Borotellurite bio-silica glasses doped by erbium nanoparticles: Structural and thermal properties

الموضوعات : Journal of Theoretical and Applied Physics

Abdulkarim Muhammad Hamza ¹ , Umar Sa'ad Aliyu ² , Halimah Mohamed Kamari ³ , Ibrahim Gana Geidam ⁴ , Raouf El-Mallawany ⁵ , Nazrin Nazrin ⁶ , Muhammad Nasirudeen Baba ⁷

1 - Department of Physics, Faculty of Science, Universiti Putra Malaysia, 43400 UPM Serdang, Selangor, Malaysia
2 - Department of Physics, Faculty of Sciences, Federal University of Lafia, Nasarawa State, Nigeria.
3 - Department of Physics, Faculty of Science, Universiti Putra Malaysia, 43400 UPM Serdang, Selangor, Malaysia
4 - Department of Physics, Faculty of Science, Yobe State University Damaturu, Nigeri
5 - Physics Department, Faculty of Science, Menoufia University, Egypt
6 - Department of Physics, Faculty of Science, Universiti Putra Malaysia, 43400 UPM Serdang, Selangor, Malaysia
7 - Department of Physics, Faculty of Sciences, Federal University of Lafia, Nasarawa State, Nigeria

تاريخ الإرسال : 06 الخميس , رمضان, 1443 تاريخ التأكيد : 14 الأحد , شوال, 1443 تاريخ الإصدار : 02 الأربعاء , ذو القعدة, 1443

الکلمات المفتاحية: Erbium Nanoparticles, Structural properties, Glasses, Thermal Properties,

ملخص المقالة :

[(TeO2)0.8 (B2O3)0.2]0.8 (SiO2)0.2}0.99 (Ag2O)0.01]1-y - (Er2O3 NPs)y, and y=0.01,0.02,0.03,0.04 and 0.05 mole% were fabricated by the melt quenching technique. X-ray diffraction (XRD) was used to verify and confirm the glasses’ non-crystallinity. X-ray fluorescence (XRF) proved the achievement of silicate of 98.6% quality from rice husk. Fourier transform infrared d (FTIR) results exposed the basic structural units such as TeO4, TeO3, BO4, BO3, Si-O-Si, and O-Si-O within the network. The concentration of Er2O3 nanoparticles’ effects on the thermal properties of ErDBST glasses was duly discussed. From the profiling of the differential scanning calorimetry (DSC), the glass crystallization temperature Tc, and transition temperature Tg are estimated. Also, the thermal stability factor, defined as Ts = Tc - Tg, was higher than 100 oC. From room temperature above the Tg for all the sample glasses, specific heat capacity Cq (≥1.4 J/gK-1) was obtained. The results showed that the glass thermal stability and the transition temperature increase with the addition of Er2O3 nanoparticles (NPs). These suggest that an ErDBST glass exhibit good thermal stability and consequently is a suitable candidate for fiber drawing.