (2016). Preparation and characterization of nanocrystalline barium ferrite ceramic. Functional Materials Letters, 9(05), 1650068.
51) Khandan, A., Karamian, E., Faghih, M., & Bataille, A. (2014). Formation of AlN Nano Particles Precipitated in St-14 Low Carbon Steel by Micro and Nanoscopic Observations. Journal of Iron and Steel Research International, 21(9), 886-890.
52) Karamian, E. B., Motamedi, M. R., Mirmohammadi, K., Soltani, P. A., & Khandan, A. M. (2014). Correlation between crystallographic parameters and biodegradation rate of natural hydroxyapatite in physiological solutions. Indian J Sci Res, 4(3), 092-9.
53) Khandan, A., & Esmaeili, S. (2019). Fabrication of polycaprolactone and polylactic acid shapeless scaffolds via fused deposition modelling technology. Journal of Advanced Materials and Processing, 7(4), 16-29.
54) Panjwani, D., Pai, M., Yellapurkar, S., Poddar, A., Rajesh, G. and Sharma, M., 2021. A novel behavioral model in initiation and sustenance of toothbrushing behavior among dental and medical students in India: an exploratory analysis. Journal of Natural Science, Biology and Medicine, 12(2), pp.149-149
55) Subramanian, S., Dalmia, P., Gnana, P. P. S., & Appukuttan, D. (2021). Laser excision of intraoral capillary hemangioma. Journal of Natural Science, Biology and Medicine, 12(1), 124. DOI:10.4103/jnsbm.JNSBM_81_20
56) Kumar, V., Nanda, A., Bhat, K. H., Ashrit, P., Babu, A., & Shakir, M. K. (2021). Urease activity in saliva and plaque as endogenous protection against dental caries in institutionalized blind children. Journal of Natural Science, Biology and Medicine, 12(1), 109.
57) Kumar, V., Fernandez, S., Sharma, D. and Kumar, A.H.S., 2021. Publication paradigm among academics in dental sciences and pseudo perceptions of journal quality matrix: A re-look into medical council of India, dental council of India, and university grants commission publication guidelines. Journal of Natural Science, Biology and Medicine, 12(1), p.1
58) Akram, A., ZamZam, R., Mohamad, N. B., Abdullah, D., & Meerah, S. M. (2012). An assessment of the prescribing skills of undergraduate dental students in Malaysia. Journal of Dental Education, 76(11), 1527-1531.
59) Nabishah, B. M., Khalid, B. A. K., Morat, P. B., Alias, A. K., & Zainuddin, M. (1992). Effects of steroid hormones on cyclic adenosine 3′, 5′-monophosphate levels in the rat lung. Journal of endocrinology, 134(1), 73-76.
60) Suhaimi, F. H., Mohamad, N. B., & Kadir, K. B. A. (2006). Isoprenaline reverses glycyrrhizic acid-induced inhibition of 11$-hydroxysteroid dehydrogenase bioactivity. Pakistan Journal of Nutrition, 5(6), 544-547.
61) Othman, Z., Khalep, H. R. H., Abidin, A. Z., Hassan, H., & Fattepur, S. (2019). The Anti-Angiogenic Properties of Morinda citrifolia. L (Mengkudu) Leaves using chicken chorioallantoic membrane (CAM) assay. Pharmacognosy Journal, 11(1).
62) Chen, S. T., Faller, E. M., Kobata, K., Fadli, M. A., & Yeoh, C. S. (2018). Effect of Collagen-Related compound on cell proliferation and matrix production with cultured human dermal fibroblasts. International Journal of Medical Toxicology & Legal Medicine, 21(3and4), 269-273.
63) Khan, J., Kusmahani, S. H., Ruhi, S., Al-Dhalli, S., Kaleemullah, M., Saad, R., ... & Yusuf, E. (2020). Design and evaluation of sustained release matrix tablet of flurbiprofen by using hydrophilic polymer and natural gum. International Journal of Medical Toxicology & Legal Medicine, 23(1and2), 149-159.
64) Saad, R., Asmani, F., Saad, M., Hussain, M., Khan, J., Kaleemullah, M., ... & Yusuf, E. (2015). A new approach for predicting antioxidant property of herbal extracts. Int. J. Pharmacogn. Phytochem. Res, 7(1), 166-174.
65) Ghasemi, M., Nejad, M. G., & Bagzibagli, K. (2017). Knowledge management orientation: an innovative perspective to hospital management. Iranian journal of public health, 46(12), 1639.
66) Ghasemi, M., & Hasanpoor, E. (2021). COVID-19 attack on the world's tourism industry. Evidence Based Health Policy, Management and Economics.
67) Malekzadeh, R., Abedi, G., Abedini, E., Haghgoshayie, E., Hasanpoor, E., & Ghasemi, M. (2020). Use of ethical predictability in respect for human rights in Iranian hospitals with a 360-degree approach. International Journal of Human Rights in Healthcare.
68) Alves KM, Franco KS, Sassaki KT, Buzalaf MA, Delbem AC. Effect of iron on enamel demineralization and remineralization in vitro. Arch Oral Biol. 2011 Nov;56(11):1192-8.
69) Malekzadeh, R., Abedi, G., Abedini, E., Haghgoshayie, E., Hasanpoor, E., & Ghasemi, M. (2021). Ethical predictability of patient safety in Iranian hospitals. International Journal of Risk & Safety in Medicine, 32(1), 51-60.
70) Karamian, E., Abdellahi, M., Khandan, A., & Abdellah, S. (2016). Introducing the fluorine doped natural hydroxyapatite-titania nanobiocomposite ceramic. Journal of Alloys and Compounds, 679, 375-383.
Investigation of enamel surface hardness using remineralization of white spot lesions with CPP-ACP, fluoride and CPP-ACPF
Farzaneh Shirani1*, Shirin Rostami2, Parastoo Afghari3
1Dental Materials Research Center, Dental Research Institute, Department of operative Dentistry, School of Dentistry, Isfahan University of Medical Sciences, Isfahan, Iran
2Department of Periodontics, School of Dentistry, Isfahan University of Medical Sciences, Isfahan, Iran
3Oral and Maxillofacial Radiologist, Self-employed Researcher, Toronto, Canada
Corresponding author: f_shirani@dnt.mui.ac.ir
Abstract: The enamel surface hardness determination plays a key role in surface abrasion a resin composite bond strength. The aim of this study was to investigate the enamel surface hardness after remineralization of white spot lesions using casein phosphopeptide amorphous calcium phosphate (CPP-ACP), fluoride and casein phosphopeptide amorphous calcium phosphate fluoride (CPP-ACPF). Materials and Methods: A 36 bovine anterior teeth were chosen and after decoronization, the teeth were mounted in acrylic resin and their baseline surface hardness was measured. Samples were then demineralized and their surface hardness was measured. The teeth were then divided into three groups and subjected to surface treatment with CPP-ACP, CPP-ACPF and fluoride mouthwash. The surface hardness was measured and the data were analyzed using SPSS software. Results: Paired t-test showed that surface hardness significantly changed after demineralization (P<0.001) and after treatment with CPP-ACPF (P<0.001) and fluoride (P=0.005), however: the change was not significant after treatment with CPP-ACP (P=0.155). Conclusions: The obtained results indicated that treatment with fluoride and CPP-ACPF may increase the surface hardness of demineralized enamel.
Keywords: Casein phosphopeptide-amorphous calcium phosphate nanocomplex; Dental enamel; Fluoride; Hardness; Tooth remineralization
1- Introduction
Demineralization and remineralization occur several times a day for each tooth and it is regulated by many factors such as the number and type of microbial flora present in the biofilm, diet, oral hygiene, genetics, dental anatomy, enamel and dentin composition [1-6]. In the initial phases of caries, demineralization is visible in the form of white opaque spots. Normally, the hydroxyapatite (HA) nanocrystals of the enamel are in balance with the saliva and are rich in phosphate and calcium [1-5]. In presence of calcium and phosphate ions in a neutral pH, demineralization is reversible and the HA nanocrystalline architecture may form again [6-18]. This process is referred to as remineralization and to obtain a suitable result, demineralization should eventually end and followed by remineralization [19-25]; however, this is not always the case [4-6]. Many advances in composition of dental materials and restorative techniques of dental caries have enhanced management of tooth caries and oral health maintenance [5]. Anti-caries features of milk have been previously proven and it directly relates to Ca and PO4 elements and casein phosphopeptide (CPP) in composition of milk [7-11]. The bond of CPP to amorphous calcium phosphate (ACP) hinders the solubility of Ca and PO4 ions. Moreover, CPP-ACP serves as a rich source of phosphate and calcium and keeps the solution saturated. Fluoride is the most commonly used substance to develop remineralization.
An increased in pH results in formation of large fluorohydroxyapatite (FHA) nanocrystals, which are resistant to demineralization. Fast deposition of fluorapatite (FA) makes a hard superficial layer, which is more resistant to demineralization. On the other hand, this layer inhibits deeper penetration of fluoride ions into the carious lesion [26-37]. Therefore, it should be noticed that remineralization of enamel surface with the support of fluoride is self-limited. Therefore, several studies have shown the ability of CPP-ACP for enamel remineralization and calcium and phosphate-based remineralizing agents such as CPP-ACP are increasingly applied in the clinical applications due to CPP-ACP properties which can impede demineralization and enhance remineralization [11-27]. Oshiro et al. showed that the CPP-ACP paste can stop enamel demineralization [28]. These results were confirmed by Pogio et al. [29]. Considering the contradictory results of previous studies [28-38], the influence of surface hardness on abrasion and composite bond present significant changes. In this study, we aimed to assess the effect of fluoride, CCP-ACP paste and CPP-ACPF on enamel surface hardness.
2- Materials and Methods
In this in vitro experimental study, 36 extracted bovine anterior teeth were selected. The teeth belonged to cows older than 30 months and teeth without caries, cracks, enamel defects and discoloration were selected, also the materials used in this work is presented in Figure 1. The teeth were stored in %0.2 thymol solution at room temperature for disinfection. Scaling and root planning were performed and the teeth were sectioned at the cementoenamel junction using a high-speed disc under water coolant. Pulp tissue was removed and the teeth were mounted in auto-polymerizing acrylic resin such that their buccal surface was exposed. Surface hardness of the teeth was measured using automated Knoop hardness tester with 25 g force applied for 10 seconds. The hardness of each surface was measured at five points. At the center and at four other sites with 300 µm distance from each other.
Figure 1: Materials used in this study for hardness analysis
To simulate the oral environment, the surface of each tooth was coated with one layer of thick artificial saliva with the composition mentioned in Table 1.
Table 1: Chemical composition of artificial saliva, remineralizing solution and demineralizing solution.
Demineralizing solution pH=5.0 | Remineralizing solution pH=7.0 | Artificial saliva pH=6.75 |
1.4 mM Ca 0.9 mM P 0.05 M Acetate buffer 0.03 ppm F
| 1.5 mM Ca 0.9 mM P 0.1 Tris buffer 0.05 ppm F | Methyl-p-hydroxybenzoate, 2g Sodium carboxymethyl cellulose,10g KCl 0.625 g MgCl2.6H2O 0.059 g CaCl2 -H2O. 0.166 g K2HPO4, 0.326 g KOH |
For the process of demineralization, the teeth were subjected to pH cycling using the Tencate’s method, which included 30 min of immersion in the demineralizing solution and 150 min of immersion in the remineralizing solution 6 times a day followed by immersion in remineralizing agent for 6 hours for a total of 3 days. After formation of white spot lesions, the surface hardness was measured again as explained earlier as shown in Figure 2.
Figure 2: Demineralization pH cycling
The teeth were then divided into 3 subgroups for treatment with CPP-ACP paste, CPP-ACPF and fluoride mouthwash. The teeth were subjected to therapeutic pH cycling over 30 days as shown in Figure 3.
Figure 3: Remineralization pH cycling
For remineralization of the white spot lesions in groups CCP-ACP and CPP-ACPF, the pastes were applied on the buccal enamel surface by a micro-brush (0.5mm thickness) for 3 minutes according to the manufacturers’ instructions. In the time interval among the 2 cycles, the teeth were washed with distilled water to avoid contamination of the demineralizing solution with the remineralizing solution. Then, the teeth were dried by paper towel and exposed to fresh materials in a new cycle. The surface hardness was then measured again as explained earlier. The surface hardness values were statistically analyzed using SPSS 22 software. The values were compared using repeated measures ANOVA, paired t-test and independent t-test at P=0.05 level of significance. The null hypothesis was that CPP-ACP, fluoride and CPP-ACPF would not have a significant effect on surface hardness.
3- Results & Discussion
Results indicated that the mean surface hardness and the repeated measures ANOVA was used to compare surface hardness at baseline, after demineralization and after treatment. The surface hardness of CCP-ACP group had significant differences with that of other two groups (P<0.001) [38-47].
Figure 4: The average surface hardness for Sample S1, S2, S3, S4 and S5 measured in this study
However, when microorganisms were inoculated from animals with active caries, they developed tooth decay in the presence of carbohydrates. Figure 4 shows the average surface hardness for five specimens. Figure 4 shows the average surface hardness for sample S1 is the highest value in which the sample S2 has the lowest value. The following diagram indicates the average hardness for all samples before demineralization S1. The average hardness value of total samples after demineralization S2 shows the average hardness value of samples in the three treated groups S3, S4, and S5 (see Table 2). The hardness table shows 36 samples on top of each other called base line and then the hardness of the 36 samples in demineralized state. Then, these 36 are divided into three parts and in three treatment groups of 12, hardness were determined. The highest surface hardness belonged to teeth before demineralization (366.7 ± 46.89) and the lowest value was noted in teeth after demineralization (266.6 ± 49.18). Among the treatment groups, the maximum and minimum surface hardness values after treatment belonged to CCP-ACPF (340.5 ± 36.87) and CCP-ACP (331.1 ± 51.29) groups, respectively.
Table 2: Mean surface hardness of groups.
Base line surface hardness mean ±SD= S1 | 366.7±46.89 | |||
Demineralized surface hardness mean±SD =S2 | 266.6±49.18 | |||
Treatment group | CPP-ACP = S3 | 296.2±37.11 | ||
CPP-ACPF = S4 | 340.5±36.87 | |||
F = S5 | 331.3±51.29 | |||
Dental caries and erosion are currently a major public health concern, and prevention is still the best approach to control them. White spot lesions are the first sign of initial caries in smooth surfaces [22, 48-58]. The most important features of initial carious lesions are presence of a sound superficial layer over underlying demineralized layers. Although, the superficial layer is intact, its mineral content has reduced. Therefore, its hardness is lower than that of sound enamel. Various hardness tests such as Vickers and Knoop have been used in previous studies [59-67]. Alves et al. [68] studied HMV-2000 with 25g force for 10 seconds was used. Several researchers performed the Knoop hardness test with 25 g force for 5 seconds and 50g force for 15 seconds. According to Tantbirojn et al. [22] the Knoop test is preferred to Vickers test because the longer diagonal is less affected by elastic recovery. Also, Knoop test was used in our study to measure the surface hardness. Use of calcium- and phosphate-based remineralizing agents such as CPP-ACP is increasing in the clinical setting since they can prevent demineralization and enhance remineralization [27, 68-70]. The mean baseline surface hardness was 366.7 in this study similar to the values reported by Rehder et al, [31] (350).
These values confirm the similarity of bovine teeth to human teeth. Rehder et al. [31] reported the mean surface hardness after demineralization to be 234.16; this value was 288.724. These values after the application of CPP-ACP were +29.4 in our study, +5.3 in the study by Rehder et al. [31]. These values after the application of CPP-ACPF was +74.1 in the present study and +0.6 in the study by Rehder et al. which may be due to duration of use of CPP-ACP and CPP-ACPF in different studies. In the study by Rehder [31], this time was 90 second while in the present study remineralizing agents were used for three minutes for a total duration of one month. Thus, it may be concluded that duration of use of remineralizing agent is an important factor affecting the hardness. In this article, fluoride and CCP-ACPF were effective for enamel remineralization and increased the surface hardness to a value close to the baseline value but single application of CCP-ACP was less effective for this purpose. Therefore, it may be concluded that fluoride and CCP-ACPF can increase the surface hardness close to the baseline value but CCP-ACP is less efficient for this purpose. The results of this study showed that all remineralizing agents were effective for increasing the surface hardness and enamel remineralization.
Figure 5: The bovine anterior teeth without any defects were tested
Although remineralization and demineralization have been extensively studied in the recent decades, there are only a few studies on depth, mineral content and mechanical features of lesions. One limitation of this study was that the effect of remineralizing agents on surface hardness of sound teeth in superficial and underlying layers was not evaluated to compare the values with those of demineralized enamel. Figure 5 demonstrate 36 bovine anterior teeth without any defects were chosen and immersed in 0.2% thymol and after decoronization. Thus, future studies with a sound control group are required to further elucidate this topic. showed that both fluoride and CPP-ACP caused remineralization of demineralized enamel and their combination had a synergistic effect intensifying remineralization [68-70]. Tantbirojn et al. [22] studied the change in hardness of enamel eroded by cola drink after treatment with fluoride and CPP-ACP and found that although fluoride and CPP-ACP effectively increased the surface hardness, the combination of the two did not have a synergistic effect.
4- Conclusion
The obtained results of this study indicated that treatment with fluoride and CPP-ACPF (in contrast to CPP-ACP) can increase the surface hardness of demineralized enamel. The advantageous of this work was investigation of surface hardness of demineralized teeth after their treatment with different remineralizing agents. The highest surface hardness belonged to teeth before demineralization (366.7 ± 46.89) and the lowest value was noted in teeth after demineralization (266.6 ± 49.18). Among the treatment groups, the maximum and minimum surface hardness values after treatment belonged to CCP-ACPF (340.5 ± 36.87) and CCP-ACP (331.1 ± 51.29) groups, respectively. Considering the controversial results, further studies are required to obtain more reliable findings. One limitation of this study was that the effect of remineralizing agents on surface hardness of sound teeth in superficial and underlying layers was not evaluated to compare the values with those of demineralized enamel.
5- Conflicts of interest Statement
The authors declare that they have no conflict of interests.
Authors’ contributions
Farzaneh Shirani: Conceptualization, Methodology, Validation, Resources, Data Curation, Writing - Original Draft, Writing - Review & Editing, Supervision, Funding acquisition.
Shirin Rostami: Formal analysis, Investigation, Resources, Data Curation, Writing - Original Draft, Writing - Review & Editing, Visualization, Project administration.
Parastoo Afghari: Formal analysis, Investigation, Resources, Data Curation, Writing - Original Draft, Writing - Review & Editing, Visualization, Project administration.
Funding
This work was financially supported by Isfahan University of Medical Sciences.
Competing interests
The authors declare that they have no conflict of interests.
Ethics approval
339444
6- References
1) Perdigão J. Resin infiltration of enamel white spot lesions: An ultramorphological analysis. J Esthet Restor Dent. 2020 Apr;32(3):317-324.
2) Chambers C, Stewart S, Su B, Sandy J, Ireland A. Prevention and treatment of demineralisation during fixed appliance therapy: a review of current methods and future applications. Br Dent J. 2013 Nov;215(10):505-11.
3) Ghadirinejad, N., Nejad, M. G., & Alsaadi, N. (2021). A fuzzy logic model and a neuro-fuzzy system development on supercritical CO2 regeneration of Ni/Al2O3 catalysts. Journal of CO2 Utilization, 54, 101706.
4) Nejad, M. G., & Kashan, A. H. (2019). An effective grouping evolution strategy algorithm enhanced with heuristic methods for assembly line balancing problem. Journal of Advanced Manufacturing Systems, 18(03), 487-509.
5) Ghasemi, M., Nejad, M. G., & Aghaei, I. (2021). Knowledge management orientation and operational performance relationship in medical tourism (overview of the model performance in the COVID-19 pandemic and post-pandemic era). Health Services Management Research, 34(4), 208-222.
6) Ghadiri Nejad, M., & Banar, M. (2018). Emergency response time minimization by incorporating ground and aerial transportation. Annals of Optimization Theory and Practice, 1(1), 43-57.
7) Davani, P. P., Kloub, A. W. M., & Ghadiri Nejad, M. (2020). Optimizing the first type of U-shaped assembly line balancing problems. Annals of Optimization Theory and Practice, 3(4), 65-82.
8) Khandan, A., Abdellahi, M., Ozada, N., & Ghayour, H. (2016). Study of the bioactivity, wettability and hardness behaviour of the bovine hydroxyapatite-diopside bio-nanocomposite coating. Journal of the Taiwan Institute of Chemical Engineers, 60, 538-546.
9) Karamian, E., Motamedi, M. R. K., Khandan, A., Soltani, P., & Maghsoudi, S. (2014). An in vitro evaluation of novel NHA/zircon plasma coating on 316L stainless steel dental implant. Progress in Natural Science: Materials International, 24(2), 150-156.
10) Nejad, M. G., Güden, H., & Vizvári, B. (2019). Time minimization in flexible robotic cells considering intermediate input buffers: a comparative study of three well-known problems. International Journal of Computer Integrated Manufacturing, 32(8), 809-819.
11) Najafinezhad, A., Abdellahi, M., Ghayour, H., Soheily, A., Chami, A., & Khandan, A. (2017). A comparative study on the synthesis mechanism, bioactivity and mechanical properties of three silicate bioceramics. Materials Science and Engineering: C, 72, 259-267.
12) Ghayour, H., Abdellahi, M., Ozada, N., Jabbrzare, S., & Khandan, A. (2017). Hyperthermia application of zinc doped nickel ferrite nanoparticles. Journal of Physics and Chemistry of Solids, 111, 464-472.
13) Kazemi, A., Abdellahi, M., Khajeh-Sharafabadi, A., Khandan, A., & Ozada, N. (2017). Study of in vitro bioactivity and mechanical properties of diopside nano-bioceramic synthesized by a facile method using eggshell as raw material. Materials Science and Engineering: C, 71, 604-610.
14) Khandan, A., & Ozada, N. (2017). Bredigite-Magnetite (Ca7MgSi4O16-Fe3O4) nanoparticles: A study on their magnetic properties. Journal of Alloys and Compounds, 726, 729-736.
15) Khandan, A., Jazayeri, H., Fahmy, M. D., & Razavi, M. (2017). Hydrogels: Types, structure, properties, and applications. Biomat Tiss Eng, 4(27), 143-69.
16) Prabhakar Attiguppe , Neetu Malik , Shivani Ballal , Saraswathi V Naik. CPP-ACP and Fluoride: A Synergism to Combat Caries. . Int J Clin Pediatr Dent.Mar-Apr 2019;12(2):120-125.
17) Mehta R, Nandlal B, Prashanth S. Comparative evaluation of remineralization potential of casein phosphopeptide-amorphous calcium phosphate and casein phosphopeptide-amorphous calcium phosphate fluoride on artificial enamel white spot lesion: an in vitro light fluorescence study. Indian J Dent Res. 2013 Nov-Dec;24(6):681-9.
18) Li X, Wang J, Joiner A, Chang J. The remineralisation of enamel: a review of the literature. J Dent. 2014 Jun; 42 Suppl 1(1):S12-20.
19) Al-Mullahi AM, Toumba KJ. Effect of slow-release fluoride devices and casein phosphopeptide/amorphous calcium phosphate nanocomplexes. on enamel remineralization in vitro. Caries Res. 2010;44(4):364-71.
20) Yamaguchi K, Miyazaki M, Takamizawa T, Inage H, Moore BK. Effect of CPP-ACP paste on mechanical properties of bovine enamel as determined by an ultrasonic device. J Dent. 2006 Mar; 34(3):23.
21) Panich M, Poolthong S. The effect of casein phosphopeptide-amorphous calcium phosphate and a cola soft drink on in vitro enamel hardness. J Am Dent Assoc. 2009 Apr; 140(4):455-60.
22) Tantbirojn D, Huang A, Ericson MD, Poolthong S. Change in surface hardness of enamel by a cola drink and a CPP-ACP paste. J Dent. 2008 Jan;36(1):74-9.
23) Ranjitkar S, Kaidonis JA, Richards LC, Townsend GC. The effect of CPP-ACP on enamel wear under severe erosive conditions. Arch Oral Biol. 2009 Jun;54(6):527-32.
24) Srinivasan N, Kavitha M, Loganathan SC. Comparison of the remineralization potential of CPP-ACP and CPP-ACP with 900 ppm fluoride on eroded human enamel: An in situ study. Arch Oral Biol. 2010 Jul;55(7):541-4.
25) Elsayad I, Sakr A, Badr Y. Combining casein phosphopeptide-amorphous calcium phosphate with fluoride: synergistic remineralization potential of artificially demineralized enamel or not? J Biomed Opt. 2009 Jul-Aug;14(4):044039.
26) Hamba H, Nikaido T, Inoue G, Sadr A, Tagami J. Effects of CPP-ACP with sodium fluoride on inhibition of bovine enamel demineralization: a quantitative assessment using micro-computed tomography. J Dent. 2011 Jun;39(6):405-13.
27) Lata S, Varghese NO, Varughese JM. Remineralization potential of fluoride and amorphous calcium phosphate-casein phospho peptide on enamel lesions: An in vitro comparative evaluation. J Conserv Dent. 2010 Jan;13(1):42-6.
28) Oshiro M, Yamaguchi K, Takamizawa T, Inage H, Watanabe T, Irokawa A, et al. Effect of CPP-ACP paste on tooth mineralization: an FE-SEM study. J Oral Sci. 2007 Jun;49(2):115-20.
29) Poggio C, Lombardini M, Dagna A, Chiesa M, Bianchi S. Protective effect on enamel demineralization of a CPP-ACP paste: an AFM in vitro study. J Dent. 2009 Dec;37(12):949-54.
30) Vashisht R, Indira R, Ramachandran S, Kumar A, Srinivasan MR. Role of casein phosphopeptide amorphous calcium phosphate in remineralization of white spot lesions and inhibition of Streptococcus mutans? J Conserv Dent. 2013 Jul;16(4):342-6.
31) Rehder Neto F.C, Maeda F.A, Turssi C.P, Serra M.C. Potetial agents to control enamel caries-like lesions. J Dent. 2009 Jun;37(2):786-790
32) Wu D, Yang J, Li J, Chen L, Tang B, Chen X, et al. Hydroxyapatite-anchored dendrimer for in situ remineralization of human tooth enamel. Biomaterials. 2013 Jul;34(21):5036-47
33) Mosallaeipour, S., Nejad, M. G., Shavarani, S. M., & Nazerian, R. (2018). Mobile robot scheduling for cycle time optimization in flow-shop cells, a case study. Production Engineering, 12(1), 83-94.
34) Honorio HM, Rios D, Santos CF, Magalhaes AC, Delbem AC, Buzalaf MA, et al. Cross-sectional microhardness of human enamel subjected to erosive, cariogenic or combined erosive/cariogenic challenges. Caries Res. 2010;44(1):29-32.
35) Karla Miyahira, Thereza Coutinho, Eduardo Silva, André Pereira, Monica Tostes. Evaluation of CPP-ACP and Fluoride on Inhibition of Human Enamel demineralisation: Cross-sectional Hardness and MicroCT Studies. Oral Health Prev Dent. . 2017;15(6):549-555.
36) Heshmat H, Hoorizad Ganjkar M , Miri Y, Kharrazi Fard MJ. The effect of two remineralizing agents and natural saliva on bleached enamel hardness. Dent Res J (Isfahan). Jan-Feb 2016;13(1):52-7.
37) DA , Abdelrahman AA , Abdelaziz RH , Nagy Dina. Effect of Two Remineralizing Agents on Initial Caries-like Lesions in Young Permanent Teeth: An in Vitro Study. J Contemp Dent Pract. 2018 Oct 1;19(10):1181-1188.
38) Rana Alkattan , Frank Lippert , Qing Tang , George J Eckert , Masatoshi Ando . The influence of hardness and chemical composition on enamel demineralization and subsequent remineralization .J Dent. . 2018 Aug;75:34-40.
39) Indrapriyadharshini K, Madan Kumar PD, Sharma K, Iyer K. Remineralizing potential of CPP-ACP in white spot lesions - A systematic review. Indian J Dent Res. 2018 Jul-Aug;29(4):487-496.
40) Sharafabadi, A. K., Abdellahi, M., Kazemi, A., Khandan, A., & Ozada, N. (2017). A novel and economical route for synthesizing akermanite (Ca2MgSi2O7) nano-bioceramic. Materials Science and Engineering: C, 71, 1072-1078.
41) Khandan, A., Abdellahi, M., Ozada, N., & Ghayour, H. (2016). Study of the bioactivity, wettability and hardness behaviour of the bovine hydroxyapatite-diopside bio-nanocomposite coating. Journal of the Taiwan Institute of Chemical Engineers, 60, 538-546.
42) Shayan, A., Abdellahi, M., Shahmohammadian, F., Jabbarzare, S., Khandan, A., & Ghayour, H. (2017). Mechanochemically aided sintering process for the synthesis of barium ferrite: Effect of aluminum substitution on microstructure, magnetic properties and microwave absorption. Journal of Alloys and Compounds, 708, 538-546
43) Heydary, H. A., Karamian, E., Poorazizi, E., Khandan, A., & Heydaripour, J. (2015). A novel nano-fiber of Iranian gum tragacanth-polyvinyl alcohol/nanoclay composite for wound healing applications. Procedia Materials Science, 11, 176-182.
44) Khandan, A., Karamian, E., & Bonakdarchian, M. (2014). Mechanochemical synthesis evaluation of nanocrystalline bone-derived bioceramic powder using for bone tissue engineering. Dental Hypotheses, 5(4), 155.
45) Karamian, E., Khandan, A., Kalantar Motamedi, M. R., & Mirmohammadi, H. (2014). Surface characteristics and bioactivity of a novel natural HA/zircon nanocomposite coated on dental implants. BioMed research international, 2014.
46) Jabbarzare, S., Abdellahi, M., Ghayour, H., Arpanahi, A., & Khandan, A. (2017). A study on the synthesis and magnetic properties of the cerium ferrite ceramic. Journal of Alloys and Compounds, 694, 800-807.
47) Razavi, M., & Khandan, A. (2017). Safety, regulatory issues, long-term biotoxicity, and the processing environment. In Nanobiomaterials Science, Development and Evaluation (pp. 261-279). Woodhead Publishing.
48) Khandan, A., Ozada, N., & Karamian, E. (2015). Novel microstructure mechanical activated nano composites for tissue engineering applications. J Bioeng Biomed Sci, 5(1), 1.
49) Ghayour, H., Abdellahi, M., Bahmanpour, M., & Khandan, A. (2016). Simulation of dielectric behavior in RFeO $$ _ {3} $$3 orthoferrite ceramics (R= rare earth metals). Journal of Computational Electronics, 15(4), 1275-1283.
50) Saeedi, M., Abdellahi, M., Rahimi, A., & Khandan, A. (2016). Preparation and characterization of nanocrystalline barium ferrite ceramic. Functional Materials Letters, 9(05), 1650068.
51) Khandan, A., Karamian, E., Faghih, M., & Bataille, A. (2014). Formation of AlN Nano Particles Precipitated in St-14 Low Carbon Steel by Micro and Nanoscopic Observations. Journal of Iron and Steel Research International, 21(9), 886-890.
52) Karamian, E. B., Motamedi, M. R., Mirmohammadi, K., Soltani, P. A., & Khandan, A. M. (2014). Correlation between crystallographic parameters and biodegradation rate of natural hydroxyapatite in physiological solutions. Indian J Sci Res, 4(3), 092-9.
53) Khandan, A., & Esmaeili, S. (2019). Fabrication of polycaprolactone and polylactic acid shapeless scaffolds via fused deposition modelling technology. Journal of Advanced Materials and Processing, 7(4), 16-29.
54) Panjwani, D., Pai, M., Yellapurkar, S., Poddar, A., Rajesh, G. and Sharma, M., 2021. A novel behavioral model in initiation and sustenance of toothbrushing behavior among dental and medical students in India: an exploratory analysis. Journal of Natural Science, Biology and Medicine, 12(2), pp.149-149
55) Subramanian, S., Dalmia, P., Gnana, P. P. S., & Appukuttan, D. (2021). Laser excision of intraoral capillary hemangioma. Journal of Natural Science, Biology and Medicine, 12(1), 124. DOI:10.4103/jnsbm.JNSBM_81_20
56) Kumar, V., Nanda, A., Bhat, K. H., Ashrit, P., Babu, A., & Shakir, M. K. (2021). Urease activity in saliva and plaque as endogenous protection against dental caries in institutionalized blind children. Journal of Natural Science, Biology and Medicine, 12(1), 109.
57) Kumar, V., Fernandez, S., Sharma, D. and Kumar, A.H.S., 2021. Publication paradigm among academics in dental sciences and pseudo perceptions of journal quality matrix: A re-look into medical council of India, dental council of India, and university grants commission publication guidelines. Journal of Natural Science, Biology and Medicine, 12(1), p.1
58) Akram, A., ZamZam, R., Mohamad, N. B., Abdullah, D., & Meerah, S. M. (2012). An assessment of the prescribing skills of undergraduate dental students in Malaysia. Journal of Dental Education, 76(11), 1527-1531.
59) Nabishah, B. M., Khalid, B. A. K., Morat, P. B., Alias, A. K., & Zainuddin, M. (1992). Effects of steroid hormones on cyclic adenosine 3′, 5′-monophosphate levels in the rat lung. Journal of endocrinology, 134(1), 73-76.
60) Suhaimi, F. H., Mohamad, N. B., & Kadir, K. B. A. (2006). Isoprenaline reverses glycyrrhizic acid-induced inhibition of 11$-hydroxysteroid dehydrogenase bioactivity. Pakistan Journal of Nutrition, 5(6), 544-547.
61) Othman, Z., Khalep, H. R. H., Abidin, A. Z., Hassan, H., & Fattepur, S. (2019). The Anti-Angiogenic Properties of Morinda citrifolia. L (Mengkudu) Leaves using chicken chorioallantoic membrane (CAM) assay. Pharmacognosy Journal, 11(1).
62) Chen, S. T., Faller, E. M., Kobata, K., Fadli, M. A., & Yeoh, C. S. (2018). Effect of Collagen-Related compound on cell proliferation and matrix production with cultured human dermal fibroblasts. International Journal of Medical Toxicology & Legal Medicine, 21(3and4), 269-273.
63) Khan, J., Kusmahani, S. H., Ruhi, S., Al-Dhalli, S., Kaleemullah, M., Saad, R., ... & Yusuf, E. (2020). Design and evaluation of sustained release matrix tablet of flurbiprofen by using hydrophilic polymer and natural gum. International Journal of Medical Toxicology & Legal Medicine, 23(1and2), 149-159.
64) Saad, R., Asmani, F., Saad, M., Hussain, M., Khan, J., Kaleemullah, M., ... & Yusuf, E. (2015). A new approach for predicting antioxidant property of herbal extracts. Int. J. Pharmacogn. Phytochem. Res, 7(1), 166-174.
65) Ghasemi, M., Nejad, M. G., & Bagzibagli, K. (2017). Knowledge management orientation: an innovative perspective to hospital management. Iranian journal of public health, 46(12), 1639.
66) Ghasemi, M., & Hasanpoor, E. (2021). COVID-19 attack on the world's tourism industry. Evidence Based Health Policy, Management and Economics.
67) Malekzadeh, R., Abedi, G., Abedini, E., Haghgoshayie, E., Hasanpoor, E., & Ghasemi, M. (2020). Use of ethical predictability in respect for human rights in Iranian hospitals with a 360-degree approach. International Journal of Human Rights in Healthcare.
68) Alves KM, Franco KS, Sassaki KT, Buzalaf MA, Delbem AC. Effect of iron on enamel demineralization and remineralization in vitro. Arch Oral Biol. 2011 Nov;56(11):1192-8.
69) Malekzadeh, R., Abedi, G., Abedini, E., Haghgoshayie, E., Hasanpoor, E., & Ghasemi, M. (2021). Ethical predictability of patient safety in Iranian hospitals. International Journal of Risk & Safety in Medicine, 32(1), 51-60.
70) Karamian, E., Abdellahi, M., Khandan, A., & Abdellah, S. (2016). Introducing the fluorine doped natural hydroxyapatite-titania nanobiocomposite ceramic. Journal of Alloys and Compounds, 679, 375-383.