Failure Evaluation of Cupronickel Alloy Used in the Condenser of the Desalination Unit
الموضوعات :Javad Hashemi 1 , Amin Rabiezadeh 2
1 - Department of Mechanical Engineering, Shiraz Branch, Islamic Azad University, Shiraz, Iran
2 - Department of Materials Engineering, Shiraz Branch, Islamic Azad University, Shiraz, Iran
الکلمات المفتاحية: desalination, X-ray diffraction, electron microscopy, pitting corrosion, Copper- nickel alloy,
ملخص المقالة :
This study looks into the various forms of corrosion that affect various elements of the South Pars Gas Company's first refinery's desalination plant, such as water compartments, tubular plates, support tubes, and the self-tube. To investigate the corrosion variables, a thorough analysis of the device's structure and process, as well as the material, was conducted. During repairs, damaged tubes were sampled and subjected to scanning electron microscopy, X-ray diffraction, and X-ray fluorescence testing. Evaluating scanning electron microscopy pictures from the inner surface of the tube reveals deformation and a rise in the tube's inner diameter. The X-ray diffraction patterns and elemental analysis by X-ray fluorescence show that the inner surface is corroded. The external surface of the tube and analysis of the diffraction patterns in this region reveal the formation of copper oxides on the outer surface of the tubes, which, when compared to electron microscopic images, distinguishes pitting corrosion caused by acid condensation collision on the outer surface of the tube. Finally, the major cause of the fracture was pitting corrosion.
[1] El-Dahshan, M.E. 2001. Corrosion and scaling problems present in some desalination plants in abu dhabi. Desalin. 138: 371-377.
[2] Hassan, A.M. and Malik, A.U. 1989. Corrosion resistant materials for seawater ro plants. Desalin. 74: 157-170.
[3] Zhang, Y., Wang, L. and Presser, V. 2021. Electrocatalytic fuel cell desalination for continuous energy and freshwater generation. Cell Reports Physical Science. 2(5): 1-9.
[4] Zapata-Sierra, A., Cascajares, M., Alcayde, A. and Manzano-Agugliaro, F. 2021. Worldwide research trends on desalination. Desalin. 519: 1-16.
[5] Hodgkiess, T. and Vassiliou, G. 2005. Complexities in the erosion corrosion of copper-nickel alloys in saline water. Desalin. 183(1-3): 235-247.
[6] Elragei, O., Elshawesh, F. and Ezuber, H.M. 2010. Corrosion failure 90/10 cupronickel tubes in a desalination plant. Desalin. Water Treat. 21(1-3): 17-22.
[7] Liu, Y., Alfantazi, A., Schaller, R.F. and Asselin, E. 2020. Localised instability of titanium during its erosion-corrosion in simulated acidic hydrometallurgical slurries. Corros. Sci. 174: 1-12.
[8] Pimputkar, S., Malkowski, T.F., Griffiths, S., Espenlaub, A., Suihkonen, S., Speck, J.S. and Nakamura, S. 2016. Stability of materials in supercritical ammonia solutions. The Journal of Supercritical Fluids. 110: 193-229.
[9] Abouswa, K., Elshawesh, F., Elragei, O. and Elhood, A. 2007. Corrosion investigation of cu–ni tube desalination plant. Desalin. 205(1-3): 140-146.
[10] Mantzavinos, D., Hodgkiess, T. and Lai, S.L.C. 2001. Corrosion of condenser tube materials in distilled water. Desalin. 138(1): 365-370.
[11] Ma, A.L., Jiang, S.L., Zheng, Y.G. and Ke, W. 2015. Corrosion product film formed on the 90/10 copper–nickel tube in natural seawater: Composition/structure and formation mechanism. Corros. Sci. 91: 245-261.
[12] Al-Odwani, A., El-Sayed, E.E.F., Al-Tabtabaei, M. and Safar, M. 2006. Corrosion resistance and performance of copper–nickel and titanium alloys in msf distillation plants. Desalin. 201(1-3): 46-57.
[13] Kear, G., Barker, B.D., Stokes, K.R. and Walsh, F.C. 2007. Electrochemistry of non-aged 90–10 copper–nickel alloy (uns c70610) as a function of fluid flow. Electrochim. Acta. 52(7): 2343-2351.
[14] Liu, M. and Gadikota, G. 2020. Single-step, low temperature and integrated co2 capture and conversion using sodium glycinate to produce calcium carbonate. Fuel. 275: 1-10.
[15] Anonymous. 1999. Studies in Physical and Theoretical Chemistry. Chapter 12 decomposition of carbonates.
[16] Nair, M. and Kumar, D. 2013. Water desalination and challenges: The middle east perspective: A review. Desalin. Water Treat. 51(10-12): 2030-2040.
[17] Parvizi, M.S., Aladjem, A. and Castle, J.E. 2013. Behaviour of 90–10 cupronickel in sea water. Int. Mater. Rev. 33(1): 169-200.
[18] Karthick, S., Muralidharan, S. and Saraswathy, V. 2020. Corrosion performance of mild steel and galvanized iron in clay soil environment. Arabian Journal of Chemistry. 13(1): 3301-3318.
[19] Alfantazi, A.M., Ahmed, T.M. and Tromans, D. 2009. Corrosion behavior of copper alloys in chloride media. Mater. Des. 30(7): 2425-2430.
[20] Wilhelm Schleich, K.M. and Powell, C. 2007. CuNi 90/10: How to avoid typical failures of seawater tubing systems and marine biofouling on structures A2 - Féron, D. In: Corrosion Behaviour and Protection of Copper and Aluminium Alloys in Seawater. New york: Woodhead Publishing.
[21] Glade, H., Meyer, J.-H. and Will, S. 2005. The release of co2 in msf and me distillers and its use for the recarbonation of the distillate: A comparison. Desalin. 182(1-3): 99-110.
[22] Tian, J., Wang, L., Sun, W., Yang, Y., Liu, Z., Wang, G., Zhao, L., Zhou, Y. and Liu, G. 2019. Failure analysis of steam jet pump at top of crude oil vacuum distillation tower. Engineering Failure Analysis. 103: 9-19.
[23] Al-Moubaraki, A.H. and Obot, I.B. 2021. Corrosion challenges in petroleum refinery operations: Sources, mechanisms, mitigation, and future outlook. Journal of Saudi Chemical Society. 25(12): 1-28.