Effect of Twist Extrusion Process on the Mechanical Properties and Microstructure Evolution of 70-30 Brass Alloy
الموضوعات :
Sara Hosseini Faregh
1
,
Amir Hasani
2
,
Majid Naseri
3
1 - Department of Materials Science and Engineering, Faculty of Engineering, Semnan University, Semnan, Iran
2 - Department of Materials science and Engineering, Faculty of Engineering, Semnan University, Semnan, Iran
3 - Department of Materials Science and Engineering, Faculty of Engineering, Shahid Chamran University of Ahvaz, Ahvaz, Iran
الکلمات المفتاحية: Mechanical Properties, Severe Plastic Deformation, Microstructure Evolution, Twist Extrusion (TE), Cartridge brass,
ملخص المقالة :
In this study, cartridge brass alloy was severely deformed by twist extrusion (TE) technique and its mechanical properties, before and after TE, was investigated using a die with the twist line slope of β = 30°. It was revealed that large strains imposed on the material by this advanced method of severe plastic deformation (SPD) led to a nano-scale ultrafine microstructure and to an enhancement of the mechanical properties. It was revealed that the more TE passes a finer grain sized microstructure obtained. Also, by increasing the number of TE passes, the yield strength and ultimate tensile strength increased. Microhardness test results show that the hardness increases from 55 (initial sample) to 110 HV and 140 HV in the center and lateral edges of the sample pass #1 TE, respectively. After six passes of twist extrusion, the microhardness of the center and lateral edges of the sample reaches 160 HV.