Corrosion Protection of AISI 304 Stainless Steel using Thin Films of Manganese Nitride

Subject Areas : Polymer

Fatemeh Abdi ¹

1 - Department of Engineering Sciences, Faculty of Advanced Technologies, University of Mohaghegh Ardabili, Namin, Iran.

Received: 2021-11-21 Accepted : 2021-11-21 Published : 2021-10-01

Keywords:

Abstract :

In this work, the thin films of manganese nitride were used to protect AISI 304 stainless steel against corrosion in 3.5% salt solution. These coatings were prepared using the physical vapor deposition of manganese. After deposition, the samples were placed in a furnace under nitrogen flux for nitriding. The crystal structure of the samples was studied using X-ray diffraction (XRD) pattern, and the formation of manganese nitride phase was observed. An atomic force microscope (AFM) was used to investigate the surface morphology of the samples. To evaluate the corrosion resistance of the structures, EiS and polarization tests were performed on the samples. the corrosion resistance of the samples was obtained by simulating the equivalent circuit. Finally, the surface of the corroded samples was observed using scanning electron microscopy (SEM).

References:

[1]. S. E. Ziemniak, M. Hanson, Corros. Sci., 44, 2209 (2002).
[2]. H. Zhang, Y. L. Zhao, Z. D. Jiang, Mater. Lett., 59, 3370 (2005).
[3]. D. H. Mesa, A. Toro, A. Sinatora, A. P. Tschiptschin, Wear., 255, 139 (2003).
[4]. J. D. Crossen, J. M. Sykes, G. A. D. Briggs, J. P. Lomas, Organic Coatings for Corrosion
Control, 98, 106 (1998).
[5]. H. Savaloni, M. Habibi, Applied Surface Science., 258, 103 (2011).
[6]. C. Liu, G. Lin, D. Yang, M. Qi, Surf. Coat. Technol., 200, 4011 (2006).
[7]. V. H. V. Sarmento, M. G. Schiavetto, P. Hammer, A. V. Benedetti, C. S. Fugivara, P. H.
Suegama, S. H. Pulcinelli, C. V. Santilli, Surf. Coat. Technol., 204, 2689 (2010).
[8]. M.Aparicio,A.Jitianu, G.Rodriguez ,A.Degnah ,K.Al-Marzoki,J.Mosa , L.C.Klein,
Electrochimica Acta, 202, 332, (2016).
[9]. D. Pech, P. Steyer, J. P. Millet, Corros., Sci., 50, 1492 (2008).
[10]. A. R. Grayeli, H. Savaloni, Applied Surface Science., 258, 9982 (2012).
[11]. H. Hoche, J. Schmidt, S. Grob, T. T. robmann, C. Berger, Surf. Coat. Technol., 205, 145
(2011).
[12]. A. Dehghanghadikolaei, N. Namdari, B. Mohammadian, B. Fotovvati, E. Research, E.
Additive, J. Sci. Eng. Res., 5, 123 (2018). 

[13]. P. J. Kelly and R. D. Arnell, Vacuum, 56 , 159 (2000).
[14]. K. Baba, R. Hatada, R. Emmerich, B. Enders and G. K. Wolf, Instrum. Method. B, 106 , 109
(1995).
[15]. G. F. Huang, L. P. Zhou, W. Q. Huang, L. H. Zhao, S. L. Li and D. Y. Li,Diam. Relat.
Mater.,12, 1406 (2003).
[16]. H. P. Feng, C. H. Hsu, J. K. Lu and Y. H. Shy, Mater. Sci. Eng. A, 347, 123 (2003).
[17]. D. Damborenea, J. Navas, C. García, J. Arenas, M. Conde, Surf. Coat. Technol, 201, 5751
(2007).
[18]. M. Mathew, E. Ariza, L. Rocha, A.C. Fernandes, F. Vaz, Tribol. Int. 41 , 603 (2008).
[19]. K. Dahm, P. Dearnley, Wear, 259, 933 (2005).
[20]. P.A Dearnley, G. Aldrich-Smith, Wear , 256, 491 (2004).
[21]. B. Fotovvati, N. Namdari, A. Dehghanghadikolaei, Mater. Res. Express , 6 12002, (2018)
[22]. L. Liu, P.Yang, C.Su, H. Guo, M An, Int. J. Electrochem. Sci, 8, 6077 (2013).
[23]. D. Fang, X. Li1, H. Li1, Q. Peng, Int. J. Electrochem. Sci., 8, 2551 (2013) .
[24]. Y.Xin, Ch. Liu W. Zhang, J. Jiang,G. Tang, X.Tian, and P. K. Chua, Journal of The
Electrochemical Society, 155 ,5 (2008).
[25]. C.S. Wu, Z. Zhang, F.H. Cao, L.J. Zhang, J.Q. Zhang,C.N. Cao, Applied Surface Science,
253,3893 (2007).
[26]. K.F. Khaled, Electrochimica, Acta ,55, 6523, (2010)
[27]. A. R. Grayeli- corpia, H. Savaloni, M. Habibi, Applied Surface Science, 276, 269 (2013).
[28]. F. Abdi, Chinese Physics B, 30, 38106, (2021)
[29]. F. Modiri, H. Savaloni, Journal of Theoretical and Applied Physics, 14, 21 (2020)
[30]. F. Modiri, H. Savaloni, Journal of Theoretical and Applied Physics, 14, 223 (2020).
[31]. F.abdi and H.savaloni, Optics Communications, 80, 69 (2016)
[32]. F.abdi and H.savaloni ,Applied Surface Science, 330, 74 (2015).
[33]. Y. Xin, C. Liu, W. Zhang, J. Jiang, G. Tang, X. Tian, P.K. Chu, Journal of The
Electrochemical Society, 155, 5 (2008).
[34]. C.S. Wu, Z. Zhang, F.H. Cao, L.J. Zhang, J.Q. Zhang, C.N. Cao, Applied Surface Science, 253
3893 (2007).
[35]. D. Fang, X. Li, H. Li, Q. Peng, Int. J. Electrochem. Sci., 8, 2551 (2013).

[36]. L. Liu, P. X. Yang, C. N. Su, H. F. Guo, M. Z. An, Int. J. Electrochem. Sci., 8, 6077 (2013).
[37]. R. Solmaz, G. Kardas, M. C. Ulha, B. Yazici, M. Erbil, Electrochim. Acta, 53, 5941 (2008).
[38]. F. Abdi, H. Savaloni, transactions of nano ferrous metals society of china, 27, 701 (2017)