Synthesis and thermal stability of nanocrystalline Mg-6Al-1Zn-1Si alloy prepared via mechanical alloying

Subject Areas : Materials synthesis and charachterization

Roholamin Sedighi ¹ (Department of Material Science and Engineering, Faculty of Mechanical Engineering, Babol Noshirvani University of Technology, Babol, Iran)
Mohammad Rajabi ² (Department of Material Science and Engineering, Faculty of Mechanical Engineering, Babol Noshirvani University of Technology)
Seyed Mahmood Rabiee ³ (Department of Material Science and Engineering, Faculty of Mechanical Engineering, Babol Noshirvani University of Technology, Babol, Iran)

Received: 2014-11-06 Accepted : 2014-12-19 Published : 2015-03-01

Keywords: Thermal stability, mechanical alloying, Mg-based alloy, Grain growth, Mechanical Strength,

Abstract :

Thermal stability and the kinetics of the grain growth of nano-crystalline Mg-6Al-1Zn-1Si alloy prepared via mechanical alloying (MA) were investigated. It started with elemental powders, using a variety of analytical techniques including differential scanning calorimetry (DSC), X-ray diffraction method (XRD), and scanning electron microscopy (SEM) coupled with energy dispersive spectrometry (EDS). The results showed that MA-processed alloy was composed of an Mg-based supersaturated solid solution with small amounts of Al and MgAl2O4. Grain growth and Mg2Si precipitation occurred upon annealing of the MA-processed Mg-based alloy. Nevertheless, grain growth in the MA-processed alloy was limited and α-Mg grains with sizes in the range of 70 nm were still present after exposure to 450 °C. The grain growth behavior of alloy can be described by the parabolic kinetic equation of grain growth. Higher strength values obtained after hot consolidation can be due to refined microstructure and the formation of Mg2Si intermetallic phase.

References:

 

1. Y. Xu, L. Hu, Y. Sun, “Hot deformation behavior and microstructure evolution of as-cast AZ91D magnesium alloy without pre-homogenization treatment”, Rare Met., Vol. 32, 2013, pp. 332–337.


2. B. Sun, S. Li, H. Imai, J. Umeda, K. Kondoh, “Synthesis kinetics of Mg₂Si and solid-state formation of Mg-Mg₂Si composite”, Powder Technol., Vol. 217, 2012, pp. 57–162.


3. F. Wen-bin, F. Wa, S. Hong-fei S, “Preparation of high-strength Mg–3Al–Zn alloy with ultrafine-grained microstructure by powder metallurgy”, Powder Technol., Vol. 212, 2011, pp.161–165.


4. L. Lu, K. K. Thong, M. Gupta, “Mg-based composite reinforced by Mg₂Si”, Compos. Sci. Technol., Vol. 63, 2003, pp. 627–632.


5. L. Wang, X. Y. Qin, “The effect of mechanical milling on the formation of nanocrystalline Mg₂Si through solid-state reaction”, Scripta Mater., Vol. 49, 2003, pp. 243–248.


6. H. M. Zhang, X. B. He, X. H. Qu, Q. Liu, X. Y. Shen, “Microstructure and thermal properties of copper matrix composites reinforced with titanium-coated graphite fibers”, Rare Met., Vol. 32, 2013, pp. 75–80.


7. L. Shaw, H. Luo, J. Villegas, D. Miracle, “Thermal stability of nanostructured Al₉₃Fe₃Cr₂Ti₂ alloys prepared via mechanical alloying”, Acta Mater., Vol. 51, 2003,
   pp. 2647–2663.


8. M. A. Thein, L. Lu, M. O. Lai, “Kinetics of grain growth in nanocrystalline magnesium-based metal–metal composite synthesized by mechanical alloying”, Compos. Sci. Technol., Vol. 66, 2006, pp. 531–537.


9. M. Rajabi, M. Vahidi, A. Simchi, P. Davami, “Microstructural evolution of Al-20Si-5Fe alloy during rapid solidification and hot consolidation”, Rare Met., Vol. 28, 2009,
   pp. 639–645.


10. D. G. Morris, M. A. Morris, “Microstructure and strength of nanocrystalline copper alloy prepared by mechanical alloying”, Acta Metall. Mater., Vol. 39, 1991, pp. 1763–1770.


11. T. R. Malow, C. C. Koch, “Grain growth in nanocrystalline iron prepared by mechanical attrition”, Acta Mater., Vol. 45, 1997,
    pp. 2177–2186.


12. Y. Guangyin, L. Manping, D. Wenjiang,
    A. Inoue, “Mechanical properties and microstructure of Mg-Al-Zn-Si-base alloy”, Mater. Trans., Vol. 44, 2003, pp. 458–462.


13. X. Wei, Q. Xiao-ying, K. Ming-guang, C. Li, “Synthesis and properties of bulk nanocrystalline Mg₂Si through ball-milling and reactive hot-pressing”, Trans. Nonferrous Met. Soc. China, Vol. 16, 2006, pp. 987–991.


14. H. E. Kissinger, “Reaction kinetics in differential thermal analysis”, Anal. Chem., Vol. 29, 1957, pp. 1702–1706.


15. H. P. Klug, X-ray diffraction procedures. New York: Jones Wiley, 1962.


16. R. Vijay, R. Sundaresan, M.P. Maiya,
    S. Srinivasa Murthy, “Comparative evaluation of  Mg-Ni hydrogen absorbing materials prepared by mechanical alloying”, Int. J. Hydrogen Energy, Vol. 30, 2005, pp. 501–508.


17. Q. Zeng, I. Baker, V. McCreary, Z. Yan, “Soft ferromagnetism in nanostructured mechanical alloying FeCo-based powders”, J.Magn.Magn.Mater., Vol. 318, 2007, pp. 28–38.


18. Z. Luo, Z. Q. Li, “A W–In solid solution synthesized by mechanical alloying”, Mater. Sci. Eng. A, Vol. 459, 2007, pp. 47–51.


19. G. Y. Yuan, Z. L. Liu, Q. D. Wang, W. J. Ding, “Microstructure refinement of Mg-Al-Zn-Si alloys”, Mater. Lett., Vol. 56, 2002, pp. 53–58.


20. R. Yu-Ping, Q. Gao-Wu, P. Wen-li, L. Song, G. Yun, Z. Hong-da, “Phase equilibria of Mg-rich corner in Mg−Zn−Al ternary system at 300 °C”, Trans. Nonferrous Met. Soc. China, Vol. 22, 2012, pp. 241−245.


21. K. Kondoh, H. Oginuma, E. Yuasa, T.Aizawa, “Solid-state synthesis of Mg₂Si from Mg-Si mixture powder”, Mater. Trans., Vol. 42, 2001, pp. 1293−1300.


22. K. Lu, “Nanocrystallinemetals crystallized from amorphous solids: Nanocrystallization, structure, and properties”, J. Mater. Sci. Eng, Vol. R16, 1996, pp. 161–221.                              

23. C. Zener, “Private communication to C. S. Smith”, Trans. Met. Soc. AIME, Vol. 1948, pp.15–51.