Effect of some additives on degradation of poly (vinyl chloride- co- vinyl
الموضوعات : Journal of the Iranian Chemical ResearchMohamamd Taghi Taghizadeh 1 , Abbas Agha Bozorgi 2
1 - Department of Physical Chemistry, Faculty of Chemistry, University of Tabriz, Tabriz, Iran
2 - Department of Physical Chemistry, Faculty of Chemistry, University of Tabriz, Tabriz, Iran
الکلمات المفتاحية: Thermal degradation, Activation energies, Copolymers, Vinyl chloride-co-Vinyl acetate, additive,
ملخص المقالة :
The thermal decomposition of 86 % vinyl chloride 14 % vinyl acetate copolymer wasstudied by the conductometry technique in the presence of nitrogen. The kinetics of stability andthermal degradation of vinyl chloride- co- vinyl acetate (PVC- co- PVAc) copolymer withcopper, copper oxide and tricalcium dicitrate (st) were investigated at various temperatures (150-180 oC ) in solution. The rate coefficients for the degradation of the copolymer were determined.The energies of activation, determined from the temperature dependence of the rate coefficientsfor copolymer alone was 63.536 kJ mol-1 and in the presence of copper, copper oxide andtricalcium dicitrate were 44.224, 55.594 and 110.332 KJ mol-1, respectively. The results showthat thermal stability was increased in the presence of tricalcium dicitrate, but its thermalstability was decreased in the presence of copper and copper oxide.
[1] F.W. Biumeyer, Textbook of Polymer Science, John Wiley, 1994.
[2] D. Braun, B. Bohringer, S. Kommerling, Appl. Macromol. Chem. Phys. 216 (1994) 1-19.
[3] D.L. Gerrad, W.F. Maddams, Marcomolecules 14 (1981) 1356-1359.
[4] T. Hejertberg, E. Sorvik, J. Appl. Polym. Sci. 22 (1978) 2415-2426.
[5] E.P. Chang, R. Salovey, J. Polym. Sci, Polym. Chem. Ed. 12 (1974) 2927-2944.
[6] G. Sivalingam, R. Karthik, G. Madras, Ind. Eng. Chem. Res. 42 (2003) 3647-3656.
[7] M. Blazo, E. Jakab, J. Anal. Appl. Pyrolysis 49 (1999) 125-143.
[8] R.S. Lehrle, J.C. Robb, Nature 183 (1959) 1671-1680.
[9] N. Grassie, I.F. Mclaren, Eur. Polym. J. 6 (1970) 679-686.
[10] N. Grassie, I.F. Mclaren, I.C. Mc Neill, Eur. Polym. J. 6 (1970) 865-877.
[11] X. Ruijian, Polym. Degrad. Stab. 28 (1990) 323-330.
[12] G. Spiliopolos, M. Statheropoulos, G. Parissakis, Eur. Polym. 25 (1989) 989-991.
[13] T. Mirokawa, Kagaku to Kogyo (Osaka) 41 (1967) 169-188.
[14] N.G. Gaylard, A. Takahashi, J. Jolym. Sci. 8 (1970) 37-48.