  1 - Synthesis and Ethanol Sensitivities of Sn02 nanowires Suvit
  . Thanasanvorakun Pongsri Mangkomtong Majid Monajjemi Nikom Sangkorntong
  Sn02 nanowires with diameters of 30 — 200 nm have been synthesized by using carbothermalprocess via a thick film of tin dioxide and carbon powder precursor. The nanowires werecharacterized by X-ray power diffraction (XRD), scanning electron microscopy (SEM),transm أکثر

  Sn02 nanowires with diameters of 30 — 200 nm have been synthesized by using carbothermalprocess via a thick film of tin dioxide and carbon powder precursor. The nanowires werecharacterized by X-ray power diffraction (XRD), scanning electron microscopy (SEM),transmission electron microscopy (TEM) and Selected Area Electron Diffraction (SAED).The gas sensing characteristic of nanowires toward ethanol vapor was investigated. The gassensitivity experiments have demonstrated that the as-synthesized Sn02 materials exhibitgood sensitivity to ethanol vapors, which may offer potential applications in gas sensors. Thedetails of its sensing characteristics were observed and discussed. تفاصيل المقالة
• حرية الوصول المقاله
  • صفحة الملخص
  • نص كامل
  
  2 - Synthesis of Nano-Sized Titania Particles by Hydrolysis of Titanium Tetrachloride
  M. Farahmandjou M. Ramazani
  Nano-sized titanium dioxide TiO2 powder was successfully prepared from its precursor titanium (IV) chloride by a simple and new wet chemical method. TiCl4 were used as precursor in hydrogen peroxide, H2O2 and ethanol. This solution was then peptized using nitric acid an أکثر

  Nano-sized titanium dioxide TiO2 powder was successfully prepared from its precursor titanium (IV) chloride by a simple and new wet chemical method. TiCl4 were used as precursor in hydrogen peroxide, H2O2 and ethanol. This solution was then peptized using nitric acid and heated under reflux at 80°C. Their physico-chemical properties were then characterized by transmission electron microscopy (TEM), scanning electron microscopy (SEM) and X-Ray diffraction (XRD). The TEM results showed that the size of as-synthesized TiO2 nanoparticles were in the range of 7-10 nm. The SEM images showed that the size of nanoparticles increased when the nanoparticles prepared in presence of nitric acid. The SEM images showed that the quality of annealed TiO2 nanoaprticles, increased when the nanoparticles synthesized without nitric acid. The crystal structure of the nanoparticles before and after annealing was done by XRD analysis. It was realized that the rutile phase was formed after heat treatment at 600°C. XRD pattern also showed that the size of annealed TiO2 nanoparticles increased from 20 to 50 nm when the nanoparticles prepared with nitric acid. تفاصيل المقالة
• حرية الوصول المقاله
  • صفحة الملخص
  • نص كامل
  
  3 - Synthesis of nanosized TiO2 powder by Sol-Gel method in acidic conditions
  Parvain Gharbani Ali Mehrizad, Samad Motameni Tabatabii
  The preparation of nano-sized TiO2 by titanium tetraisopropoxide (Ti(OiPr)4) via sol-gelmethod using acid as a catalyst is investigated and the optimized conditions concerning theproportional amount of acid, water, alcohol is established by XRD and SEM. The effect ofcal أکثر

  The preparation of nano-sized TiO2 by titanium tetraisopropoxide (Ti(OiPr)4) via sol-gelmethod using acid as a catalyst is investigated and the optimized conditions concerning theproportional amount of acid, water, alcohol is established by XRD and SEM. The effect ofcalcination temperature on phase transformation of TiO2 (rutile, anatase and brookite) wasdetermined by XRD. The smallest grain size of TiO2 powder we have obtained is 25 nm foranatase at 400 ºC by controlling the acidity and the mole ratio of starting materials. تفاصيل المقالة
• حرية الوصول المقاله
  • صفحة الملخص
  • نص كامل
  
  4 - بررسی اثر TiO2 برکیفیت مخلوط رس‌های نسوز معادن سمیرم و قشلاق در ارتباط با کاربرد آن در صنعت نسوز
  حسین پایدار جمال طراح
  در این پروژه مخلوط هایی از دو ماده اولیه ی رسی از معادن سمیرم و قشلاق به منظور تعیین رفتار حرارتی برای تولید آجرهای نسوز مورد بررسی قرار گرفته اند. علت مخلوط نمودن این دو خاک، بالا بودن مقدار TiO2 (08/5 درصد) در خاک رس قشلاق و پایین بودن اکسید تیتانیم (52/1 درصد) در رس أکثر

  در این پروژه مخلوط هایی از دو ماده اولیه ی رسی از معادن سمیرم و قشلاق به منظور تعیین رفتار حرارتی برای تولید آجرهای نسوز مورد بررسی قرار گرفته اند. علت مخلوط نمودن این دو خاک، بالا بودن مقدار TiO2 (08/5 درصد) در خاک رس قشلاق و پایین بودن اکسید تیتانیم (52/1 درصد) در رس سمیرم بود. چند نمونه از این ماده مخلوط شده به مدت 5 ساعت در دماهای 1340 و 1600 درجه سانتی گراد پخت داده شده اند. ترکیب شیمیایی و مینرالی ماده خام و پخته شده آنها با استفاده از روش های XRF، XRD و SEM مشخص گردیدند. کانی های اصلی رس خام سمیرم عبارتند از کائولینیت، دیکیت، گوتیت و کوارتز و رس قشلاق متشکل از کائولینیت، بوهمیت، روتیل، دیاسپور(؟)، دیکیت و گوتیت می باشد. مخلوط پخته شده شامل مولیت، سیلیس و روتیل است. نتیجه آزمایشات انجام شده در این پروژه نشان داده که با اختلاط مناسب دو خاک با محتوای متفاوت TiO2 می توان میزان این ماده را در مخلوط دو خاک مورد بررسی به حد مطلوب رسانید تا قابل استفاده برای مصرف در صنعت نسوز باشد. تفاصيل المقالة