Fabrication and characterization of ribbon and powder of amorphous alloy MBF-100 used in super alloy FSX- 414 TLP bonding

Subject Areas :

Mohamad Rajabi ¹ , رضا بختیاری ²

1 - Phd. Student, Department of Materials Engineering, Faculty of Engineering, Science and Research Branch, Islamic Azad University, Tehran
2 - استادیار دانشگاه رازی کرمانشاه

Received: 2015-07-31 Accepted : 2018-06-18 Published : 2018-05-22

Keywords: Super alloy FSX-414, MBF-100 ribbon or powder, Transient liquid phase (TLP) bonding,

Abstract :

In this research, the process of TLP joint for super alloy FSX-414 by using the interface layer of MBF-100 as ribbon or powder have been studied. For this purpose, two samples of cobalt base alloy super clubs FSX-414 with dimensions of 10  mm for connecting sample with MBF ribbon & the other with the same dimensions with U&V shape track for connecting with powder have been done. In the following, both samples were subjected to a heat treatment cycle at temperature of 1175 degree of centigrade for 30 minutes’ microstructure of TLP connection area was investigated by using light microscope, scanning electronical microscope & EDS analysis, EDS map analysis & micro hardness. In microscopic pictures related to TLP bonding with ribbon & sample of powder of fuzzy areas, including the area under fuzzing & influenced area were specified completely. The result of EDS analysis & EDS map analysis & micro hardness of penetration capability& better connecting of ribbon rather than powder has been valided

References:

 

[1]    D. Foster & C. T. Sims, “FSX-414 an alloy for gas turbines”, Metal progress, pp. 83-85, 1969. 

 

[2]    T. Sims, N. S. Stoloff & W. C. Hagel, Superalloy II John wiley and Sons, 1987.

 

[3]    T. Sims, “A Contemporary view of Cobalt-base alloys”, Journal of Metals, pp. 27-42, 1969.

 

[4]    R. Brooks, Heat treatment, structure and properties of nonferrous alloys, ASM, pp. 244-251, 1982.

 

[5]    R. Brunetaud, Conf. proc of high temperature alloys for gas turbines1982, D. Reidel pub Company, held in liege, -Belgium, Vol. 4-6, pp. 936-946, 1982.

 

[6]    S. Balsone, Buckets and nozzles, Greenville: Gene Electric Company, 2004.

 

[7]    D. Coutsoursdis, A. Davin & M. Lamberigts, “Cobalt-base superalloys for applications in gas turbinesMaterˮ, Sci En, 1987.

 

[8]    P. W. Schilke, “Advanced gas turbine materials and coatingsˮ, New York: General Electric Company, 2004.

 

[9]    C. Soare, Gas Turbines: a handbook of air, land and sea, applications, Texas: Elsevier Butterworth-Heinemann, 2008.

 

[10] W. M. Miglietti, “Wide gap diffusion braze repairs of nozzle segments cast from FSX-414 Co-based superalloyˮ, Proc. 3rd Int. Conf. on Brazing and Soldering. Texas: ASM International, 2004.

 

[11] O. A. Ojo, N. L. Richards & M. C. Charturvedi, “Effect of gap size and process parameters on diffusion brazing of Inconel 738ˮ, Sci Technol Weld Joining, Vol. 9, pp. 209-20, 2004.

 

[12] W. F.Gale & D. A. Butts, “Transient liquid phase bondingˮ, Sci Technol Weld Joi, Vol. 9, pp. 283-300, 2004.

 

 [13] R. Bakhtiari & A. Ekrami, “Transient liquid phase bonding of FSX-414 super alloy at the standard heat treatment conditionˮ, Journal of Materials Characterization, Vol. 66, pp. 38-45, 2012