Effect of PCA addition on microstructural and magnetic Properties a new Fe-based amorphous alloy prepared by Mechanical Alloying

Subject Areas : journal of New Materials

ehsan bahadori yekta ¹ (Department of Materials Science and Engineering, shahid bahonar University of kerman, kerman, Iran)
Amir Hossein Taghvaei ² (Department of Materials Science and Engineering, Shiraz University of Technology, Shiraz, Iran)
shahriyar sharafi ³ (Department of Materials Science and Engineering, shahid bahonar University of kerman, kerman, Iran)

Received: 2018-05-05 Accepted : 2018-12-15 Published : 2019-01-21

Keywords: mechanical alloying, Fe-based amorphous alloys, magnetic properties,

Abstract :

Nowadays, Fe-based amorphous/nanocrystalline alloys have been greatly developed due to the excellent magnetic properties, as well as their relatively low cost. In this study, the effect of process control agent (PCA) addition on the microstructure and magnetic properties of Fe75Ta5Si10C10 alloy produced by mechanical alloying was investigated. The X-ray diffraction (XRD) results showed that the addition of 2 wt. % PCA notably increases the glass forming ability (GFA) in the present alloying system and the percentage of the amorphous phase eventually reaches a value of 94 wt.% after 120 h milling. The amorphization reaction upon addition of the PCA was further confirmed by the transmission electron microscopy (TEM) analyzes. The crystallite size and lattice strain after 50 h milling were calculated as 10 nm and 1.44% after PCA addition, and 15 nm and 1.37% before that, respectively. The scanning electron microscopy (SEM) results confirmed that the powder prepared with the PCA exhibits finer particles with a more spherical shape. Magnetic measurements demonstrated that that both saturation magnetization and coercivity decrease and the soft magnetic behavior is improved with the PCA addition. Therefore, overall results in this study contain improvement of glass forming ability and soft magnetic properties with the PCA addition.

References:

References:
 [1]. J. Xu, Y.Z. Yang, W. Li, Z.W. Xie, X.C. Chen, "Effect of the substitution of C for Si on microstructure , magnetic properties and bending ductility in high Fe content FeSiBCuPC alloy ribbons", Alloys & Compound. Vol. 727, pp. 610–615, (2017).      

[2]. Mchenry.M.E., Johnson. F, Okumura. H, Ohkubo. T, "The kinetics of nanocrystallization and microstructural observations in FINEMET , NANOPERM and HITPERM nanocomposite magnetic materials", Scripta Materialia, Vol.48, pp. 881–887, (2003).

[3]. Makino. A, Men. H, Kubota. T, Yubuta. K, Inoue. A, "New Fe-metalloids based nanocrystalline alloys with high B_s of 1.9 T and excellent magnetic softness", Applied Physics, Vol. 105, 07A308, pp.10–13, (2009).

[4]. Bitoh. T, Makino. A, Inoue. A, "Origin of  low coercivity of Fe-(Al,

 

 

 

Ga)-(P, C, B, Si, Ge) bulk glassy alloys",

Material Transaction. Vol. 44, pp. 2020–2024, (2003).         
 

[5]. Herzer. G, "Modern soft magnets:

Amorphous and nanocrystalline materials", Acta Material, Vol. 61, pp. 718–734, (2013). 80-85, (2016).  

[5]. Herzer. G, "Modern soft magnets: Amorphous and nanocrystalline materials", Acta Material, Vol. 61, pp. 718–734, (2013).    

[6]. Makino. A, Kubota. T, Makabe. M, Chang. C. T, Inoue. A, "FeSiBP metallic glasses with high glass-forming ability and excellent magnetic properties", Material Science and Engineering B Solid-State Material Advance Technology, Vol. 148, pp. 166–170 , (2008).

[7]. Neamţu. B .V, Chicinaş. H .F, Marinca. T. F, Isnard. O, Chicinaş. I, "Preparation and characterisation of Co–Fe-Ni–M-Si–B (M = Zr, Ti) amorphous powders by wet mechanical alloying",  Alloys and Compounds, Vol. 673, pp.

[8]. Gheiratmand. T, Hosseini. H. R. M, Davami. P, Sara. C, "Fabrication of FINEMET bulk alloy from amorphous powders by spark plasma 80-85, sintering", Powder Technology, Vol. 289, pp. 163–168, (2016).  

[9]. Seifoddini. A, Stoica. M, Nili-ahmadabadi. M , Heshmati-manesh. S, Uta. K, "New (Fe_0.9Ni_0.1)₇₇Mo₅P₉C_7.5B_1.5 glassy alloys with enhanced glass-forming ability and large compressive strain", Materials Science & Engineering A, Vol. 560, pp. 575–582, (2013).          

[10]. Suryanarayana. C, "Mechanical alloying and milling", Progress in Material Science, pp. 1–184, (2001).
 

[11]. Yoshizawa. K.Y.Y, Oguma. S, "New Fe-based soft magnetic alloys composed of ultrafine grain structure", Applied Physics, Vol. 64 (10), pp. 6044–6046, (1988).        

[12]. Suzuki. T . M .K, Makino. A, "soft mgnetic properties of bcc Fe-M-B-Cu (M = Ti, Nb or Ta) alloys with nanoscale grain size", Japanese Applied Physics, Vol. 30 (10A), (1991).     

[13]. Willard. M . A, Laughlin. D . McHenry. M . E, "Structure and magnetic properties of (Fe_0.5Co_0.5)₈₈Zr₇B₄Cu₁ nanocrystalline alloys", Applied Physics. Vol, 84 (12), pp. 6773–6777, (1998).      

[14]. Taghvaei. A. H, Stoica. M , Khoshkhoo . M . S, Thomas. J, Vaughan. G, Janghorban. K, Eckert. J, "Microstructure and magnetic properties of amorphous/nanocrystalline Co₄₀Fe₂₂Ta₈B₃₀ alloy produced by mechanical alloying", Materials Chemistry and Physics, Vol. 134, pp.  1214–1224, (2012).      

[15]. Zuo. M, Meng. S, Li. Q, Li. H, Chang. C, "Effect of metalloid elements on magnetic properties of Fe-based bulk metallic glasses", Intermetallics. Vol. 83, pp. 83–86, (2017).    

[16]. Jiao. Z .B, Li. H. X, Gao. J . E, Wu. Y, Lu. Z. P, "Effects of alloying elements on glass formation , mechanical and soft-magnetic properties of Fe-based metallic glasses", Intermetallics, Vol. 19, pp. 1502–1508, (2011).         

[17]. Taghvaei.A. H, Khoshrodi. A. K, "Characterization, thermodynamic analysis and magnetic investigation of new soft magnetic amorphous/nanocrystalline Co₅₀Fe₂₁Ti₁₉Ta₅B₅ powders produced by mechanical alloying", Alloys and Compounds,Vol. 742, pp. 887-896, (2018).

[18]. Ogawa. H, Miura. H, "Compositional dependence of amorphization of M – C – Si ( M = Fe , Co or Ni ) materials by mechanical alloying", Materials Processing TechnologyVol. 144, pp. 256–260, (2003).

[19]. Mchenry. M. E, Willard. M. A, Laughlin. D. E, "Amorphous and nanocrystalline materials for applications as soft magnets", Progress in Materials Science, Vol. 44, pp. 291-433, (1999).

[20]. Yekta. E. B, Taghvaei. A. H, Sharafi. S, "Glass formation and magnetic study of new Fe₇₀Ta₅Si₁₀C₁₅ powders prepared by mechanical alloying with high thermal stability", Powder Technology. Vol. 322, pp. 241–249, (2017).           

[21]. Takeuchi. A, Inoue. A, "Classification of Bulk Metallic Glasses by Atomic Size Difference, Heat of Mixing and Period of Constituent Elements and Its Application to Characterization of the Main Alloying Element", Materials Transaction. Vol. 46, pp. 2817–2829, (2005).       

[22]. Taghvaei. A. H, Stoica. M, Vaughan. G, Ghaffari. M, Maleksaeedi. S, Janghorban. K, "Microstructural characterization and amorphous phase formation in Co₄₀Fe₂₂Ta₈B₃₀ powders produced by mechanical alloying", Journal of Alloys and Compounds. Vol. 512, pp. 85–93, (2012).     

[23]. Neamţu. B .V, Chicinaş. H .F, Marinca. T. F, Isnard. O, Chicinaş. I, "Amorphisation of Fe-based alloy via wet mechanical alloying assisted by PCA decomposition", Materials Chemistry and Physics, Vol. 183, pp.83-92, (2017).            

[24]. E. B. Yekta, A. H. Taghvaei, S. Sharafi, "The effect of metalloid content on glass forming ability, thermal stability and magnetic properties of Fe-Ta-Si-C powders prepared by mechanical alloying", Journal of Non-Crystalline Solids.      

25- ا. بهادری یکتا، ا.ح. تقوایی و ش. شرفی، " اثر زمان آسیاکاری و بررسی تحلیل ترمودینامیکی بر تشکیل فاز آمورف در آلیاژ Fe-C-Ta تولید شده به روش آلیاژسازی مکانیکی،" نشریه مواد نوین، شماره 31، ص 122-10، 1397.           

[26]. Dekhil. L, Alleg. S, Bououdina. M, Suñol. J. J, Grenèche. J. M, "Phase transformations and magnetic properties of ball-milled Fe-6P-1.7C powders", Advance Powder Technology. Vol. 26, pp. 519–526, (2015).           

[27]. Sourmail. T, "Near equiatomic FeCo alloys: Constitution, mechanical and magnetic properties", Progress in Materials Science, Vol. 50, pp.816-880, (2005).

[28]. Amini. R, Hadianfard. M. J, Salahinejad. E, Marasi. M, Sritharan. T, "Microstructural phase evaluation of high-nitrogen Fe– Cr– Mn alloy powders synthesized by the mechanical alloying process", Material Science, Vol. 44, pp. 136–148, (2009).        

[29]. Yelsukov. E. P, Dorofeev. G. A, Zagainov. A. V, Vildanova. N. F, "Initial stage of mechanical alloying in the Fe–C system", Material Science and Engineering A. Vol. 369, pp. 16–22, (2004).
 

[30]. Moumeni. H, Nemamch. A, Alleg. S, Grenèche. J. M, "Hyper fine interactions and structural features of Fe₄₄Co₆Mo (wt.%)  nanostructured powders", Materials Chemistry and Physics, Vol. 138, pp. 209–214, (2013). 

[31]. Yousefi. M, Sharafi. S, Mehrolhosseiny. A, "Correlation between structural parameters and magnetic properties of ball milled nano-crystalline Fe–Co–Si powders", Advance Powder Technology. Vol. 25, pp. 752–760, (2014).           

[32]. Taghvaei. A. H, Ghajari. F, Marko. D, Prashtanth. K. G, "Influence of milling time on microstructure and magnetic properties of Fe₈₀P₁₁C₉ alloy produced by mechanical alloying", Magnetism and Magnetic Material, Vol. 395, pp. 354-360, (2015).      

[33]. Sharma. S, "Amorphous Phase Formation in Mechanically Alloyed Fe-based Systems", PhD Thesis, (2008).

[34]. Wang. Y, Zhang.Y, Takeuchi. A, Makino. A, Liang. A, Kawazoe. Y, "Magnetic influence of alloying elements in Fe-rich amorphous alloys studied by abinitio molecular dynamics simulations", IEEE Transaction on Magnetics. Vol. 51, pp. 1–4, (2015).

[35]. Marinca. T. F, Chicinas. I, Isnard. O, Popa. F, "Structural and magnetic characteristics of Co-based amorphous powders prepared by wet mechanical alloying", Advance Powder Technology, Vol. 26, pp. 323-328, (2014).      

[36]. Gheisari. K, Shahriari. S, Javadpour. S, "Structural evolution and magnetic properties of nanocrystalline 50 Permalloy powders prepared by mechanical alloying", Journal of Alloys and Compounds. Vol. 574, pp. 71–82, (2013).

[37]. Nowroozi. M. A, Shokrollahi. H, "Magnetic and structural properties of amorphous/nanocrystalline Fe₄₂Ni₂₈Zr₈Ta₂B₁₀C₁₀ soft magnetic alloy produced by mechanical alloying", Advance Powder Technology, Vol. 24, pp. 1100–1108, (2013).          

[38]. Zeng. Q, Baker. I, Mccreary. V, Yan. Z, "Soft ferromagnetism in nanostructured mechanical alloying FeCo-based powders", Journal of Magnetism and Magnetic Materials, Vol. 318, pp. 28–38, (2007).       

[39]. Chen. C. W, "Magnetism and Metallurgy of Soft Magnetic Materials", North- Holland, Amsterdam, (1977).

[40]. Comstock. R. L, "Introduction to Magnetism and Magnetic Recording", Wiley, New York, (1999).

[41]. Herzer. G, Gmbh. V, Hanau. D, Germany. F. R, "Grain size dependence of coercivity and permeability", IEEE Xplore, Vol. 26, pp. 1397–1402, (1990).

[42]. Tavakoli. M, Shokrollahi. H, Karimi. L, Janghorban. K, "Investigation of structural, microstructural and magnetic properties of mechanically alloyed nanostructured (Fe₅₀Co₅₀)_100−xMo_x(x=25,35) powders", Powder Technology. Vol. 234, pp. 13–18, (2013).