Hardness Prediction in the Ni-Based Superalloy GTD-111 Using Quench Factor Analysis (QFA)

Subject Areas : journal of New Materials

S.A Sajjadi ¹ (استاد، مهندسی مواد و متالورژی، دانشگاه فردوسی مشهد – مشهد، ایران)
مهدی Kianezhad ² (دانشجوی کارشناسی ارشد، مهندسی مواد و متالورژی، دانشگاه فردوسی مشهد – مشهد، ایران)

Received: 2016-12-26 Accepted : 2018-05-08 Published : 2018-04-21

Keywords: QFA, GTD-111, Quench Factor Analysis, hardness prediction, superall,

Abstract :

Prediction of mechanical properties for different alloys is an appropriate way to design alloys with adequate properties. One of the methods is Quench-Factor Analysis (QFA). The technique is used to predict mechanical properties of heat treated alloys. However, there is not yet any study concentrated on superalloys. In the present study, the efficiency of the method for the prediction of hardness of the Ni-based superalloy GTD-111 was evaluated. For this reason, some specimens were quenched in different quenching media. After measuring the hardness values of the samples, they were fitted to the data obtained using classical equations of quench factor analysis. Values k₂ to k₃ for GTD-111 were determined as 12×10^-11 s and 68 j.mol^-1, respectively using the cooling curves and measured hardness values. Moreover, the Time-Temperature-Property curve of the superalloy GTD-111 was obtained using the k₂ to k₅ constants. The results showed that, QFA is an appropriate method for hardness prediction of the Ni-based superalloys.         

References:

1- M.P. Petkov, A. Somoza, G. Santos & K.G. Lynn, “Nucleation and Growth Precipitates in a Ni-Based Superalloy”, Mater. Sci. Forum, 363, pp. 189-191, 2001.

2- J.R. Ho & S.H. Hong, “Effect of elastic interaction energy on coarsening of γ΄ precipitates in a mechanically alloyed ODS Ni-base superalloy”, J. Mater. Sci., 34, pp. 329-336, 1999.     
 

3- A.M. Ges, O Fornaro & H.A. Palacio, “Coarsening behaviour of a Ni-base superalloy under different heat treatment conditions”, Mater. Sci. and Eng. A, 458, pp. 96-100, 2007.       
 

4- S.A. Sajjadi, S. Nategh & R.I.L. Guthrie, “Study of microstructure and mechanical properties of high performance Ni-base superalloy GTD-111”, Mater. Sci. and Eng. A, 325, pp. 484-489, 2002.       
 

5- S.A. Sajjadi & S. Nategh, “A high temperature deformation mechanism map for the high performance Ni-base superalloy GTD-111”, Mater. Sci. and Eng. A, 307, pp. 158-164, 2001.     

6-S.A. Sajjadi, S.M. Zebarjad, R.I.L. Guthrie & M. Isac, “Microstructure evolution of high performance Ni- base superalloy GTD-111 with heat treatment parameters”, J. Mater. Proc. Techn., 175, pp. 376-381, 2006.     

7- J.W. Eavancho & J.T. Staley, “Kinetics of Precipitation in Aluminum Alloys During Continuous Cooling”, Metal. Trans., 5, pp. 43-47, 1974.     

8- A. Zehtab Yazdi, S.A. Sajjadi, S.M. Zebarjad & S.M. Moosavi Nezhad, “Prediction of hardness at different points of Jominy specimen using quench factor analysis method”, J. Mater. Proc. Techn., 199, pp. 124-129, 2008.           

9-J.D. Bernardin & I. Mudawar, “Validation of the quench factor technique in predicting hardness in heat treatable aluminum alloys”, International Journal for Heat Mass Transfer, 38, pp. 863-873, 1995.

10- J.T. Staley, R.D. Doherty & A.P. Jaworski, “Improved model to predict properties of aluminum alloy products after continuous cooling”, Metall. Trans., A 24, pp. 2417-2427, 1993.        

11- C.E. Bates & G.E. Totten, “Quench severity effects on the as-quenched hardness of selected alloy steels”, Heat Treatment of Metals, 2, pp. 45-48, 1992.
 

12- C.E. Bates, “Predicting properties and minimizing residual stress in quenched steel parts”, J. Heat Treat., 6, pp. 27-45, 1988.

13- C.R. Brooks, “Principles of heat treatment of plain carbon and low alloy steels”, ASM international, 1996.   

14- M. Avrami, “Kinetic of phase change”, J. Chem. Phys., 8, pp. 212-224, 1940).

15- J.W. Cahn, “Transformation kinetics during continuous cooling”, Acta Metallurgica, 4, pp. 572-575, 1956.   

16- P.A. Rometsch, M.J. Starink & P.J. Gregson, “Improvements in quench factor modelling”, Mater. Sci. and Eng. A, 339, pp. 225-264, 2003.    

17- R.J. Flynn & J.S. Robinson, “The application of advances in quench factor analysis property prediction to the heat treatment of 7010 aluminum alloy”, J. Mater. Proc. Techn., 153, pp. 674-680, 2004.

18- J.T. Staley, “Quench factor analysis of aluminum alloys”, Mater. Sci. and Techn., 3, pp. 923-935, 1987.        

19- M. Kianezhad & S.A. Sajjadi, “Improvement of Quench Factor Analysis in Phase and Hardness Prediction of a Quenched Steel”, Metal. and Mater. Trans. A, 5, pp. 2053-2059, 2012.      

20- S.A. Sajjadi, H.R. Elahifar & H. Farhangi, “Effects of cooling rate on the microstructure and mechanical properties of the Ni-base superalloy UDIMET 500”, J. Alloys and Comp., 455, pp. 215-220, 2008.

21- C.E. Bates, “Selecting quenchants to maximize tensile properties and minimize distortion in aluminum parts”, J. Heat Treating, 5, pp. 27-40, 1987.