Synthesis of Fe3O4/SiO2/TiO2-Ag Core Shell Nanocomposites and Investigation of its Magnetic Properties

Subject Areas : journal of New Materials

فردین Ghasemi piranloo ¹ (مدیر و ریاست بخش پژوهش آزمایشگاه معتمد محیط زیست، شرکت فن آوران زیست کره، ابهر، زنجان، ایران)
سعیده Dadashian ² (کارشناس تحقیق آزمایشگاه معتمد محیط زیست، شرکت فن آوران زیست کره، ابهر، زنجان، ایران)
فاطمه Bavarsiha ³ (کارشناس آموزش آزمایشگاه معتمد محیط زیست، شرکت فن آوران زیست کره، ابهر، زنجان، ایران)

Received: 2016-10-21 Accepted : 2018-05-08 Published : 2018-04-21

Keywords: Nanocomposite, Core&ndash, shell structure, Titanium oxide, Ag particle, magnetic recoverable,

Abstract :

In this study, core–shell structure Fe₃O₄/SiO₂/TiO₂-Ag nanocomposites were synthesized in several stages. At first the Fe₃O₄ magnetic particles were obtained using the carbon reduction method. Then the Fe₃O₄/SiO₂ composite was synthesized using Tetraethyl orthosilicate (TEOS) precursor via sol-gel method. In the following a shell of TiO₂ was coated directly on it. Finally, Ag particle was deposited on the surface of TiO₂ nano-shell by an in situ wet chemistry route. Prepared nanocomposites were characterized by environmental scanning electron microscopy analysis (FESEM), transmission electron microscopy (TEM), X-ray diffraction (XRD) and Vibrating Sample Magnetometer (VSM). The results revealed Fe₃O₄/SiO₂/TiO₂–Ag nanocomposites have been successfully synthesized. The average size of Fe₃O₄ particles was about 300-400 nm and the size of Fe3O4/SiO2 particles is averagely between 400-450 nm and the average size of Fe₃O₄/SiO₂/TiO₂-Ag particles was calculated between 450-480 nm. Saturation magnetization (M_s) of nanocomposite showed a decreasing from 80emu/g to 37emu/g. Further coating of SiO₂ and TiO₂ decreases the saturation magnetization.

References:

- ن. بهرمندی طلوع، م.ح. فتحی، ا. منشی، و. مرتضوی، ف. شیرانی و م. محمدی سیچانی، "سنتز و ارزیابی رفتار ضدباکتریایی نانوذرات تیتانیا دوپ شده با نقره به عنوان یک افزودنی ضدباکتریایی به مواد دندانی"، مجله مواد نوین، جلد 4، شماره 1، ص 34-21، پاییز 92.

2- H. Liu, Z. Jia, S. Ji, Y. Zheng, M. Li, H. Yang, "Synthesis of TiO₂/SiO₂@Fe₃O₄ magnetic microspheres and their properties of photocatalytic degradation dyestuff", Catalysis Today 175, 293– 298, 2011.

3- J.P. Cheng, R. Ma, M. Li, J.S. Wu, F. Liu, X.B. Zhang," Anatase nanocrystals coating on silica-coated magnetite: Role of

polyacrylic acid treatment and its photocatalytic properties", Chemical Engineering Journal 210, 80–86, 2012.

4- Z. Teng, X. Su, G. Chen, C. Tian, H. Li, L. Ai, G. Lu, "Superparamagnetic high-magnetization composite microspheres with Fe₃O₄@SiO₂ core and highly crystallized mesoporous TiO₂ shell", Colloids and Surfaces A: Physicochem. Eng. Aspects 402, 60–65, 2012.

5- W. Wu, C.Z. Jiang, V.A.L. Roy, "Recent progress in magnetic iron oxide-semiconductor composite nanomaterials as promising photocatalysts", Nanoscale 7, 38–58, 2015.

6- Z. Liu, F.T. Chen, Y.P. Gao, Y. Liu, P.F. Fang, S.J. Wang, "A novel synthetic route for magnetically retrievable Bi₂WO₆ hierarchical microspheres with enhanced visible photocatalytic performance", J. Mater. Chem. A1, 7027–7030, 2013.

7- V. Belessi, D. Lambropoulou, I. Konstantinou, R. Zboril, J. Tucek, D. Jancik, T. Albanis, D. Petridis, "Structure and photocatalytic performance of magnetically separable titania photocatalysts for the degradation of propachlor", Appl. Catal. B, 87, 181-189, 2009.

8- D. Beydoun, R. Amal, G. Low, S. McEvoy, "Occurrence and prevention of photodissolution at the phase junction of magnetite and titanium dioxide", J. Mol. Catal. A, 180, 193-200, 2002.

9- X. F. Song, L. Gao, "Fabrication of bifunctional titania/silica-coated magnetic spheres and their photocatalytic activities", J. Am. Ceram. Soc., 90, 4015-4019, 2007.

10- C. X. Wang, L. W. Yin, L. Y. Zhang, L. Kang, X. F. Wang, R. Gao, "Magnetic (γ-Fe₂O₃@SiO₂)_n@TiO₂ Functional Hybrid Nanoparticles with Actived Photocatalytic Ability", J. Phys. Chem. C, 113, 4008, 2009.

11- J.C. Aphesteguy, S.E. Jacobo, N.N. Schegoleva, G.V. Kurlyandskaya, "Characterization of Nanosized Spinel Ferrite Powders Synthesized by Coprecipitation and Autocombustion Method", J. Alloys Compd. 495 509–512, 2010.

12- Z.H. Zhou, J. Wang, X. Liu, H.S.O. Chan, "Synthesis of Fe₃O₄ nanoparticles from emulsions", J. Mater. Chem. 11, 1704–1709, 2001.

13- H. L. Ding, Y. X. Zhang, S. Wang, J. M. Xu, S. C. Xu and G. H. Li, "Fe₃O₄@SiO₂ Core/Shell Nanoparticles: The Silica Coating Regulations with a Single Core for Different Core Sizes and Shell Thicknesses", Chem. Mater., 24, 4572, 2012.

14- M. Stjerndahl, M. Andersson, H. E. Hall, D. M. Pajerowski, M. W. Meisel and R. S. Duran, "Superparamagnetic Fe₃O₄/SiO₂ Nanocomposites: Enabling the Tuning of Both the Iron Oxide Load and the Size of the Nanoparticles", Langmuir, 24, 3532, 2008.

15- R. Fu, X. Jin, J. Liang, W. Zheng, J. Zhuang and W. Yang, "Preparation of nearly monodispersed Fe₃O₄/SiO₂ composite particles from aggregates of Fe3O4 nanoparticles", J. Mater. Chem., 21, 15352, 2011.

16- Y. Wang, X. Peng, J. Shi, X. Tang, J. Jiang and W. Liu, "Highly selective fluorescent chemosensor for Zn²⁺ derived from inorganic-organic hybrid magnetic core/shell Fe₃O₄@SiO₂ nanoparticles", Nanoscale Res. Lett., 7, 86, 2012.

17- C. Hui, C. Shen, J. Tian, L. Bao, H. Ding, C. Li, Y. Tian, X. Shia and H. J. Gao, "Core-shell Fe₃O₄@SiO₂ nanoparticles synthesized with well-dispersed hydrophilic Fe₃O₄ seeds", Nanoscale, 3, 701, 2011.

18- Everett. D. H, "Basic princinples of Colloid Science", Royal Society of Chemistry, 1988.

19- T. Hirakawa, P.V. Kamat, "Charge separation and catalytic activity of Ag@TiO₂ core–shell composite clusters under UV-irradiation", J. Am. Chem. Soc. 127, 3928–3934, 2005.

20- J.F. Guo, B. Ma, A. Yin, K. Fan, W.L. Dai, "Photodegradation of rhodamine B and 4- chlorophenol using plasmonic photocatalyst of Ag-AgI/Fe₃O₄@SiO₂ magnetic nanoparticle under visible light irradiation", Appl. Catal. B Environ. 101, 580–586, 2011.

21- B. Cui, H. Peng, H. Xia, X. Guo, H. Guo, "magnetically recoverable core–shell nanocomposites -Fe₂O₃@SiO₂@TiO₂–Ag with enhanced photocatalytic activity and antibacterial activity", Separation and Purification Technology 103: 251–257, 2013.

22- Junyang Li, Libo Gao, Qiang Zhang, Ruiting Feng, Hongyan Xu, JieWang, Dong Sun, and Chenyang Xue, "Photocatalytic Property of Fe₃O₄/SiO₂/TiO₂ Core-Shell Nanoparticle with Different Functional Layer Thicknesses", Journal of Nanomaterials, Article ID 986809, 7 pages, 2014.

23-Y. H. Deng, C. C. Wang, J. H. Hu, W. L. Yang, and S. K. Fu, "Investigation of formation of silica-coated magnetite nanoparticles via sol-gel approach", Colloids and Surfaces A, vol. 262, no. 1–3, pp. 87–93, 2005.

24- M.M. Ye, Q. Zhang, Y.X. Hu, J.P. Ge, Z.D. Lu, L. He, Z.L. Chen, Y.D. Yin, "Magnetically recoverable core–shell nanocomposites with enhanced photocatalytic activity", Chem. Eur. J. 16 (2010) 6243–6250.

25- Y. Chi, Q. Yuan, Y.J. Li, L. Zhao, N. Li, X.T. Li, W.F. Yan, "Magnetically separable Fe₃O₄@SiO₂@TiO₂-Ag microspheres with well-designed nanostructure and enhanced photocatalytic activity", J. Hazard. Mater. 262 (2013) 404–41.

26- Haiping Qi, Jing Ye, Nan Tao, Minghua Wen, Qianwang Chen, "Synthesis of octahedral magnetite microcrystals with high crystallinity and low coercive field", Journal of Crystal Growth 311, 394–398, 2009.

27- Xiaotai Zhang,  Jiaqi Wan, Kezheng Chen, Shuxian Wang, "Controlled synthesis of spherical and cubic nanocrystal clusters", Journal of Crystal Growth 372, 170–174, 2013.

28- Sachnin A. Kulkarni, P. S. Sawadh, Prakash K. Palei, "Synthesis and Characterization of Superparamagnetic Fe₃O₄@SiO₂ Nanoparticles", Journal of the Korean Chemical Society, Vol. 58, No. 1, 2014.

29- J. Lee, M. Othman, Y. Eom, T. Lee, W. Kim, J. Kim, "The effects of sonification and TiO₂ deposition on the micro-characteristics of the thermally treated SiO₂/TiO₂ spherical core–shell particles for photo-catalysis of methyl orange", Microp-orous Mesoporous Mater. 116 (2008) 561–568.

30- J.W. Lee, K. Hong, W.S. Kim, J. Kim, "Effect of HPC concentration and ultrasonic dispersion on the morphology of titania-coated silica particles", Journal of Industrial Engineering Chemistry 11 (2005) 609–614.

31- Jian Wang, Jinghai Yang, Xiuyan Li, Bing Wei, Dandan Wang, Hang Song, Hongju Zhai, Xuefei Li, "Synthesis of Fe₃O₄@SiO₂@ZnO–Ag core–shell microspheres for the repeated photocatalytic degradation of rhodamine B under UV irradiation", Journal of Molecular Catalysis A: Chemical 406 (2015) 97–105.

32- X. Wang, L.Y. Wang, X.W. He, Y.K. Zhang, L.X. Chen, "A molecularly imprinted polymer-coated nanocomposite of magnetic nanoparticles for estrone recognition". Talanta, 2009, 78: 327―332.