Synthesis and characterization of poly (AAm-co-AAc)/NaA nanocomposite and removal of methylene blue with it
الموضوعات : Journal of the Iranian Chemical ResearchMojgan Zendehdel 1 , Abolfazl Barati 2 , Haniyeh Alikhani 3
1 - Department of Chemistry, Faculty of Science, Arak University, Arak, Iran
2 - Department of Chemical Engineering, Faculty of Engineering, Arak University, Arak, Iran
3 - Department of Chemistry, Faculty of Science, Arak University, Arak, Iran
الکلمات المفتاحية: Adsorption, nanocomposites, Poly (Acryl amide-co-Acrylic acid), NaA zeolite, Methylene Blue,
ملخص المقالة :
The nanocomposites of poly (Acryl amide-co-Acrylic acid) with different contents of NaAzeolite were prepared using ammonium persulfate as an initiator and N, N′-methylenebisacrylamide as the crosslinker. The morphology was characterized by SEM and the structure ofnanocomposite materials was studied with XRD and FT-IR that showed the interaction betweenporous materials and poly (AAm-co-Aac). The adsorption behaviors of methylene blue wereinvestigated for nanocomposites. It was shown that poly (AAm-co-AAc)/NaA nanocompositeshave higher adsorption than NaA and poly (AAm-co-AAc) alone. This effect was attributed togood interaction between the hydroxyl group in porous materials and carboxylic group in poly(AAm-co-AAc) with methylene blue.
[1] R.W. Thompson, in: H.G. Karge, J. Weitkamp (Eds.), Molecular Sieves: Science and Technology:
Synthesis, Springer, Berlin, 1998.
[2] N. Jovanovic, D. Skala, M. Marjanovic, M. Stankovic, T. Zerarka, in: B. Drzaj, S. Hocevar, S.
Pejovnik (Eds.), Zeolite: Synthesis, Structure, Technology and Application, Elsevier, Amsterdam,
1985.
[3] G. Giannetto, G. Perot, M. Guisnet, in: B. Drzaj, S. Hocevar, S. Pejovnik (Eds.), Zeolite: Synthesis,
Structure, Technology and Application, Elsevier, Amsterdam, 1985.
[4] Y. Nishizaka, M. Misono, Chem. Lett. (1993) 1295-1298.
[5] Y. Yan, T. Bein, J. Am. Chem. Soc. 117 (1995) 9990-9994
[6] L. Scandella, G. Binder, T. Mezzacasa, J. Gobrecht, R. Berger, H.P. Lang, C. Gerber,
J.K. Gimezewski, J.H. Koegler, J.C. Jansen, Micropor. Mesopor. Mater. 21 (1998) 403-408.
[7] C. Striebel, K. Hoffmann, F. Marlow, Micropor. Mater. 9 (1997) 43-50.
[8] D.W. Breck, Zeolite Molecular Sieves, Wiley, New York, 1974.
[9] M. Kondo, M. Komori, H. Kita, J. Membr. Sci. 133 (1997) 133-141.
[10] J.J. Jafar, M. Budd, Micropor. Mater. 12 (1997) 305-311.
[11] A.S. Huang, Y.S. Lin, W.S. Yang, J. Membr. Sci. 245 (2004) 41-51.
[12] L.C. Boudreau, M. Tsapatsis, Chem. Mater. 9 (1997) 1705-1709.
[13] S. Mintova, V. Valtchev, Zeolites 16 (1996) 31-34.
[14] I. Kumakirl, T. Yamaguchi, S. Nakao, Ind. Eng. Chem. Res. 38 (1999) 4682-4688.
[15] X.C. Xu, W.S. Yang, J. Liu, Mesopor. Micropor. Mater. 43 (2000) 299-311.
[16] J. Zah, H.M. Krieg, J.C. Breytenbach, J. Membr. Sci. 284 (2006) 276-290.
[17] Y.H. Ma, Y.J. Zhou, R. Poladi, Sep. Purif. Technol. 25 (2001) 235-240.
[18] A.S. Huang, W.S. Yang, Micropor. Mesopor. Mater. 102 (2007) 58-69.
[19] D. Solpan, S. Duran, M. Torun, Radiat. Phys. Chem. 77 (2008) 447-452.
[20] K. Haraguchi, T. Takehisa, Adv. Mater. 14 (2002) 1120-1124.
[21] W. Tao, W. Xiaoqing, Y. Yi, H. Wenqiong, Polym. Int. 55 (2006) 1413-1419.
[22] M. Zendehdel, A. Barati, H. Alikhani, A. Hekmat, 1th International conference on advances in
wastewater treatment and reuse, 10-12 November 2009, Tehran, Iran.
[23] J.Z. Yi, L.M. Zhang, Biores. Technol. 99 (2008) 2182-2186.
[24] G. Rytwo, D. Trop, C. Serban, Apply Clay Sci. 20 (2002) 273-82.