Investigation on Hot Tearing Susceptibility of A201 Aluminum Alloy in Different Ingate Velocities and Molds

Subject Areas : Journal of Environmental Friendly Materials

M. H Ayandeh ¹ ( Materials and Mines Faculty, YazdUniversity, Yazd, Iran )
A. A Kashi ² ( University of Applied Science, Niroo Moharrekeh Co, Qazvin, Iran )
M. Ghambarian ³ ( Iran University of Industries and Mines (IUIM), Qazvin, Iran )
H. Karimi ⁴ ( University of Applied Science, Niroo Moharrekeh Co, Qazvin, Iran )
A. Mootabha ⁵ ( ShahidRajaei Power Plant, Qazvin, Iran )
A. Khoyini ⁶ ( R&D Department, Qazvin Gas Company, Qazvin, Iran )
E.M. Boushehri ⁷ ( R&D Department, Qazvin Gas Company, Qazvin, Iran )

Received: 2019-04-20 Accepted : 2019-07-06 Published : 2019-12-01

Keywords: Aluminum-Copper Alloys, Hot Tearing, Mold Strength, Critical Velocity,

References:

[1] D. Warrington and D. G. McCartney, Cast Met., 2, (1989), 134.

[2] G. Cao and S. Kou, Metall. Mater. Trans., A, 37 A, (2006), 3647.

[3] D. G. Eskin, "Physical metallurgy of direct chill casting of aluminium", First Edition (2008), CRC Press.

[4] J. B. Mitchell, S. L. Cockcroft, D . Viano, C. Davidson and D. John, Metall. Mater. Trans., A (2007), 2503.

[5] R. A. Rosenberg, M. C. Flemings and H. F. Taylor, AFS Trans., (1960), 518.

[6] J. A. Spittle and A. A. Cushway, Met. Technolo., 10 (1983), 6.

[7] F. D'Elia and C. Ravindran, Materials and Design 64 (2014), 44.

[8] J. A. Spittle and A. A. Cushway, "Influences of superheat and grain structure on hot tearing susceptibilities of Al-Cu alloy castings", The metal Society (1983).

[9] M. Ghambarian, S.M.A. Boutorabi and F. Shahri, J. Environ. Friendly Mater., 2, 1 (2018), 13.

[10] M. Nasr Esfahani and B. Niroumand,, Mater. Charact., 61 (2010), 318.

[11] M. Mirzayi, M. Sc Thesis, Iran University of Sci. Technol. , (2011), 70.