Investigation of two step sintering on microstructure and compresive strenght of nano structured forsterite scaffold using lost foam

Subject Areas : journal of New Materials

Seyed M Mirhadi ¹ (مربی ، گروه مهندسی مواد ، واحد شهرضا ،دانشگاه آزاد اسلامی ،شهرضا،ایران)
A.A Nourbakhsh ² (دانشیار، گروه مهندسی مواد ، واحد شهرضا ،دانشگاه آزاد اسلامی ،شهرضا،ایران)
نجمه Lotfian ³ (دانشگاه آزاد اسلامی، واحد شهرضا، باشگاه پژوهشگران جوان و نخبگان، شهرضا، ایران)
پریسا Mashayekh ⁴ (کارشناسی ارشد،گروه مهندسی مواد ، واحد شهرضا ،دانشگاه آزاد اسلامی ،شهرضا،ایران)

Received: 2014-11-07 Accepted : 2017-11-16 Published : 2017-08-23

Keywords: forsterite scaffold, lost foam, porousity, Two step sintering,

Abstract :

This paper reports the successful synthesis of nano structured forsterite (Mg₂SiO₄)scaffold with high compressive strength for tissue engineering application. Forsterite slurry was prepared and pre-cut foams were immersed in the slurry for 5 min. The saturated foams were then annealed at various times and temperatures using the two step sintering method. The compressive strength and porosity of the scaffolds were in the range of 0.03-24.16 MPa and 58-88% depends on the heat treatment process, respectively. The J samples consisted of grains in the range of24 to35 nm and micron size pores that could be detected by SEM observation.

References:

1. S.I.R. Esfahani, F. Tavangarian, R. Emadi, "Nanostructured bioactive glass coating on porous hydroxyapatite scaffold for strength enhancement", Mater. Lett, vol. 62, pp. 3428-3430 2008.       


2. R. Emadi, S.I.R. Esfahani, F. Tavangarian, "A novel, low temperature method for the preparation of ß-TCP/HAP biphasicnano structured ceramic scaffold from natural cancellous bone", Mater. Lett,vol.64, pp. 993-996.2010         .


3. R.Emadi, F.Tavangarian, S.R.I. Esfahani, A. Sheikhhosseini, M.Kharaziha, "Nanostructured Forsterite Coating Strengthens Porous Hydroxyapatite for Bone Tissue Engineering", J. Am. Ceram. Soc, vol. 93, pp. 2679–2683.2010.      


4. R. Emadi, F. Tavangarian, S.I.R.Esfahani, "Biodegradable and bioactive properties of novel bone scaffold coated with nano crystalline bioactive glass for bone tissue engineering", Mater. Lett, vol. 64, pp. 1528–1531. 2010.           


5. M. Vallet-Reg, "Revisiting ceramics for medical application", Dalton Trans, Vol.44, pp. 5211–5220. 2006.           


6. V. Karageorgiou, D. Kaplan, "Porosity of 3D biomaterial scaffolds and osteogenesis", Biomaterials, vol. 26 , pp. 5474–5491. 2005.


7. A.J. Salgado, O.P. Coutinho, R.L. Reis, "Bone tissue engineering: state of the art and future trends", Macromol. Biosci, vol. 4, pp. 743–765. 2004.           


8. A. Rohlmann, H. Zilch, G. Bergman, "Material properties of femoral cancellous bone in axial loading. Part I: Time independent properties", Arch. Orthop. Trauma Surg, vol. 97 ,pp. 95–102. 1980.


9. F. Tavangarian, , R. Emadi, S.I.R. Esfahani, "A novel method to synthesis of β-TCP/HA biphasic nanocrystalline powder by using bovine bone", Int. J. Mod. Phys. B, vol. 24 ,pp. 3365-3372. 2010.          


10. F. Tavangarian, R. Emadi, "Nanostructure effects on the bioactivity of forsterite bioceramic",Materials letter, vo. 65 , pp. 740-743. 2011.    


11. F. Tavangarian, R. Emadi, "Improving degradation rate and apatite formation ability of nano structure forsterite", Ceram. Int, vol. 37 , pp. 2275–2280. 2011.         


12. H.W. Kim, J.C. Knowles, H.E. Kim, "Hydroxyapatite porous scaffold engineered with biological polymer hybrid coating for antibiotic Vancomycin release" Journal of materials science. Materials in medicine, vol. 16, pp. 189-195. 2005.           


13. H.W. Kim, J.C. Knowles, H.E. Kim, "Hydroxyapatite/poly(epsilon-caprolactone) composite coatings on hydroxyapatite porous bone scaffold for drug delivery",  Biomaterials, vol. 25 , pp. 1279-1287. 2004.     


14. م.مظفری،ن.جوهری،م.ح.فتحی،"داربست کامپوزیتی پلی کاپرولاکتون-هیدروکسی آپاتیت:بررسی تاثیر ذرات هیدروکسی آپاتیت و مقایسه ذرات با سایز نانومتری و میکرومتری و اثر آن ها برخواص مکانیکی و زیست تخریب پذیری داربست،"مجله مواد نوین،جلد5،شماره 20 ،ص 142-131تابستان1394.


15. T. Tian, D. Jiang, J. Zhang, Q. Lin, "Fabrication of bioactive composite by developing PLLA onto the framework of sintered HA scaffold", Mater. Sci. Eng. C, vol. 28 , pp. 51-56. 2008.           


16. X. Miao,G. Lim,K.H. Loh,"Preparation and characterization of calcium phosphate bone cement", materials processing for properties and performance , vol. 3 ,pp. 319-324. 2004.        


17. H. Ghomi, M. Jaberzadeh, M.H. Fathi, "Novel fabrication of forsterite scaffold with improved mechanical properties", J. Alloy Compd, vol. 509 , pp. 63–68. 2011.      


18. S. Ni, L. Chou, J. Chang, "Preparation and characterization of forsterite (Mg2SiO4) bio ceramics", Ceram Int, vol.33, pp. 83–88. 2007.              


19. F. Tavangarian, R. Emadi, "Mechanical activation assisted synthesis of pure nano crystalline forsterite powder", J. Alloys Compd 485 (2009) pp. 648–652. 2009.   


20. F. Tavangarian, R. Emadi, "Effects of fluorine ion and mechanical activation on nanostructure forsterite formation mechanism", Powder Technol, vol. 203, pp. 180–186. 2010.       


21. A. Douy, "Aqueous synthesis of forsterite (Mg2SiO4) and enstatite (MgSiO3)", J. Sol–Gel Sci. Technol, vol. 24, pp. 221–228. 2002.          


22. M. Kharaziha, M.H. Fathi, "Synthesis and characterization of bioactive forsterite      nanopowder", Ceramics International, vol. 35, pp. 2449-2454. 2009 .