The effect of preparation method and presence of impurity on structural properties and morphology of iron oxide

الموضوعات : فصلنامه نانوساختارهای اپتوالکترونیکی

Maryam Mahdavi Matin ¹ , Mohsen Hakimi ² , M . Mazloum-Ardakani ³

1 - Master student, Research and Technology of Magnetizm lab physics Department Yazd University, Yazd
2 - Assistant Professor, Research and Technology of Magnetizm lab physics Department Yazd University, Yazd
3 - Professor, Department of Chemistry, Yazd University, Yazd

تاريخ الإرسال : 22 الثلاثاء , صفر, 1438 تاريخ الإصدار : 03 الأحد , ربيع الثاني, 1438

الکلمات المفتاحية: Iron oxide, Co-precipitation, Hydrothermal, CCl4 Additive, Bar structure shape,

ملخص المقالة :

In this paper, the effect of the structural properties and morphology of iron oxide product, have been studied in co-precipitation and hydrothermal methods. Also, the effect of adding CCl₄ impurities and final annealing of the materials is taken into account. The more homogeneous particle size in hydrothermal method has been explained by the effect of adding CCl₄ as impurities to prevent the continuation of nucleation. It has also been observed that in co-precipitation sample additive has a key role for providing the bar shape particles by mediating of the anisotropic connection of nuclei. The difference in the crystal structure of the anneal samples has been related to the oxygen content.

المصادر:

[1]    D. J. Sellmyer, R. Skomski, Advanced magnetic nanostructure, Springer Science & Business Media, (2006).

[2]    M. Bahrami, Synthesize of magnetite nano particles (Fe₃O₄) and to evaluate its efficiency in the removal of cadmium from aqueous solutions, Water and Wastewater, (3) (2013).

[3]    V. Pillai, P. Kumar, M. S. Multani, D.O. Shah, Structure and magnetic properties of nanoparticles of barium ferrite synthesized using microemulsion processing, Colloids and Surfaces A: Physicochemical and Engineering Aspects, 80(1) (1993), 69-75.

[4]    C. T. Seip, E. E. Carpenter, C. J. O'Connor, V. T. John, S. Li, Magnetic properties of a series of ferrite nanoparticles synthesized in reverse micelles. IEEE transactions on magnetics, 34(4) (1998), 1111-1113.

[5]    H. Yu, M. Chen, P. M. Rice, S. X. Wang, R. L. White, S. Sun, Dumbbell-like bifunctional Au-Fe₃O₄ nanoparticles. Nano letters, 5(2) (2005), 379-382.

[6]    B. Zheng, M. Zhang, D. Xiao, Y. Jin, M. M. Choi, Fast microwave synthesis of Fe₃O₄ and Fe₃O₄/Ag magnetic nanoparticles using Fe²⁺ as precursor, Inorganic Materials, 46(10) (2010), 1106-1111.

[7]    J. Wang, Q. Chen, C. Zeng, B. Hou, Magnetic‐Field‐Induced Growth of Single‐Crystalline Fe₃O₄ Nanowires. Advanced Materials, 16(2) (2004), 137-140.

[8]    H. P. Johnson, R. T. Merrill, Low‐temperature oxidation of a single‐domain magnetite, Journal of Geophysical Research, 79(35) (1974), 5533-5534.

[9]    M. Cao, T. Liu, S. Gao, G. Sun, X. Wu, C. Hu, Z. L. Wang, Single‐crystal dendritic micro‐pines of magnetic α‐Fe₂O₃: large‐scale synthesis, formation mechanism, and properties, Angewandte Chemie International Edition, 44(27) (2005), 4197-4201.