Thermal Stability and Dynamic Magnetic Properties of NiO/Fe Multilayered Thin Films Prepared by Oblique-Angle Sputtering Technique
محورهای موضوعی : Magnetic Materialskhalil gheisari 1 , C.K. Ong 2
1 - Department of Materials Science and Engineering, Faculty of Engineering, Shahid Chamran University of Ahvaz, Ahvaz, Iran
2 - Center for Superconducting and Magnetic Materials, Department of Physics, National University of Singapore, Singapore
کلید واژه: Sputtering, Thin films, Magnetic anisotropy, NiO/Fe Film, Ferromagnetic resonance frequency,
چکیده مقاله :
In this work, the bilayer NiO/Fe thin films compared with single-layer Fe film were deposited on Si (100) substrate using the sputtering technique at deposition angles of 0° and 31.5°. Structure, the static magnetic properties, and the temperature dependence of the dynamic magnetic properties in the range from 300 K to 420 K have been investigated. The results show that the nanocrystalline BCC phase of Fe with the average crystallite size of 11-12 nm and (110) preferred orientation is formed during the deposition process. The resonance frequency is found to rise from 1.03 GHz to 1.13 GHz by employing the NiO sublayer for the typically deposited Fe film. Moreover, the resonance frequency increases for the NiO/Fe films from 1.13 GHz to 1.67 GHz as the deposition angle increases from 0° and 31.5° as a result of the increase in the magnetic anisotropy from 16 Oe to 45 Oe. The permeability values decrease for both as-deposited films with increasing temperature; however, the higher values of the permeability are observed for the film obtained at a deposition angle of 31.5°.
[1] X. Zhong, N.N. Phuoc, Y. Liu, C. Ong, Employment of Co underlayer and oblique deposition to obtain high resonance frequency and excellent thermal stability in FeCo thin films, Journal of magnetism and magnetic materials, 365 (2014) 8-13.
[2] X. Zhu, Z. Wang, Y. Zhang, L. Xi, J. Wang, Q. Liu, Tunable resonance frequency of FeNi films by oblique sputtering, Journal of magnetism and magnetic materials, 324 (2012) 2899-2901.
[3] L. Phua, N. Phuoc, C. Ong, Effect of Ni concentration on microstructure, magnetic and microwave properties of electrodeposited NiCoFe films, Journal of alloys and compounds, 543 (2012) 1-6.
[4] K. Gheisari, C. Ong, Magnetic properties and thermal stability of nanocrystalline Fe films prepared by oblique sputtering deposition method, Physica B: Condensed Matter, 595 (2020) 412365.
[5] K. Gheisari, C. Ong, Enhancing High-Frequency Properties of Nanocrystalline Sputtered Fe Thin Films by Using MnIr Underlayer and Oblique Deposition, Journal of Superconductivity and Novel Magnetism, 3-5- 1 (2021) 4.
[6] L. Phua, N. Phuoc, C. Ong, Investigation of the microstructure, magnetic and microwave properties of electrodeposited NixFe1− x (x= 0.2–0.76) films, Journal of alloys and compounds, 520 (2012) 132-139.
[7] X. Zhong, N.N. Phuoc, G. Chai, Y. Liu, C. Ong, Thermal stability and dynamic magnetic properties of FeSiAl films fabricated by oblique deposition, Journal of alloys and compounds, 610 (2014) 126-131.
[8] Y. Fukuma, Z. Lu, H. Fujiwara, G. Mankey, W. Butler, S. Matsunuma, Strong uniaxial magnetic anisotropy in CoFe films on obliquely sputtered Ru underlayer, in, American Institute of Physics, 2009.
[9] N.N. Phuoc, C. Ong, FeCoHfN thin films fabricated by co-sputtering with high resonance frequency, Journal of alloys and compounds, 509 (2011) 4010-4013.
[10] N.N. Phuoc, G. Chai, C. Ong, Enhancing exchange bias and tailoring microwave properties of FeCo/MnIr multilayers by oblique deposition, Journal of Applied Physics, 112 (2012) 113908.
[11] B.K. Kuanr, R. Camley, Z. Celinski, Exchange bias of NiO/NiFe: Linewidth broadening and anomalous spin-wave damping, Journal of applied physics, 93 (2003) 7723-7725.
[12] S. Husain, V. Barwal, N.K. Gupta, S. Hait, S. Chaudhary, Tunable magnetic anisotropy in obliquely sputtered Co60Fe40 thin films on Si (100), Physica B: Condensed Matter, 570 (2019) 1-5.
[13] C. Hsu, S. Chen, W. Liao, F. Yuan, W. Chang, J. Tsai, Effect of Pt underlayer on the coercivity of FePt sputtered film, Journal of alloys and compounds, 449 (2008) 52-55.
[14] X. Liu, H. Kanda, A. Morisako, The effect of underlayers on FeCo thin films, in: Journal of Physics: Conference Series, IOP Publishing, 2011, pp. 012037.
[15] G. Chai, N.N. Phuoc, C. Ong, Optimizing high-frequency properties of stripe domain ferrite doped CoFe thin films by means of a Ta buffer layer, Journal of Physics D: Applied Physics, 46 (2013) 415001.
[16] Z. Liu, C. Ong, Microstructure and thickness dependent magnetic properties of nanogranular Co–Zn–O thin films for microwave applications, Journal of alloys and compounds, 509 (2011) 10075-10079.
[17] M. Belusky, S. Lepadatu, J. Naylor, M. Vopson, Study of roughness effect in Fe and Co thin films prepared by plasma magnetron sputtering, Physica B: Condensed Matter, 574 (2019) 411666.
[18] M. Zölfl, S. Kreuzer, D. Weiss, G. Bayreuther, Epitaxial nanomagnets with intrinsic uniaxial in-plane magnetic anisotropy, Journal of Applied Physics, 87 (2000) 7016-7018.
[19] X. Zhong, N.N. Phuoc, W.T. Soh, C. Ong, L. Peng, L. Li, Tailoring the magnetic properties and thermal stability of FeSiAl-Al2O3 thin films fabricated by hybrid oblique gradient-composition sputtering, Journal of Magnetism and Magnetic Materials, 429 (2017) 52-59.
[20] F. Tang, D.-L. Liu, D.-X. Ye, Y.-P. Zhao, T.-M. Lu, G.-C. Wang, A. Vijayaraghavan, Magnetic properties of Co nanocolumns fabricated by oblique-angle deposition, Journal of applied physics, 93 (2003) 4194-4200.
[21] J. Ma, X. Ni, J. Huang, J. Li, Effects of Dipolar Interaction on Magnetic Properties of Fe x (SiO2) 1− x Nanocomposites, Journal of nanoscience and nanotechnology, 10 (2010) 791-797.
[22] N. N. Jiang, Y. Yang, Y. X. Zhang, J. P. Zhou, P. Liu, C.-Y. Deng, Influence of zinc concentration on structure, complex permittivity and permeability of Ni–Zn ferrites at high frequency, Journal of Magnetism and Magnetic Materials, 401 (2016) 370-377.
[23] N. Borhan, K. Gheisari, Structural and magnetic properties of nanocrystalline lithium–zinc ferrite synthesized by microwave-induced glycine–nitrate process, Journal of Superconductivity and Novel Magnetism, 27 (2014) 1483-1490.