An Studying on the Synthesis and Densification Behavior of β''- Alumina Electrolyte for Sodium-Sulfur Batteries

Subject Areas : journal of New Materials

هاجر Ahmadi Moghadam ¹ , M. H Paaydar ²

1 - دانشجوی دکتری بخش مهندسی مواد دانشگاه شیراز.
2 - استاد، هیئت علمی بخش مهندسی مواد دانشگاه شیراز.

Received: 2016-05-20 Accepted : 2016-05-20 Published : 2015-12-22

Keywords: Microstructure, β''- Alumina, Zeta Process, Sintering, Synthesize,

Abstract :

β''-Alumina electrolyte as a sodium ion conductor is used in sodium sulfur batteries. To obtain the appropriate ionic conductivity, this electrolyte should gain high density and uniform microstructure during manufacturing process. For this purpose, in the present work, β''-alumina powder was synthesized and the parameters influencing the densification behavior of β''-alumina ceramic have been studied. β''- alumina powder synthesized by the zeta process and the raw samples were formed by uniaxial pressing and sintered at different temperatures and for different times. The phase identification of the synthesized powder and fabricated electrolyte was performed by X-ray diffraction (XRD), scanning electron microscopy and measuring of density were used to investigate the densification behavior. The results showed that the microstructure of the β''-alumina ceramics strongly depends on the sintering conditions.Decreasing in the density and the duplex microstructure occurred with increasing the time of the sintering. The optimum condition for the sinte ring of the β''- alumina electrolyte was determined to be at 1620 ºC for 15 min, which results in a dense sample with more than 99% of theoretical density, uniform microstructure, without excessive grain growth and the lack of duplex microstructure including more than 99 percent β''-Al₂O₃ phase.

References:

1- J. L. Sudworth and A. R. Tilley, The Sodium Sulphur Battery, p. 33, Chapman and Hall, London, 1985.

2- L. Xiaochuan, X. Guanguang, P .John and Y. Zhenguo, "Advanced Materials for Sodium-Beta Alumina Batteries: Status, Challenges and Perspectives", Power Sources, Vol. 195, pp. 2431-2442, 2010.

3- T. Oshima, M. Kajita and A. Okuno, "Development of Sodium-Sulfur Batteries", Applied Ceramic Technology, Vol. 1, pp. 269-276, 2004.

4- V. Jayaraman,T. Gnanasekaran and G. Periaswami, "Low-temperature synthesis of β-Aluminas by a Sol-Gel technique",Materials Letters, Vol. 30, pp. 157-162,1997.

5- A. Mali and A. Petr, "Synthesis of Sodium -Alumina powder by Sol–Gel Combustion", European Ceramic Society, Vol. 32, pp. 1229-1234, 2012.

6- S. Sartori,A. Martucci,A. Muffato and M. Guglielmi, "Sol-gel synthesis of Na- beta-Al₂O₃ Powders", European Ceramic Society, Vol. 24, pp. 911-914, 2004.

7- T. Mathews, "Solution Combustion Synthesis of Magnesium Compensated Sodium-β-aluminas", Materials Science and Engineering B, Vol. 78, pp. 39-43, 2000.

8- K. Lee,S. Lee,D. Lee and S. Lim, "Phase formation of Na-Beta-Alumina Synthesized by Double Zeta Process," Industrial and Engineering Chemistry, Vol. 19, pp. 829-837, 2013.

9-ز. شرافت و م. پایدار،"بررسی تاثیر افزودنی اکسید مس بر روند زینترینگ ، ریز ساختار و هدایت پروتونی ترکیبات زیرکونات باریم،"مجله مواد نوین، سال1 شماره 4، ص 85-75، تابستان 1390.

11- A. I. Sitnikov, G. B. Telnova, L. I. Shvorneva, A. Yu. Fedotovand and K. A. Solntsev, Study of the Thermomechanical Properties of a Ceramic Based Sodium Polyaluminate with the Structure of Na- β″- Alumina", Refractories and Industrial Ceramics, Vol. 53, No. 5, January, 2013.

12- A.V. Virkar and S.R. Gordon, "Fracture Properties of Poly Crystalline Lithia – Stabilized βʺ-Alumina", American Ceramic Society, vol. 60, pp.58-61, 1977.    

13- Y. Sheng and P. Nicholson, "Microstructural development of a ZrO₂-Na-β″-Al₂O₃ composite", Materials Science, Vol. 23, pp. 982-986, 1988.

14- M. W. Barsoum, Fundamentals of Ceramics, pp. 334, CRC Press, 2002.