فهرس المقالات Surface morphology

• حرية الوصول المقاله
  • صفحة الملخص
  • نص كامل
  
  1 - Optical and morphological characterization of nanostructured AgO thin films
  Adeleh Granmayehrad Hamed Abbasi
  10.57647/j.jtap.2023.1701.04
  Silver Oxide (AgO) thin films were prepared by using a cylindrical direct current reactive magnetron sputtering system at 10-5 torr initial pressure on BK7 glass substrate. Samples deposited for 3, 5 and 7 minutes. Surface characterization of AgO thin films in the nanom أکثر

  Silver Oxide (AgO) thin films were prepared by using a cylindrical direct current reactive magnetron sputtering system at 10-5 torr initial pressure on BK7 glass substrate. Samples deposited for 3, 5 and 7 minutes. Surface characterization of AgO thin films in the nanometer scale can be accurately determined using the atomic force microscopy (AFM) and X-ray diffraction (XRD). The average roughness (Ravg), maximum peak to valley height (Rt) and root mean square (Rrms) roughness are used to analyze the surface morphology of AgO films. The linear optical absorption data were measured in the visible-near infrared spectral regions and the nonlinear refractive index (n2) of thin films is evaluated by the moiré deflectometery technique. The investigation indicates that, increase in AgO thickness leads to reduction in nonlinear refractive index. تفاصيل المقالة
• حرية الوصول المقاله
  • صفحة الملخص
  • نص كامل
  
  2 - Effects of different gas flow rates and non-perpendicular incidence angles of argon cold atmospheric-pressure plasma jet on silver thin film treatment
  Maryam Hosseinpour Akbar Zendehnam Seyedeh Mehri Hamidi Sangdehi Hamidreza Ghomi Marzdashti
  10.1007/s40094-019-00351-7
  AbstractIn this study, the influences of variations in the gas flow rate and incidence angles of argon cold atmospheric-pressure plasma jet on the morphology and absorption spectra of silver thin films (60 nm, 80 nm, and 100 nm film thickness) are investigated. To evalu أکثر

  AbstractIn this study, the influences of variations in the gas flow rate and incidence angles of argon cold atmospheric-pressure plasma jet on the morphology and absorption spectra of silver thin films (60 nm, 80 nm, and 100 nm film thickness) are investigated. To evaluate the surface morphology, atomic force microscopy (AFM) was employed on the silver thin film surface before and after plasma processing. To analyze the effect of plasma treatment on the grain size, the one-dimensional AFM surface profiles of Ag thin films are approximated using a Gaussian function. The absorbance of Ag thin films is measured in wavelength range of 190–1100 nm utilizing UV–Vis absorption spectrometer. Compared to the gas flow rates 0.5 standard litter per minute (SLM) and 2 SLM, surface treatment of Ag thin film with gas flow rate of 1 SLM increased the valley depth, the peak valley height, and the distance between two deepest valleys remarkably. A sequential argon plasma treatment (2-min plasma treatment perpendicular to surface was followed by 2-min plasma processing with non-perpendicular incidence angle of 60°) offers considerable improvement in the uniformity of grains and also changes shape of grains, especially the peak height (about 44 times higher than untreated sample) and area of grains (almost 136 times greater than untreated sample) which can be applicable for optical sensing technology. تفاصيل المقالة
• حرية الوصول المقاله
  • صفحة الملخص
  • نص كامل
  
  3 - مورفولوژی سطح شکست و ارتباط آن با چقرمگی/انعطاف پذیری در شیشه فلز حجمی آلیاژ Zr46(Cu4.5/5.5Ag1/5.5)46Al8
  محمدتقی اسدی خانوکی
  هدف از این پژوهش بررسی رفتار شکست و پدیده‌ی تبدیل نرمی به تردی در یک شیشه‌فلز حجمی آلیاژ پایه‌ی زیرکونیم است. همچنین به-طور خاص ارتباط بین مورفولوژی‌های سطح شکست و چقرمگی و انعطاف‌پذیری بررسی شده است. به همین منظور با استفاده از فرآیند ذوب قوسی و ریخته‌گری مکشی در خلأ، أکثر

  هدف از این پژوهش بررسی رفتار شکست و پدیده‌ی تبدیل نرمی به تردی در یک شیشه‌فلز حجمی آلیاژ پایه‌ی زیرکونیم است. همچنین به-طور خاص ارتباط بین مورفولوژی‌های سطح شکست و چقرمگی و انعطاف‌پذیری بررسی شده است. به همین منظور با استفاده از فرآیند ذوب قوسی و ریخته‌گری مکشی در خلأ، آلیاژ آمورف تولید و در نرخ mm/min 2/0 و دماهای 77 و 298 کلوین تحت آزمون خمش سه-نقطه‌ای قرار گرفت. سطوح شکست به کمک SEM مورد مطالعه و ارزیابی قرار گرفتند و با استفاده از مدل ناپایداری انحنای جریان، ضمن تعیین چقرمگی آلیاژ مورد مطالعه از طریق محاسبه‌ی اندازه‌ی مورفولوژی سطح شکست، ساز و کار شکست ترد و نرم بررسی شد. در ادامه، شرایط و دلایل تشکیل مورفولوژی‌های مختلف در این دو حالت به‌صورت کمّی تعیین گردید. نتایج نشان می‌دهد که آلیاژ پایه‌ی زیرکونیم علی‌رغم نرم بودن در دمای اتاق، در دماهای بسیار پایین (77 کلوین) به‌شدت ترد و بیان‌گر رفتار تبدیل نرمی به تردی است. تحت این شرایط میزان متوسط چقرمگی شکست از حدود MPa.m1/2 16 در دمای اتاق به حدود MPa.m1/2 5/3 در دمای 77 کلوین کاهش یافت. همچنین با کمک مدل ناپایداری انحنای جریان و اطلاعات سطح شکست، طول موج اعوجاج بحرانی (λc) برای این آلیاژ nm 127 محاسبه شد. درصورتی که طول موج اعوجاج اولیه (λI) کمتر از این مقدار بحرانی باشد، مشخصه‌ی سطح شکست به صورت نانو شیارهای موازی و متناوب خواهد بود. در صورتی که λI بزرگتر از مقدار بحرانی باشد شرایط برای تشکیل طرح دیمپل و طرح رگه‌ای فراهم خواهد شد. تفاصيل المقالة