Effects of Friction Stir Processing on Mechanical Properties of AA7075 Aluminum Alloy after Joining by Gas Tungsten Arc Welding

محورهای موضوعی : Manufacturing process monitoring and control

Hamed Fotouhi ¹ , Sayed Ahmad Behgozin ² , Ahmad Afsari ³

1 - Mechanical Engineering Department, National University of Skills (NUS), Tehran, Iran
2 - Department of Mechanical Engineering, Shiraz Branch, Islamic Azad University, Shiraz, Iran P.O.B. 71365-364 Shiraz, Iran
3 - Department of Mechanical Engineering, Shiraz Branch, Islamic Azad University, Shiraz, Iran P.O.B. 71365-364 Shiraz, Iran

تاریخ دریافت : 1403/07/05 تاریخ پذیرش : 1403/10/04 تاریخ انتشار : 1403/12/09

کلید واژه: FSP, TIG, Grain Refinement, 7075-T6 Aluminum Alloy, Micro-Hardness, Elongation, Ultimate Tensile Strength, Yield Strength,

چکیده مقاله :

Friction stir processing (FSP) is a method of changing the properties of a metal through intense, localized plastic deformation. The influence of FSP on the mechanical properties of AA7075-T6 aluminum alloy welded by Gas Tungsten Arc Welding (GTAW) was investigated. The original and friction Stir-processed welds were assessed, and their microstructure and mechanical properties were compared. FSP was found to produce a great extent of refinement in microstructure accompany with uniformly distributed fine particles. Using FSP improved the mechanical properties of the welds, particularly those joined by GTAW, through grain refinement in the fusion zone (FZ). The FSP at 1600 rpm and 80 mm/min improved the elongation, tensile strength, and hardness of 7075-T6 aluminum alloy. FSP increased the tensile properties of 7075-T6 GTAW due to grain refinement of the weld zone by 14 percent. Elongation increased about 200 percent for the joint fabricated using WS of 80 mm per min and RS of 1600 rpm compared to unprocessed weld. Hardness decreased from 120 Hv to 60 Hv after welding and then increased to 90 Hv after FSP. Decreasing hardness attributed to welding heat effects, which increase after FSP, is related to grain refinement. This work showed that FSP is an effective method for improving the mechanical properties of fusion welds in 7075 Al-Zn alloy through microstructural modification.

چکیده انگلیسی:

Friction stir processing (FSP) is a method of changing the properties of a metal through intense, localized plastic deformation. The influence of FSP on the mechanical properties of AA7075-T6 aluminum alloy welded by Gas Tungsten Arc Welding (GTAW) was investigated. The original and friction Stir-processed welds were assessed, and their microstructure and mechanical properties were compared. FSP was found to produce a great extent of refinement in microstructure accompany with uniformly distributed fine particles. Using FSP improved the mechanical properties of the welds, particularly those joined by GTAW, through grain refinement in the fusion zone (FZ). The FSP at 1600 rpm and 80 mm/min improved the elongation, tensile strength, and hardness of 7075-T6 aluminum alloy. FSP increased the tensile properties of 7075-T6 GTAW due to grain refinement of the weld zone by 14 percent. Elongation increased about 200 percent for the joint fabricated using WS of 80 mm per min and RS of 1600 rpm compared to unprocessed weld. Hardness decreased from 120 Hv to 60 Hv after welding and then increased to 90 Hv after FSP. Decreasing hardness attributed to welding heat effects, which increase after FSP, is related to grain refinement. This work showed that FSP is an effective method for improving the mechanical properties of fusion welds in 7075 Al-Zn alloy through microstructural modification.

منابع و مأخذ:

[1] Isadare, A.O., Aremo, B. and Adeoye, M.O. 2013. Effect of Heat treatment on some mechanical properties of 7075 alloy. Material research. 16(1) :190-194. doi: 10.1590/s1516-14392012005000167.
[2] Imran, M. and Anwar Khan, A.R. 2019. Characterization of Al-7075 metal matrix composites: a review. Materials Research and Technology. 8(3):3347-3356. doi: 10.1016/j.jmrt.2017.10.012.
[3] Kumar, A., Fuloria, D., Srivastava, M. and Rathee, S. 2024. Fundamentals of Friction Stir Processing. Friction Stir Welding and Processing. doi: 10.1002/9781394169467.
[4] Balasubramanian, V., Ravisankar, V. and Madhusudhan Reddy, G. 2008. Influences of pulsed current welding and post weld aging treatment on fatigue crack growth behaviour of AA7075 aluminum alloy joints. Fatigue. 30(3):405–416. doi: 10.1016/j.ijfatigue.2007.04.012.
[5] Arwin, R., Abraham, S., Rajendran, P. and Shanmugasundaram, R.P. 2024. Reinforcement of SiC Particles on Friction Stir Processing of Aluminium AA7050. International Conference on Processing and Performance of Materials, (ICPPM). doi: 10.3390/engproc2024061045.
[6] Hariharan, V., Elumalai, P.V. and Nambiraj, M., Jayakar, J., Parthasarathy, M. and Venkata Kamesh, V. 2021. Experimental investigation of friction stir welding on aluminum AA6063. Materials Today: Proceedings. 47(19):6830-6834. doi: 10.1016/j.matpr.2021.05.140.
[7] Girish, G. 2023. Effect of tool pin geometry and multi-pass intermittent friction stir processing on the surface properties of aerospace grade aluminum 7075 alloy. Proceedings of the Institution of Mechanical Engineers, Part E: Journal of Process Mechanical Engineering. doi: 10.1177/09544089231158948.
[8] Hashmi, A.W, Mehdi, H, Mabuwa, S, Msomi, V. and Mohapatra, P. 2022. Influence of FSP parameters on wear and microstructural characterization of dissimilar TIG welded joints with Si-rich filler metal. Silicon. 14(17):11131-45. doi: 10.1007/s12633-022-01848-8.
[9] Sterling, C.J, Nelson, T.W, Sorensen, C.D. and Posada, M. 2004. Effects of friction stir processing on the Microstructure and Mechanical properties of fusion weld 304L Stainless Steel. BYU theses and dissertation. 1-52. doi: 10.21236/ada515247.
[10] Yamamoto, H., Imagawa, Y., Ito, K, Chen, K. and Zhang L. 2021. Alloying a topmost steel-plate layer with WC tool constituent elements during friction stir processing. Journal of Manufacturing Processes. 69:311-9. doi: 10.1016/j.jmapro.2021.07.050.
[11] Prasad, R. K., Janaki Ram, G.D. and Stucker, B.E. 2010. Effect of friction stir processing on corrosion resistance of aluminium–copper alloy GTA welds. Materials and Design. 31:1576–1580. doi: 10.1016/j.matdes.2009.09.029.
[12] Parkhe, S.S. and Patil, R.J. 2023. A Review of Friction Stir Welding and Processing on Aluminum Alloys. Journal of Mines, Metals and Fuels. doi: 10.18311/jmmf/2023/34919.
[13] Jata, K.V., Sankaran, K.K. and Ruschau, J. 2000. Friction stir welding effects on microstructure and fatigue of aluminum alloy 7050- T7451, Metallurgical and Materials Transactions A. 31(9):2181–2192. doi: 10.1007/s11661-000-0136-9.
[14] Uematsu, Y., Tokaji, K., Shibata, H., Tozaki, Y. and Ohmune, T. 2009. Fatigue behavior of friction stir welds without neither welding flash nor flaw in several aluminum alloys. International Journal of Fatigue. 31:1443–1453. doi: 10.1016/j.ijfatigue.2009.06.015.
[15] Ma, Z.Y., Sharma, S.R. and Mishra, R.S. 2006. Effect of friction stir processing on the microstructure of cast A356 aluminum, Materials Science and Engineering A. 433:269–278. doi: 10.1016/j.msea.2006.06.099.
[16] Cavalierea, P., Nobilea, R., Panella, F.W. and Squillace, A. 2006. Mechanical and microstructural behaviour of 2024-7075 aluminum alloy sheets joined by friction stir welding. Machine Tools & Manufacture. 46:588–594. doi: 10.1016/j.ijmachtools.2005.07.010.
[17] Rajakumar S., Muralidharan C. and Balasubramanian V. 2011. Influence of friction stir welding process and tool parameters on strength properties of AA7075-T6 aluminum alloy joints. Materials and Design. 32:535–549. doi: 10.1016/j.matdes.2010.08.025.
[18] Flores, O.V., Kennedy, C., Murr, L.E., Brown, D., Pappu, S. and Nowak, B.M. Microstructural issues in a friction stir welded aluminum alloy, Scripta Mater. 1998. 38(5):703–708. doi: 10.1016/s1359-6462(97)00551-4.
[19] Elangovan K. and Balasubramanian V. 2008. Influences of tool pin profile and welding speed on the formation of friction stir processing zone in AA2219 aluminum alloy. Materials processing technology. 200:163–175. doi: 10.1016/j.jmatprotec.2007.09.019.