An Experimental Investigation on Fracture Analysis of Polymer Matrix Composite under Different Thermal Cycling Conditions

Subject Areas : Engineering

A.R Ghasemi ¹ , M Moradi ²

1 - Faculty of Mechanical Engineering, Department of Solid Mechanics, University of Kashan, Kashan, Iran
2 - Faculty of Mechanical Engineering, Department of Solid Mechanics, University of Kashan, Kashan, Iran

Received: 2017-07-02 Accepted : 2017-09-04 Published : 2017-12-30

Keywords: Taguchi Method, Thermal cycling, Polymer matrix composites (PMCs), Fracture of composite,

Abstract :

Fracture analysis of glass/epoxy composites under different thermal cycling conditions is considered. Temperature difference, stacking sequence, fiber volume fraction and number of thermal cycles are selected as the experimental design factors. The Taguchi method is implemented to design of the experiment and an apparatus is developed for automatic thermal cycling tests. The tensile tests are done to study mechanical behavior of the specimens after the thermal cycling. The results show that the stacking sequence is the main effective factor on the fracture surface behavior of the specimens. Also, long splitting, lateral and angled breakage are the dominate failure mode of [0]8, [02/902]s and [0/±45/90]s layups, respectively. It’s found that the thermal cycling and temperature difference cause to increase the surface matrix loss significantly. This surface matrix loss can be an initial region to matrix debonding and crack propagation. Also, when the angle difference between lamina is increased the mechanical properties are reduced under the thermal cycling, significantly.

References:

[1] Kessler S., McManus H., Matuszeski T., 2001, The effects of cryo-cycling on the mechanical properties of IM7/977-2, Proceedings of the American Society for Composites, Blacksburg.
[2] Paillous A., Pailler C., 1994, Degradation of multiply polymer-matrix composites induced by space environment, Composite 25(4): 287-295.
[3] Ramanujam N., Vaddadi P., Nakamura T., Singh R.P., 2008, Interlaminar fatigue crack growth of cross-ply composites under thermal cycles, Composite Structures 85: 175-187.
[4] Eselun S.A., Neubert H.D., Wolff E.G., 1979, Microcracking effects on dimensional stability, National SAMPE Technical Conference, Proceedings of the 24th Conference.
[5] Rinaldi G., Maura G., 1993, Durable glass–epoxy composites cured at low temperatures– effects of thermal cycling, UV irradiation and wet environmental, Polymer International 31(3): 339-345.
[6] Cohen D., Hyer M.W., Tompkins S.S., 1984, The effects of thermal cycling on matrix cracking and stiffness changes in composite tubes, National SAMPE Technical Conference, Proceedings of the 16th Conference.
[7] Ghasemi A.R., Baghersad R., Sereshk M.R.V., 2011, Non-linear behavior of polymer based composite laminates under cyclic thermal shock and its effects on residual stresses, Journal of Polymer Science and Technology 24(2): 133-140.
[8] Adams D.S., Bowles D.E., Herakovich C.T., 1986, Thermally induced transverse cracking in graphite-epoxy cross-ply laminates, Journal of Reinforced Plastics & Composites 3: 152-169.
[9] Rouquie S., Lafarie_Frenot M. C., Cinquin J., Colombaro A. M., 2005, Thermal cycling of carbon/epoxy laminates in neutral and oxidative environments, Composites Science and Technology 65: 403-409.
[10] Scida D., Assarar M., Poilâne C., Ayad R., 2013, Influence of hygrothermal ageing on the damage mechanisms of flax-fibre reinforced epoxy composite, Composites Part B:Engineering 48: 51-58.
[11] Lafarie-Frenot M.C., Rouquie S., 2004, Influence of oxidative environments on damage in c/epoxy laminates subjected to thermal cycling, Composite Science and Technology 64(10-11): 1725-1735.
[12] Mouzakis D.E., Zoga H., Galiotis C., 2008, Accelerated environmental ageing study of polyester/glass fiber reinforced composites (GFRPCs), Composites Part B:Engineering 39: 467-475.
[13] Lafarie-Frenot M.C., Ho N. Q., 2006, Influence of free edge intralaminar stresses on damage process in CFRP laminates under thermal cycling conditions, Composites Science and Technology 66(10): 1354-1365.
[14] Devore J.L., Farnum N.R., 1999, Applied Statistics for Engineering and Scientists, Duxbury Press, Pacific Grove, CA.
[15] Ju J., 2007, Transverse cracking of M40J/PMR-II-50 composites under thermal-mechanical loading: Part I- Characterization of main and interaction effects using statistical design of experiments, Journal of Composite Materials 41(9): 1067-1086.
[16] Lochner R.H., Matar J.E.,1990, Design for Quality–An Introduction to the Best of Taguchi and Western Methods of Statistical Experimental Design, New York.
[17] Vankanti V.K., Ganta V., 2014, Optimization of process parameters in drilling of GFRP composite using Taguchi method, Journal of Material Research & Technology 3(1): 35-41.
[18] ASTM D3039/ D 3039 M-95a, 1997, Standard test method for tensile properties of polymer matrix composite materials.
[19] Ghasemi A.R., Moradi M., 2015, Surface degradation of polymer matrix composites under different low thermal cycling conditions, Journal of Solid Mechanics 9(1): 54-62.
[20] MINITAB 17 statistical software, Minitab Inc, 2013.