Investigation of high temperature wear properties of NiCrBSi and satellite coatings deposited on hot work tool steel DIN-1.2344

Subject Areas :

مصطفی طهری ¹ , مجتبی اسماعیلیان ² , Behrooz Shahriari ³

1 - هیئت علمی/مجتمع آموزش عالی فنی و مهندسی اسفراین
2 - دانشگاه مالک اشتر
3 - PhD, Department of Mechanical and Aerospace Engineering, Malek Ashtar University of Technology, Tehran, Iran

Received: 2015-06-25 Accepted : 2017-03-11 Published : 2017-02-19

Keywords: High Temperature Wear, Thermal spray, Hot Work Steel, Satellite 6, NiCrBSi,

Abstract :

In this study, satellite 6 and NiCrBSi coatings deposited on hot work tool steel DIN-2344/1 by thermal spraying and cladding were investigated. Stellite 6 and NiCrBSi powders were deposited on the substrate by HVOF and Stellate 6 wire were cladded by GTAW. Scanning electron microscopy with energy dispersive spectroscopy and optical microscopy, pins on disk wear machine, macro and micro hardness meter were used to analyze the coatings. Results showed that the hardness and wear resistance of thermal spray coating were higher than cladding coating. At high temperature, the results of wear test show, that the NiCrBSi coating has the better wear resistance rather than satellite 6 coating. This behavior of NiCrBSi coating attributed to silicate and boride particles in this coating. On the other hand, the thermal spray satellite 6 coating show the very low friction coefficient due to chromium oxide formed on the surface of coatings.

References:

 [1] ح، شفیعی، ح، شفیعی و ,. شفیعی " بررسی و مطالعه رفتار سایشی سه پوشش TiN ، TiCN، Tin-TiCN-TiN، اعمال شده بر روی فولاد ابزار D2 به روش تبخیر پرتو الکترونی EB-PVD"، فرایندهای نوین در مهندسی مواد، دوره 9، شماره 1، صفحه 131-141، بهار 94.

 

[2]     Y. Birol & D. I˙sler, “Response to thermal cycling of CAPVD (Al, Cr) N-coated hot work tool steelˮ, Surface and Coating Technology. doi: 10.1016/j. surfcoat, 06.038, 2010.

 

[3]     B. Podgornik, V. Leskov & F. Tehovnik, “Vacuum heat treatment optimization for improved load carrying capacity and wear properties of surface engineered hot work tool steelˮ, Surface & Coatings Technology, doi: 10.1016/j. surfcoat, 11.021, 2014.

 

[4]     W. Xu, W. Li & Y. Wang, “Experimental and theoretical analysis of wear mechanism in hot-forging die and optimal design of die geometryˮ, Vol. 318, pp. 78–88, 2014.

 

[5]     Y. Birol & D. Isler, “Abrasive wear performance of AlCrN-coated hot work tool steel at elevated temperatures under three-body regimeˮ, Vol. 270, pp. 281–286, 2011.

 

[6]     F. H. Stott, “The role of oxidation in the wear of metalsˮ, Tribology International, Vol. 31, pp. 61–71, 1998.

 

[7]       ک. طاهرخانی، خ. محمدی و ح. تارقلی زاده، "بررسی خواص سطحی و سایشی پوشش نیتریدی ایجاد شده بر روی فولاد ابزار گرم کار H11  در روش نیتروژن دهی پلاسمایی پالسی"، فرایندهای نوین در مهندسی مواد، دوره 10، شماره 3، صفحه 23-36، پاییز 1395.

 

[8]     H. Kashani, A. Amadeh & H. M. Ghasemi, “Room and high temperature wear behaviors of nickel and cobalt base weld overlay coatings on hot forging diesˮ, Vol. 262A, pp. 800–806, 2007.

 

[9]     Y. Birol, “Thermal fatigue testing of Inconel 617 and Stellite 6 alloys as tooling materials for thixoforming of steelsˮ, Materials Science and Engineering, Vol. 5270A, pp. 1938–1945, 2010.

 

[10] Y. Birol, “the use of CrNiCo-based superalloy as die material in semi-solid processing of steelsˮ, Solid State Phenomena, Vol. 141A, pp. 289–294, 2008.

 

[11] P. Richer, A. Zuniga, M. Yandouzi & B. Jodoin, “CoNiCrAlY microstructural changes induced during Cold Gas Dynamic Sprayingˮ, Surface & Coatings Technology, Vol. 203, pp. 364–371, 2008.

 

[12] C. J. Li & W. Ya. Li, “Effect of sprayed powder particle size on the oxidation behavior of MCrAlY materials during high velocity oxygen-fuel depositionˮ, Surface and Coatings Technology, Vol. 162, pp. 31-41, 2002.

 

[13] S. Kamal, R. Jayaganthan & S. Prakash, “Mechanical and microstructural characteristics of detonation gun sprayed NiCrAlY + 0.4 wt% CeO2 coatings on superalloysˮ, Materials Chemistry and Physics, Vol. 122, pp. 262–268, 2010.

 

[14] Gholipour, M. Shamanian & F. Ashrafizadeh, “Microstructure and wear behavior of stellite 6 cladding on 17-4 PH stainless steelˮ, Vol. 509, pp. 4905–4909, 2011.

 

[15] G. Marot, J. Lesage & M. Hadad, “Interfacial indentation and shear tests to determine the adhesion of thermal spray coatingsˮ, Surface & Coatings Technology, Vol. 201, pp. 2080–2085, 2006.

 

[16] M. Pellizzari, D. Cescato & M. G. De Flora, “Hot friction and wear behaviour of high speed steel and high chromium iron for rollsˮ, Vol. 267, pp. 467–475, 2009.

 

[17] W. M. Xian & W. Shuqi, “Selection of Heat Treatment Process and Wear Mechanism of High Wear Resistant Cast Hot-Forging Die Steelˮ, Journal of Iron and Steel Research, International, Vol. 19, pp. 50-56, 2011.