The effect of mechanical activation on the kinetic and formation mechanism of a niobium aluminide based nanocomposite

محورهای موضوعی : Materials synthesis and charachterization

Hossein Mostaan ¹ (Arak University)
Mahdi Rafiei ² (Islamic Azad University, Najaf Abad Branch)
Fathallah Karimzadeh ³ (Isfahan University of Technology)

تاریخ دریافت : 1395/06/24 تاریخ پذیرش : 1395/07/03 تاریخ انتشار : 1395/06/11

کلید واژه: Intermetallic compounds, Nanostructures, DTA, Kinetic study, Niobium,

چکیده مقاله :

In this paper the feasibility of NbAl3/Al2O3 nanocomposite formation through mechanochemical reaction between Al and Nb2O5 and the effect of mechanical activation on the kinetic and reaction mechanism were investigated. Structural and phase evolution during mechanical alloying were studied by employing transmission electron microscopy (TEM), X-ray diffraction (XRD) and differential thermal analysis (DTA) techniques. It was found from the results that the reduction of Nb2O5 by Al takes place in an explosive mode and after 450 min of mechanical alloying leading to the formation a microstructure consisting of NbAl3 matrix and nanocrystalline Al2O3 particles. The results also showed that heating the as-blended powder mixture of Nb2O5 and Al, leads to the formation of NbAl3/Al2O3 composite through two exothermic reaction; A thermite reaction at 880 °C followed by the synthesis of NbAl3 intermetallic at 944 °C. The mechanical activation of Nb2O5 and Al powder for 5h decreased the formation temperature of NbAl3/Al2O3 from 944 °C to 625 °C. Five isoconversional methods, of Kissinger-Akahira-Sunose, Tang, Flynn-Wall-Ozawa, Starink and Friedman were used to determine the activation energy, Eα, for NbAl3/Al2O3 formation reaction and its variation with conversion degree α. The results showed that these methods lead to similar or comparable values of Eα.

منابع و مأخذ:

[1] C. Koch,  "Intermetallic matrix composites prepared by mechanical alloying-a review", Mater. Sci. Eng., A, Vol. 244, 1998, pp. 39–48.

[2] Y. Murayama,  S. Hanada, "Solid solution hardening of Nb₃Al alloys containing tungsten, molybdenum and tantalum", Scr. Mater., Vol. 37, 1997, pp. 949–953.

[3] Y. Abe, S. Hanada, S. Saito, K. Hirano, N. Kobayashi, "Compositions at Nb3Al Phase boundaries at 1873K in the Nb-Al binary phase diagram", Scr. Metall. Mater., Vol. 32, 1995, pp. 27–30.

[4] S. Saito, S. Hanada, K. Ikeda, A. Nagata, K. Noto, "Effect of the layer thickness on Nb3Al superconducting wires", Mater. Sci. Eng., B: B, Vol. 7, 1990, pp. 31–36.

[5] S.K. Dolukhanyan, O.P. Ter Galstyan, A.G. Aleksanyan, A.G. Hakobyan, N.L. Mnatsakanyan, V.S. Shekhtman, "Study of the formation of niobium aluminides in the hydride cycle", Russ. J. Phys. Chem. B, Vol. 9, pp. 2015, 702–709.

[6] C. Milanese, F. Maglia, A. Tacca, U. Anselmi-Tamburini, C.P. Zanotti, iuliani, "Ignition and reaction mechanism of Co–Al and Nb–Al intermetallic compounds prepared by combustion synthesis", J. Alloys Compd., Vol. 421, 2006, pp. 156–162.

[7] V. Gauthier, C. Josse, F. Bernard, E. Gaffet, J. Larpin, "Synthesis of niobium aluminides using mechanically activated self-propagating high-temperature synthesis and mechanically activated annealing process", Mater. Sci. Eng., A, Vol. 265, 1999, pp. 117–128.

[8] Y. Yang, I. Baker, "The influence of vacancy concentration on the mechanical behavior of Fe-40Al", Intermetallics, Vol. 6, 1998, pp. 167–175.

[9] M. Muñoz-Morris, C. Garcia Oca, D. Morris, "Microstructure and room temperature strength of Fe-40Al containing nanocrystalline oxide particles", Acta Mater., Vol. 51, 2003, pp. 5187–5197.

[10] V. Gauthier, F. Bernard, E. Gaffet, C. Josse, J. Larpin, "In-situ time resolved X-ray diffraction study of the formation of the nanocrystalline NbAl₃ phase by mechanically activated self-propagating high-temperature synthesis reaction", Mater. Sci. Eng., A, Vol. 272, pp. 334–341, 1999.

[11] M. Shirani, A. Saidi, M. Kasiri, A. Shirani, "Fabrication of TiC particulate reinforced Ni-50Fe super alloy matrix composite powder by mechanical alloying", J. Adv. Mater. Proc., Vol. 1, 2013, pp. 53–63.

[12] S.Z. Anvari, F. Karimzadeh, M.H.  Enayati, "Synthesis and characterization of NiAl–Al₂O₃ nanocomposite powder by mechanical alloying", J. Alloys Compd., Vol. 477, 2009, pp. 178–181.

[13] M. Rafiei, M.H. Enayati, F. Karimzadeh, "Mechanochemical synthesis of (Fe,Ti)₃Al–Al₂O₃ nanocomposite", J. Alloys Compd., Vol. 488, 2009, pp. 144–147.

[14] T. Mousavi, F. Karimzadeh, M.H. Abbasi, "Mechanochemical assisted synthesis of NiTi intermetallic based nanocomposite reinforced by Al₂O₃", J. Alloys Compd., Vol. 467, 2099, pp. 173–178.

[15] N. Forouzanmehr, F. Karimzadeh, M.H. Enayati, "Synthesis and characterization of TiAl/α-Al₂O₃ nanocomposite by mechanical alloying", J. Alloys Compd., Vol. 478, 2009, pp. 257–259.

[16] G. Williamson, W. Hall, "X-ray line broadening from filed aluminium and wolfram", Acta Metall., Vol. 1, 1953, pp. 22–31.

[17]      C. Suryanarayana, "Mechanical alloying and milling", Prog. Mater Sci., Vol. 46, 2001, pp. 1–184.

[18] T.S. Dyer, Z.A. Munir, "The synthesis of nickel aluminides by multilayer self-propagating combustion", Metall. Mater. Trans. B, Vol. 26, 1995, pp. 603–610.

[19] H. Mostaan, F. Karimzadeh, M.H. Abbasi, "Investigation of in-situ synthesis of NbAl₃/Al₂O₃ nanocomposite by mechanical alloying and its formation mechanism", J. Alloys Compd., Vol. 503, 2010, pp. 294–298.

 [20]     N.J. Welham, "Mechanical activation of the solid-state reaction between Al and TiO₂", Mater. Sci. Eng., A, Vol. 255, 1998, pp. 81–89.

[21] A.A. Joraid, A.A. Abu-Sehly, M.A. El-Oyoun, S.N. Alamri, "Nonisothermal crystallization kinetics of amorphous Te_51.3As_45.7Cu₃", Thermochim. Acta, Vol. 470, 2008, pp. 98–104.

[22] M.J. Starink, "Activation energy determination for linear heating experiments: deviations due to neglecting the low temperature end of the temperature integral", J. Mater. Sci., Vol. 42, 2006, pp. 483–489.