Influence of Nd3+ ions on TL characteristics of Li2O-MO-B2O3 (MO = ZnO, CaO, CdO) glass system
محورهای موضوعی : Journal of Theoretical and Applied PhysicsJ. Anjaiah 1 , C. Laxmikanth 2 , Cephas John Lyobha 3 , N. Veeraiah 4 , P. Kistaiah 5
1 - Department of Physics, The University of Dodoma;Department of Physics, Geethanjali College of Engineering and Technology
2 - Department of Physics, The University of Dodoma
3 - Department of Physics, The University of Dodoma
4 - Department of Physics, Acharya Nagarjuna University
5 - Department of Physics, Osmania University
کلید واژه: Infra red spectra, Thermoluminescence, Borate glasses, Neodymium,
چکیده مقاله :
AbstractThermoluminescence (TL) characteristics of X-ray irradiated pure and doped with Nd3+ ions glasses have been studied in the temperature range 303–573 K; all the pure glasses have exhibited single TL peak at 382, 424 and 466 K, respectively. When these glasses are doped with Nd3+ ions no additional peaks are observed but the glow peak temperature of the existing glow peak shifted gradually towards higher temperatures with gain in intensity of TL light output. The area under the glow curve is found to be maximum for Nd3+-doped glasses mixed with cadmium oxide as modifier. The trap depth parameters associated with the observed TL peaks have been evaluated using Chen’s formulae. The possible use of these glasses in radiation dosimetry has been described. The result clearly showed that neodymium (Nd)-doped cadmium borate glass has a potential to be considered as the thermoluminescence dosimeter.