Comparison of Tribological Behavior of Single-Layer and Multilayer Electroless Nickel-Phosphorus Coatings in the Presence of Al2O3 and SiC Reinforcing Particles
محورهای موضوعی : Journal of Environmental Friendly Materials
A.I. Abduljaleel Al Rabeeah
1
(Department of Materials Engineering, South Tehran Branch, Islamic Azad University, Tehran, Iran.)
M. Razazi Boroujeni
2
(Department of Materials Engineering, Lenjan Branch, Islamic Azad University, Isfahan, Iran.)
کلید واژه: Multilayer Coating, Wear Mechanism, Adhesion, Nickel-Phosphorus,
چکیده مقاله :
Due to their morphology, chemical composition, and phase structure, electroless nickel-phosphorus coatings are used on various substrates, including st37 steel, with the aim of improving working life in various industries. The latest generation of these coatings is the multilayer or hybrid type of nickel-phosphorus electroless coatings. In this research, for the first time, a three-layer Ni-P/Ni-P-Al2O3/Ni-P-SiC coating was produced and its tribological properties were investigated. X-ray diffraction test, energy beam spectrometer, optical and electron microscope images, hardness measurement, roughness measurement, adhesion test (according to ASTM B571 standard), and pin-on-disk wear (according to ASTM-G99 standard) were used for characterization. In the X-ray diffraction pattern related to the multilayer coating, in addition to the amorphous nickel-phosphorus phase, SiC and Al2O3 phases were also seen. The hardness of multilayer coating was 126 Vickers more than that of single-layer coating. The adhesion of all the coatings was very good, so after performing the bending test, no galling was observed in the coatings. In general, it was found that the use of multi-layer coating compared to single-layer coating (with the same thickness) leads to increased hardness, better adhesion, and superior wear behavior. The wear mechanism of the coatings was also evaluated with the help of electron microscope images and energy-dispersive X-ray spectroscopy. The wear mechanism of the electroless nickel-phosphorus coating was delamination and Abrasive, while the hybrid coating changed the mechanism to adhesive by creating a gradient of mechanical properties and lubrication.
Due to their morphology, chemical composition, and phase structure, electroless nickel-phosphorus coatings are used on various substrates, including st37 steel, with the aim of improving working life in various industries. The latest generation of these coatings is the multilayer or hybrid type of nickel-phosphorus electroless coatings. In this research, for the first time, a three-layer Ni-P/Ni-P-Al2O3/Ni-P-SiC coating was produced and its tribological properties were investigated. X-ray diffraction test, energy beam spectrometer, optical and electron microscope images, hardness measurement, roughness measurement, adhesion test (according to ASTM B571 standard), and pin-on-disk wear (according to ASTM-G99 standard) were used for characterization. In the X-ray diffraction pattern related to the multilayer coating, in addition to the amorphous nickel-phosphorus phase, SiC and Al2O3 phases were also seen. The hardness of multilayer coating was 126 Vickers more than that of single-layer coating. The adhesion of all the coatings was very good, so after performing the bending test, no galling was observed in the coatings. In general, it was found that the use of multi-layer coating compared to single-layer coating (with the same thickness) leads to increased hardness, better adhesion, and superior wear behavior. The wear mechanism of the coatings was also evaluated with the help of electron microscope images and energy-dispersive X-ray spectroscopy. The wear mechanism of the electroless nickel-phosphorus coating was delamination and Abrasive, while the hybrid coating changed the mechanism to adhesive by creating a gradient of mechanical properties and lubrication.
[1] Kumar S, Banerjee T, Patel D. Tribological characteristics of electroless multilayer coating: a review. Mater.Today: proc. 2020; 33:5678-82.
[2] Fayyad EM, Abdullah AM, Hassan MK, Mohamed AM, Jarjoura G, Farhat Z. Recent advances in electroless-plated Ni-P and its composites for erosion and corrosion applications: a Rev. Emergent Mater. 2018; 1:3-24.
[3] Sudagar J, Lian J, Sha W. Electroless nickel, alloy, composite and nano coatings–A critical Rev. J. Alloys Compd. 2013; 571:183-204.
[4] Wang Y, Shu X, Wei S, Liu C, Gao W, Shakoor RA, Kahraman R. Duplex Ni–P–ZrO2/Ni–P electroless coating on stainless steel. J. Alloys Compd. 2015; 630:189-94,
[5] Vitry V, Bonin L. Formation and characterization of multilayers borohydride and hypophosphite reduced electroless nickel deposits. Electrochim. Acta. 2017; 243:7-17.
[6] Hong LI, Guo RX, Zhu LI. Characteristics of microstructure and performance of laser-treated electroless Ni–P/Ni–W–P duplex coatings. Trans. Nonferrous Met. Soc. China. 2012; 22(12):3012-20.
[7] Wang SJ, Wang Y, Shu X, Tay S, Gao W, Shakoor RA, Kahraman R, Preparation and property of duplex Ni–B–TiO2/Ni nano-composite coatings.
Int. J. Mod. Phys. B. 2015; 29(10n11):1540022.
[8] Yang Z, Xu H, Shi YL, Li MK, Huang Y, Li HL. The fabrication and corrosion behavior of electroless Ni–P-carbon nanotube composite coatings. Mater. Res. Bull. 2005; 40(6):1001-9.
[9] Mohanty S, Jamal N, Das AK, Prashanth KG. Electroless Ni-P-MoS2-Al2O3 composite coating with hard and self-lubricating properties. Mater. 2022; 15(19):6806.
[10] Ranganatha S, Venkatesha TV, Vathsala K. Development of electroless Ni–Zn–P/nano-TiO2 composite coatings and their properties. Appl. Surf. Sci. 2010; 256(24):7377-83,
[11] Shu X, He Z, Wang Y, Yin L. Mechanical properties of Ni-based coatings fabricated by electroless plating method. Surf Eng. 2020; 36(9):944-51.
[12] Singh G, Mohanty S, Singh RK, Dixit AR, Sharma AK. Comparative study on electroless composite coatings of textured and untextured Al-substrates. Mater. Today: Proc. 2023; 80:233-40.
[13] Murali P, Gopi R, Saravanan I, Devaraju A, Karthikeyan M. Wear and mechanical properties of electroless NiP and NiP-Silicon Carbide (SiC) composite coatings on En8 steel. Mater. Today: Proc. 2022; 68:1707-10.
[14] Wang Y, Guan L, He Z, Zhang S, Singh H, Hayat MD, Yao C. Influence of pretreatments on physicochemical properties of Ni-P coatings electrodeposited on aluminum alloy. Mater. Des. 2021; 197:109233.
[15] Ni M, Wang S, Huang W, Li W. A novel self-lubricating Ni-P-AlN-WS 2 nanocomposite coating. Mater. Res. Express. 2019; 6(11):116413.
[16] Cao J, Zhao W, Wang X, Zhao Y, Ma P, Jiang W, Song G. The microstructure and tribological behavior of ultrasonic electroless Ni-P plating on TC4 titanium alloy with heat-treatment. Ferroelectrics. 2022; 589(1):1-1.