Additive Manufacturing in the Development of Ni-Base Superalloys
الموضوعات : Journal of Environmental Friendly Materialsخشایار مومن 1 , zahrasadat seyedraoufi 2 , Mehrdad Abbasi 3
1 -
2 - Faculty of Materials Engineering, Islamic Azad University Karaj Branch, Karaj, Iran
3 - Islamic Azad University Karaj Branch
الکلمات المفتاحية: Additive Manufacturing, Ni-base, Superalloy, Microstructure,
ملخص المقالة :
In this Article, laser-based additive manufacturing (AM) of Ni-based superalloys has been evaluated. By reviewing past research and recognizing the challenges and benefits of additive manufacturing, the future of this path can be well described. For this purpose, it is very important and useful to know the target industries, the resulting microstructure, the relationship between the microstructure and the mechanical properties of the final part. In addition, the ways to prevent possible defects of this process are summarized in the report. This report tries to introduce this process in the direction of less damage to the environment and available resources. To be introduced as an environmentally friendly method for manufacturing parts needed for energy supply and transmission. In the future, more reports of this process will be provided by the authors of this review article.
[1] Shajari Y, Razavi SH, Seyedraoufi ZS, Samiee M, The effect of time and temperature of solutionizing heat treatment on γ′ characterization in a Ni-base superalloy.Metallogr, Microstruc, and Anal. 2021; 10(4):441-447.
[2] Selvaraj SK, Sundaramali G, Jithin Dev S, Srii Swathish R, Karthikeyan R, Vijay Vishaal KE, Paramasivam V, Recent Advancements in the Field of Ni‐Based Superalloys. Adv. Mater. Sci. Eng. 2021; 2021(1):9723450.
[3] Shahwaz M, Nath P, Sen I, A critical review on the microstructure and mechanical properties correlation of additively manufactured nickel-based superalloys. J. Alloys Compd., 2022; 907:164530.
[4] Perrut M, Caron P, Thomas M, Couret A, High temperature materials for aerospace applications: Ni-based superalloys and γ-TiAl alloys. C R Phys. 2018; 19(8):657-671.
[5] Gudivada G, Pandey AK. Recent developments in nickel-based superalloys for gas turbine applications. J. Alloys Compd. 2023:171128.
[6] Shahwaz M, Nath P, Sen I, A critical review on the microstructure and mechanical properties correlation of additively manufactured nickel-based superalloys. J. Alloys Compd. 2022; 907:164530.
[7] Antolovich SD, Microstructural aspects of fatigue in Ni-base superalloys. Philosophical Transactions of the Royal Society A: Math. Phys. Eng. Sci. 2015; 373(2038):20140128.
[8] Kaleybar SP, Safari HM, Raoofi ZS, Shajari Y, Bakhtiari H, Microstructure Investigation, Hot Tensile and Hot Corrosion of IN600 to Nimonic 75 heterogeneous Connection in Spot Welding. Mapta J. Mech. Ind. Eng. (MJMIE). 2021; 5(1):1-10.
[9] Pike, L. M. (2008). Development of a fabricable gamma-prime (γ′) strengthened superalloy. Superalloys 2008, 191-200.
[10] Hosseini E, Popovich VA, A review of mechanical properties of additively manufactured Inconel 718. Addit. Manuf. AM 2019; 30:100877.
[11] Xia W, Zhao X, Wang J, Yue Q, Cheng Y, Kong L, Zhang Y, Gu Y, Bei H, Zhang Z, New strategy to improve the overall performance of single-crystal superalloys by designing a bimodal γ′ precipitation microstructure. Acta Materialia. 2023; 257:119200.
[12] Prashar G, Vasudev H, Hot corrosion behaviour of super alloys. Mater. Today: Proc. 2020; 26:1131-1135.
[13] Wang RZ, Zhu SP, Wang J, Zhang XC, Tu ST, Zhang CC, High temperature fatigue and creep-fatigue behaviors in a Ni-based superalloy: Damage mechanisms and life assessment. Int. J. Fatigue. 2019; 118:8-21.
[14] Shajari, Y., Seyedraoufi, ZS, Alizadeh, A, Razavi, SH, Porhonar M, Mirzavand K, Effect of solution temperature of rejuvenation heat treatment on the stability of γ′ precipitates in Ni-base superalloy IN738LC during long-term heating. Mater. Res.Express 2019; 6(12):126571.
[15] Wangyao P, Rojhirunsakool T, Korthamniwet W, Saenarjhan N, Lothonkum G, Effects of adding Ni and Co on microstructure and gamma prime phase stability in Ni superalloy Inconel 738 with 1 wt.-% Al. Mater. Test. 2020; 62(5):448-453.
[16] Eriş R, Akdeniz MV, Mekhrabov AO, Unveiling the effect of Hf-(Mo,W) addition on the coarsening, agglomeration, and dissolution behaviour of γ'-Ni3Al precipitates in model Ni-based superalloys. J. Alloys Compd. 2023; 936:167869.
[17] Liu S, Wang C, Yan P, Yu T, The effect of Ta, W, and Re additions on the tensile-deformation behavior of model Ni-based single-crystal superalloys at intermediate temperature. Mater. Sci. Eng. A. 2022; 850:143594.
[18] Tayal A, Kalsi NS, Gupta MK, Machining of superalloys: A review on machining parameters, cutting tools, and cooling methods. Mater. Today: Proc. (MTP) 2021; 43:1839-1849.
[19] Khan A, Gupta K, Experimental evaluation of surface quality characteristics in laser machining of nickel-based superalloy. Optik. 2019; 196:163199.
[20] Hashemi N, Seyedraoufi ZS, Shajari Y, The effect of partial solution heat treatment parameters on microstructure evaluation of IN792 superalloy. Metallogr. Microstruct. Anal. 2021; 10:627-633.
[21] Błachnio J, Chalimoniuk M, Kułaszka A, Borowczyk H, Zasada D, Exemplification of detecting gas turbine blade structure defects using the X-ray computed tomography method. Aerospace. 2021; 8(4):119.
[22] Cobbinah PV, Nzeukou RA, Onawale OT, Matizamhuka WR, Laser powder bed fusion of potential superalloys: A Rev. Metals. 2020; 11(1):58.
[23] Kuntoğlu M, Salur E, Gupta MK, Waqar S, Szczotkarz N, Vashishtha G, Korkmaz ME, Krolczyk GM, A review on microstructure, mechanical behavior and post processing of additively manufactured Ni-based superalloys. Rapid Prototyp. J. 2024; 30(9):1890-1910.
[24] Kuo YL, Kamigaichi A, Kakehi K, Characterization of Ni-based superalloy built by selective laser melting and electron beam melting. Metall. Mater. Trans. A. 2018; 49:3831-3837.
[25] Murr LE, Martinez E, Pan XM, Gaytan SM, Castro JA, Terrazas CA, Medina F, Wicker RB, Abbott DH, Microstructures of Rene 142 nickel-based superalloy fabricated by electron beam melting. Acta Mater. 2013; 61(11):4289-4296.
[26] Shaikh AS, Schulz F, Minet-Lallemand K, Hryha E, Microstructure and mechanical properties of Haynes 282 superalloy produced by laser powder bed fusion. Mater. Today Commun. 2021; 26:102038.
[27] Chakraborty A, Muhammad W, Masse JP, Tangestani R, Ghasri-Khouzani M, Wessman A, Martin É, Role of alloy composition on micro-cracking mechanisms in additively manufactured Ni-based superalloys. Acta Mater. 2023; 255:119089.
[28] Kaplanskii YY, Levashov EA, Korotitskiy AV, Loginov PA, Sentyurina ZA, Mazalov AB, Influence of aging and HIP treatment on the structure and properties of NiAl-based turbine blades manufactured by laser powder bed fusion. Addit Manuf. (AM) 2020; 31:100999.
[29] Bassini E, Sivo A, Martelli PA, Rajczak E, Marchese G, Calignano F, Biamino S, Ugues D, Effects of the solution and first aging treatment applied to as-built and post-HIP CM247 produced via laser powder bed fusion (LPBF). J. Alloys Compd. 2022; 905:164213.
[30] Zhang G, Zhang Y, Zheng L, Peng Z, Research progress in powder metallurgy superalloys and manufacturing technologies for aero-engine application. Acta Metall Sin. 2019; 55(9):1133-1144.
[31] Benjamin JS, Larson JM, Powder metallurgy techniques applied to superalloys. J. Aircr. 1977; 14(7):613-623.
[32] Li Y, Wang D, He Y, Ormastroni LM, Wang L, Cormier J, Zhang J, High temperature VHCF of a 3rd generation Ni-based single crystal superalloy with different casting pore sizes. Int. J. Fatigue. 2023; 175:107804.
[33] Selvaraj SK, Sundaramali G, Jithin Dev S, Srii Swathish R, Karthikeyan R, Vijay Vishaal KE, Paramasivam V, Recent Advancements in the Field of Ni-Based Superalloys. Adv. Mater. Sci. Eng. 2021; 2021(1):9723450.
[34] Ma LY, Han ZJ, Feng QS, Wan M, Meng B, Pulse current enhanced densification and mechanical property of Inconel 718 superalloy fabricated by spark plasma sintering. Mater. Sci. Eng. A. 2024; 913:147061.
[35] Razavi SH, Mirdamadi SH, Szpunar J, Arabi H, Improvement of age-hardening process of a nickel-base superalloy, IN738LC, by induction aging. J. Mater. Sci. 2002; 37:1461-1471.
[36] Qin Z, Li Q, Wang G, Liu F, Microstructural Characterization and Prior Particle Boundary (PPB) of PM Nickel-Based Superalloys by Spark Plasma Sintering (SPS). Mater. 2023; 16(13):4664.
[37] Kaierle S, Overmeyer L, Alfred I, Rottwinkel B, Hermsdorf J, Wesling V, Weidlich N, Single-crystal turbine blade tip repair by laser cladding and remelting. CIRP J. Manuf. Sci. Technol. 2017; 19:196-199.
[38] Rittinghaus SK, Schmelzer J, Rackel MW, Hemes S, Vogelpoth A, Hecht U, Weisheit A, Direct energy deposition of TiAl for hybrid manufacturing and repair of turbine blades. Mater. 2020; 13(19):4392.
[39] Scott-Emuakpor O, Johnson P, Forgiarini M, Noronha T, Applying Rapid Qualification to Fatigue Assessment of a Binder Jet Superalloy. InTurbo Expo: Power for Land, Sea, and Air 2024; 88018: V009T17A020.
[40] Raghavan S, Zhang B, Wang P, Sun CN, Nai ML, Li T, Wei J, Effect of different heat treatments on the microstructure and mechanical properties in selective laser melted INCONEL 718 alloy. MaterManuf. Processes. 2017; 32(14):1588-1595.
[41] Mostafa A, Picazo Rubio I, Brailovski V, Jahazi M, Medraj M, Structure, texture and phases in 3D printed IN718 alloy subjected to homogenization and HIP treatments. Metals. 2017; 7(6):196.
[42] Deshpande A, Deb Nath S, Atre S, Hsu K, Effect of post processing heat treatment routes on microstructure and mechanical property evolution of Haynes 282 Ni-based superalloy fabricated with selective laser melting (SLM). Metals. 2020; 10(5):629.
[43] Dudova N, Belyakov A, Sakai T, Kaibyshev R, Dynamic recrystallization mechanisms operating in a Ni–20% Cr alloy under hot-to-warm working. Acta Materialia. 2010; 58(10):3624-3632.
[44] Pataky GJ, Sehitoglu H, Maier HJ, High temperature fatigue crack growth of Haynes 230. Mater. Charact. 2013; 75:69-78.
[45] Dastgerdi HH, Shabani MO, Shajari Y. The effect of cooling rate on the solutionizing of IN718 superalloy produced via selective laser melting (SLM) method. J. Environ. Friendly Mater. (JEFM) 2019; 3(1):17-22.
[46] Ni M, Liu S, Chen C, Li R, Zhang X, Zhou K, Effect of heat treatment on the microstructural evolution of a precipitation-hardened superalloy produced by selective laser melting. Mater. Sci. Eng.: A. 2019; 748:275-285.
[47] Ni M, Liu S, Chen C, Li R, Zhang X, Zhou K, Effect of heat treatment on the microstructural evolution of a precipitation-hardened superalloy produced by selective laser melting. Mater. Sci. Eng.: A. 2019; 748:275-285.
[48] Carter LN, Martin C, Withers PJ, Attallah MM, The influence of the laser scan strategy on grain structure and cracking behaviour in SLM powder-bed fabricated nickel superalloy. J. Alloys Compd. 2014; 615:338-347.
[49] Badrossamay M, Rezaei A, Foroozmehr E, Maleki A, Foroozmehr A, Effects of increasing powder layer thickness on the microstructure, mechanical properties, and failure mechanism of IN718 superalloy fabricated by laser powder bed fusion.Int. J. Adv. Manuf. Technol. 2022:1-5.
[50] Sangid MD, Book TA, Naragani D, Rotella J, Ravi P, Finch A, Kenesei P, Park JS, Sharma H, Almer J, Xiao X, Role of heat treatment and build orientation in the microstructure sensitive deformation characteristics of IN718 produced via SLM additive manufacturing. Addit Manuf. (AM) 2018; 22:479-496.